Search

Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As‐prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1‐89.1 MPa at high porosity levels of 66.0%‐87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high‐performance alumina ceramic foams toward practical applications. [ABSTRACT FROM AUTHOR]

The weak compressive strength of dried ceramic foams is a disadvantage of fabricating ultralight ceramic foams, especially for the ceramic foams with porosity exceeding 95%. In this study, dried alumina foams were enhanced by agar and PVA-freezing-thawing using sodium dodecyl sulfate as surfactant. It is found that the two additives have no negative influence on adsorption of sodium dodecyl sulfate on alumina particles as well as the hydrophobic character of alumina particles. Stable alumina particle-stabilized foams were prepared with less than 0.5 wt% agar and 1.0 wt% PVA. High additive concentration above the critical values weakens stability of wet foams, which is probably due to the aggregate of alumina particles caused by long-chain molecules connecting. The compressive strength of dried alumina foams has a significant improvement with the employment of agar and PVA-freezing-thawing. The dried foams prepared with 1wt% PVA assisted by freezing-thawing has porosity of 97.1% and compressive strength of 0.16 MPa, which could maintain integrity of dried foams without destruction in the fabricating process. [ABSTRACT FROM AUTHOR]

Abstract The mechanical strength of highly porous ceramic foams shows significant attenuation with the increase of porosity, especially for ceramic foams with very high porosity level above 95%. Ultra-light bulk composite ceramic foams were fabricated via introducing 20 wt% zirconia in alumina-based cell wall, aiming at improving mechanical strength of alumina based ceramic foams. The preparation and stability of alumina and zirconia particles synergistically stabilized foams were investigated. The obtained bulk ceramic foams manifested an exciting combination of both high porosity above 96% and excellent specific compressive strength, due to their closed pore structure, defect-free cell wall with uniform thickness, and uniformly distributed zirconia grains in alumina matrix. The alumina/zirconia composite ceramic foams with porosity of 96.7% exhibited compressive strength of 1.11 ± 0.07 MPa, which was much higher than that of alumina ceramic foams in the case of same porosity. [ABSTRACT FROM AUTHOR]

Mechanically robust alumina ceramics with low shrinkage were successfully prepared via gelcasting using Isobam as the gelling agent and pre-sintered alumina powder as the raw material for the first time. The influence of amount of pre-sintered alumina powder and powder's pre-sintering temperature on the viscosity of suspension and mechanical properties of low-shrinkage alumina ceramics were systematically investigated. The results showed that low-shrinkage alumina ceramics with flexural strength of 294.5 ± 33.0 MPa, linear shrinkage of 7.79% and relative density of 91.5% can be obtained with the addition of 60 wt% alumina powder pre-sintered at 1600 °C. This convenient and facile approach is promising to fabricate low-shrinkage alumina ceramics with large sizes, high dimensional accuracy and complex shapes. [ABSTRACT FROM AUTHOR]

Graphical abstract Highlights • Carbamate functional group was grafted onto carbon black surface. • Hierarchical PACs with 3D reticular architectures were fabricated. • PACs showed superior high-temperature particulate matter filtration. Abstract Porous ceramics with high porosity and extensive interconnected pores have great application potential in fields ranging from dye removal to high-temperature particulate matter (PM) capture. However, constructing these materials to achieve efficient filtration is extremely challenging. Herein, a novel strategy to create hierarchical-structured porous alumina ceramics (PACs) with three-dimensional (3D) reticular architecture is reported based on polyurethane (PU) foaming method. To ensure the efficient flow-through filtration, carbamate-grafted carbon black is used as the pore-forming agent and assembled into the porous PU framework. Submicron and micron-sized pores on the cell walls are observed in hierarchical-structured PACs. This unique structure enables a high PM removal efficiency (94.1%) at an ultralow pressure drop (20 Pa). Our work has demonstrated great application potentials of as-prepared PACs as an efficient high-temperature PM filter and provided new insights to develop highly effective filter. [ABSTRACT FROM AUTHOR]

Abstract In the present work, Al 2 O 3 -Si 3 N 4 porous ceramics with a cactus-like architecture were fabricated by calcining Al 2 O 3 -Si binary particle-stabilized foams in the nitrogen atmosphere. A large number of acicular Si 3 N 4 nanobelts were constructed on the surface of cell walls as a consequence of CVD process to achieve an interlaced network. Such structure was beneficial to realize a high capture efficiency of particulate matters (PM) during filtration. Resultant products having a bulk density of 0.38 g/cm3 at an apparent porosity of 86% can potentially be applied as the air filters in environment field. [ABSTRACT FROM AUTHOR]

In order to reduce thermal conductivity but to exhibit better mechanical properties of porous alumina ceramics (PACs), a novel approach, based on the modification of pore structures (i.e. mean pore size, micro-pore proportions and pore shape factor) by impregnation of alumina sol, is reported in the present work. The properties of as-impregnated samples were compared with commercial alumina hollowsphere bricks. Results show that impregnation of alumina sol in PACs has a positive influence on pore structures, leading to a superior strength and a lower thermal conductivity. In particular, when 8 wt% alumina sol solid content is impregnated, the crushing strength (35.3 MPa) and thermal conductivity (0.15 W/m K at 200 °C) of sample are much better than that of the commercial alumina hollowsphere bricks. This novel method for excellent PACs provides promising applications as insulating lining materials in the fields of industrial furnace. [ABSTRACT FROM AUTHOR]

A novel temperature induced gelation method for alumina suspension using oleic acid as dispersant is reported. Non–aqueous suspension with high solid loading and low viscosity is prepared using normal octane as solvent. Influence of oleic acid on the dispersion of suspension was investigated. There was a well disperse alumina suspension with 1.3 wt% oleic acid. Influence of gelation temperature on the coagulation process and properties of green body was investigated. The sufficiently high viscosity to coagulate the suspension was achieved at −20 °C. The gelation temperature was controlled between the melting point of dispersant and solvent. The gelation mechanism is proposed that alumina suspension is destabilized by dispersant separating out from the solvent and removing from the alumina particles surface. The alumina green body with wet compressive strength of 1.07 MPa can be demolded without deformation by treating 53 vol% alumina suspension at −20 °C for 12 h. After being sintered at 1550 °C for 3 h, dense alumina ceramics with relative density of 98.62% and flexural strength of 371±25 MPa have been obtained by this method. [ABSTRACT FROM AUTHOR]