Search

Bacterial pathogens cause pain and death, add significantly to the expense of healthcare globally, and pose a serious concern in many aspects of daily life. Additionally, they raise significant issues in other industries, including pharmaceuticals, clothing, and food packaging. Due to their unique properties, a great deal of attention has been given to biogenic metal nanoparticles, nanocomposites, and their applications against pathogenic bacteria. This study is focused on biogenic silver and copper nanoparticles and their composites (UL/Ag2 O-NPS, Ul/CuO-NPs, and Ul/Ag/Cu-NCMs) produced by the marine green alga Ulva lactuca. The characterization of biogenic nanoparticles UL/Ag2 O-NPS and Ul/CuO-NPs and their composites Ul/Ag/Cu-NCMs has been accomplished by FT-IR, SEM, TEM, EDS, XRD, and the zeta potential. Minimum inhibitory concentration (MIC) and minimum bactericidal concentration (MBC) experiments were conducted to prove antibacterial activity against both Gram-positive and Gram-negative bacteria and anti-biofilm. The FTIR spectroscopy results indicate the exiting band at 1633 cm−1, which represents N–H stretching in nanocomposites, with a small shift in both copper and silver nanoparticles, which is responsible for the bio-reduction of nanoparticles. The TEM image reveals that the Ul/Ag/Cu-NCMs were hexagonal, and the size distribution ranged from 10 to 35 nm. Meanwhile, Ul/CuO-NPs are rod-shaped, whereas UL/Ag2 O-NPS are spherical. The EDX analysis shows that Cu metal was present in a high weight percentage over Ag in the case of bio-Ag/Cu-NCMs. The X-ray diffraction denotes that Ul/Ag/Cu-NCMs, UL/CuO-NPs, and UL/Ag2 O-NPS were crystalline. The results predicted by the zeta potential demonstrate that Ul/Ag/Cu-NCMs were more stable than Ul/CuO-NPs. The antibacterial activity of UL/Ag2 O-NPS, Ul/Ag/Cu-NCMs, and UL/CuO-NPs was studied against eleven Gram-negative and Gram-positive multidrug-resistant bacterial species. The maximum inhibition zones were obtained with UL/Ag2 O-NPS, followed by Ul/Ag/Cu-NCMs and Ul/CuO-NPs in all the tested bacteria. The maximum anti-biofilm percentage formed by E. coli KY856933 was obtained with UL/Ag2 O-NPS. These findings suggest that the synthesized nanoparticles might be a great alternative for use as an antibacterial agent against different multidrug-resistant bacterial strains. [ABSTRACT FROM AUTHOR]

Zinc oxide nanoparticles have many advantages for nano-biotechnologists due to their intense biomedical applications. ZnO-NPs are used as antibacterial agents, which influence bacterial cells through the rupture of the cell membrane and the generation of reactive free radicals. Alginate is a polysaccharide of natural origin due to its excellent properties that are used in various biomedical applications. Brown algae are good sources of alginate and are used as a reducing agent in the synthesis of nanoparticles. This study aims to synthesize ZnO-NPs by using brown alga Fucus vesiculosus (Fu/ZnO-NPs) and also to extract alginate from the same alga, which is used in coating the ZnO-NPs (Fu/ZnO-Alg-NCMs). The characterizations of Fu/ZnO-NPs and Fu/ZnO-Alg-NCMs were determined by FTIR, TEM, XRD, and zeta potential. The antibacterial activities were applied against multidrug resistance bacteria of both gram-positive and negative. The results obtained in FT-TR showed there are some shifts in the peak positions of Fu/ZnO-NPs and Fu/ZnO-Alg-NCMs. The peak at 1655 cm−1, which assigned amide I-III, is present in both Fu/ZnO-NPs and Fu-Alg-ZnO-NCMs; this band is responsible for bio-reductions and stabilization of both nanoparticles. The TEM images proved the Fu/ZnO-NPs have rod shapes with sizes ranging from 12.68 to 17.66 and are aggregated, but Fu/ZnO/Alg-NCMs are spherical in shape with sizes ranging from 12.13 to 19.77. XRD-cleared Fu/ZnO-NPs have nine sharp peaks that are considered good crystalline, but Fu/ZnO-Alg-NCMs have four broad and sharp peaks that are considered semi-crystalline. Both Fu/ZnO-NPs and Fu/ZnO-Alg-NCMs have negative charges (−1.74 and −3.56, respectively). Fu/ZnO-NPs have more antibacterial activities than Fu/ZnO/Alg-NCMs in all tested multidrug-resistant bacterial strains. Fu/ZnO/Alg-NCMs had no effect on Acinetobacter KY856930, Staphylococcus epidermidis, and Enterobacter aerogenes, whereas there was an apparent effect of ZnO-NPs against the same strains. [ABSTRACT FROM AUTHOR]

One of the most prevalent chronic infectious disorders is tooth decay. Acids produced when plaque bacteria break down sugar in the mouth cause tooth decay. Streptococcus mutans and Lactobacillus acidophilus are the most prominent species related to dental caries. Innovative biocidal agents that integrate with a biomaterial to prevent bacterial colonization have shown remarkable promise as a result of the rapid advancement of nanoscience and nanotechnology. In this study, Ulva lactuca was used as a cellulose source and reducing agent to synthesize nanocellulose and Ulva/Ag/cellulose/nanocomposites. The characterizations of nanocellulose and Ulva/Ag/cellulose/nanocomposites were tested for FT-IR, TEM, SEM, EDS, XRD, and zeta potential. Ulva/Ag/cellulose/nanocomposites and Ulva/nanocellulose, both blended with fluoride, were tested as an antibacterial against S. mutans ATCC 25175 and L. acidophilus CH-2. The results of the SEM proved that nanocellulose is filament-shaped, and FT-IR proved that the functional groups of Ulva/nanocellulose and Ulva/Ag/cellulose/nanocomposites and cellulose are relatively similar but present some small diffusion in peaks. The TEM image demonstrated that the more piratical size distribution of Ulva/Ag/cellulose/nanocomposites ranged from 15 to 20 nm, and Ulva/nanocellulose ranged from 10 to 15 nm. Ulva/Ag/cellulose/nanocomposites have higher negativity than Ulva/nanocellulose. Ulva/Ag/cellulose/nanocomposites and Ulva/nanocellulose possess antibacterial activity against S. mutans ATCC 25175 and L. acidophilus CH-2, but Ulva/Ag/cellulose/nanocomposites are more effective, followed by that blended with fluoride. It is possible to use Ulva/Ag/cellulose/nanocomposites as an antimicrobial agent when added to toothpaste. It is promising to discover an economic and safe nanocomposite product from a natural source with an antimicrobial agent that might be used against tooth bacteria. [ABSTRACT FROM AUTHOR]