Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As‐prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1‐89.1 MPa at high porosity levels of 66.0%‐87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high‐performance alumina ceramic foams toward practical applications. [ABSTRACT FROM AUTHOR]

The weak compressive strength of dried ceramic foams is a disadvantage of fabricating ultralight ceramic foams, especially for the ceramic foams with porosity exceeding 95%. In this study, dried alumina foams were enhanced by agar and PVA-freezing-thawing using sodium dodecyl sulfate as surfactant. It is found that the two additives have no negative influence on adsorption of sodium dodecyl sulfate on alumina particles as well as the hydrophobic character of alumina particles. Stable alumina particle-stabilized foams were prepared with less than 0.5 wt% agar and 1.0 wt% PVA. High additive concentration above the critical values weakens stability of wet foams, which is probably due to the aggregate of alumina particles caused by long-chain molecules connecting. The compressive strength of dried alumina foams has a significant improvement with the employment of agar and PVA-freezing-thawing. The dried foams prepared with 1wt% PVA assisted by freezing-thawing has porosity of 97.1% and compressive strength of 0.16 MPa, which could maintain integrity of dried foams without destruction in the fabricating process. [ABSTRACT FROM AUTHOR]

Abstract In the present work, Al 2 O 3 -Si 3 N 4 porous ceramics with a cactus-like architecture were fabricated by calcining Al 2 O 3 -Si binary particle-stabilized foams in the nitrogen atmosphere. A large number of acicular Si 3 N 4 nanobelts were constructed on the surface of cell walls as a consequence of CVD process to achieve an interlaced network. Such structure was beneficial to realize a high capture efficiency of particulate matters (PM) during filtration. Resultant products having a bulk density of 0.38 g/cm3 at an apparent porosity of 86% can potentially be applied as the air filters in environment field. [ABSTRACT FROM AUTHOR]