Two-dimensional/three-dimensional hierarchical self-supporting potassium ammonium vanadate@MXene hybrid films exhibit excellent electrochemical performance. [Display omitted] Currently, aqueous zinc ion batteries (AZIBs) have grown to be a good choice for large-scale energy storage systems due to their high theoretical specific capacity, low redox potential, low cost, and non-toxicity of the aqueous electrolyte. However, it is still challenging to obtain high specific capacity and stability suitable cathodes. Herein, hierarchical self-supporting potassium ammonium vanadate@MXene (KNVO@MXene) hybrid films were prepared by vacuum filtration method. Due to the three-dimensional nanoflower structure of KNVO with dual ions intercalation, high conductivity of two-dimensional Ti 3 C 2 T x MXene, and the hierarchical self-supporting structure, the AZIB based on the KNVO@MXene hybrid film cathode possessed superior specific capacity (481 mAh/g at 0.3 A/g) and cycling stability (retaining 125 mAh/g after 1000 cycles at a high current density of 10 A/g). In addition, the storage mechanism was revealed by various ex-situ characterizations. Hence, a new viewpoint for the preparation of AZIB self-supporting cathode materials is presented. [ABSTRACT FROM AUTHOR]

Due to the presence of the hierarchical freestanding structure, outstanding MXene conductive networks and abundant oxygen vacancy, the d-NVO@MXene hybrid film exhibits excellent electrochemical properties. [Display omitted] Aqueous zinc ion batteries (AZIBs) have gained extensive attention due to the numerous advantages of zinc, such as low redox potential, high abundance, low cost as well as high theoretical specific capacity. However, the development of AZIBs is still hampered due to the lack of suitable cathodes. In this work, the freestanding defective ammonium vanadate@MXene (d-NVO@MXene) hybrid film was synthesized by simple vacuum filtration strategy. Due to the presence of the hierarchical freestanding structure, outstanding MXene conductive networks and abundant oxygen vacancy (in the d-NVO nanoribbons), the d-NVO@MXene hybrid film can not only expose more active sites but also possess outstanding conductivity and kinetics of charge transfer/ion diffusion. When the d-NVO@MXene hybrid film was directly used as the cathode, it displayed a high specific capacity of 498 mAh/g at 0.5 A/g and superior cycling stability performance with near 100 % coulomb efficiency. Furthermore, the corresponding storage mechanism was elucidated by ex situ various characterizations. This work provides new ideas for the development of freestanding vanadium-based cathode materials for AZIBs. [ABSTRACT FROM AUTHOR]