The instability of the keyhole and bubble being captured by solidification interface are the main factors that affect the formation of porosity in laser welding of both aluminum alloy and steel. In laser welding of aluminum alloy, the more violent fluid flow behind the keyhole, the larger depth to width ratio can cause the keyhole more unstable, and susceptive to collapse that can be described as three necessary steps. The much larger solidification rate and longer escaping distance make the bubble easily captured by the solidification interface, and easily combined. All of these reasons contribute to the formation of larger number and size of porosity in laser welding of aluminum alloy. The numerical and experimental results are in good agreement. [ABSTRACT FROM AUTHOR]

The droplet escape condition is established, a three-dimensional numerical model is built to investigate the behavior of the weld pool in fiber laser welding of 5083 aluminum alloy, the shear stress caused by the metallic vapor flow that has great influence on spatter formation is considered. A high speed photography system is used to capture the transient images of the weld pool, the spatter formation is discussed. The numerical and experimental results show that the spatters generate mainly around the keyhole. Two factors are responsible for the spatter formation: the surface tension of the molten metal around the keyhole is low. The recoil pressure caused by evaporation and the shear stress caused by metallic vapor flow accelerate the upward moving melt around the keyhole. Increasing the welding speed and placing the nozzle at the trailing position can decrease the upward momentum of the molten metal around the keyhole, and stabilize the keyhole, which are help to suppress the formation of spatter. [ABSTRACT FROM AUTHOR]

This paper concerns the dynamic variation in plume velocity and keyhole size during the laser welding process of 5083 Al-alloy. The keyhole size and plume velocity were measured from high-speed images through imaging process methods and the particle image velocimetry (PIV) method. The correlation between the oscillation in plume velocity and keyhole size was discussed based on the pressure balance inside the keyhole. Results show that the keyhole keeps opening and collapsing during the welding process. During the time the keyhole is open, the size of the keyhole continuously oscillates until it collapses. Plume velocity increases to a maximum at the initial stage of keyhole's opening, and then varies in synchronisation with the oscillation of the keyhole size. It is considered that local evaporation occurs on the humps of the keyhole front wall, which results in the oscillation in plume velocity. The oscillation in plume velocity then leads to the variation in the pressure balance in the keyhole and drives the keyhole to expand or shrink accordingly. [ABSTRACT FROM AUTHOR]