The keyhole behaviors were observed directly by laser welding experiment with quartz glass. Based on Fresnel absorption of laser beam and multi-reflection combined with volume of fluid (VOF) method, a three-dimensional mathematical model was established to study the role of welding speed on keyhole behaviors and keyhole-induced porosity formation in laser welding of aluminum alloy. The keyhole behaviors and weld pool fluid flow were discussed, and the result shows that, although the welding speed varies, the mechanism of keyhole collapse was similar. However, the keyhole stability at higher welding speed was improved due to reduced weld depth fluctuations, spatter number, keyhole depth to width ratio, and keyhole collapse frequency. Furthermore, the improved keyhole stability impeded the keyhole collapse, and the lower weld depth and solidification rate facilitated bubble escaping from the weld pool easily, which are the main factors for suppression of porosity at higher welding speed. [ABSTRACT FROM AUTHOR]

The droplet escape condition in laser welding is established in this paper. A three-dimensional numerical model is developed to study the weld pool convection and spatter formation at full penetration during the fiber laser welding of 5083 aluminum alloy. It is found that when laser power is 9 kW, the bottom of the keyhole is dynamically opened and closed. When the bottom of the keyhole is closed, the molten metal at the bottom of the back keyhole wall flows upwards along the fusion line. When the bottom of the keyhole is opened, few spatters can be seen around the keyhole at the top surface, two flow patterns exists in the rear part of the keyhole: a portion of molten metal flows upwards along the fusion line, other portion of molten metal flows to the bottom of the keyhole, which promote the spatter formation at the bottom of the keyhole rear wall. [ABSTRACT FROM AUTHOR]