Search

Objectives: The application of selective laser melting (SLM) to dentistry has been rapidly expanding; however, SLM-processed parts possess orientation-dependent properties (i.e., anisotropy) that can affect the long-term reliability of the dental prostheses. This study aimed to evaluate the anisotropic corrosion response of SLM-processed Co-Cr-Mo alloys under various heat treatments., Methods: Samples fabricated via SLM along the horizontal plane (x-y plane) and vertical plane (x-z plane), with respect to the build direction, were subjected to various heat treatments. The resulting microstructures of the samples were characterized, and their corrosion properties were evaluated using anodic polarization and immersion tests., Results: All samples showed similar transpassive behavior of the polarization curves. However, the immersion tests showed that the as-built x-z plane samples released significantly more metal ions than those fabricated on the x-y plane because of the larger area of preferentially corroded molten pool boundaries (MPBs) in the x-z plane samples. Our results further demonstrated that the heat treatments eliminated the MPBs, resulting in isotropic corrosion properties. However, excessive heat treatment at high temperatures induces the formation of coarse precipitates, resulting in a less-protective passive film., Significance: The post-build heat treatments at temperatures that eliminate the MPBs are effective in reducing anisotropic corrosion behavior, and the lowest possible temperature is suitable for reducing the amount of released metal ions. These findings are expected to facilitate the application of SLM in dentistry to allow fast and precise production of prosthetic devices., (Copyright © 2020 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.)

The artifact volume generated in magnetic resonance (MR) images was quantitatively evaluated to investigate how artifact behavior correlates to the magnetic susceptibility and volume of an implanted metal device. For this, a new low-magnetic-susceptibility Zr-14Nb alloy was compared with two conventional dental alloys, Ti-6Al-7Nb alloy and Co-Cr-Mo alloy, using spherical specimens of each alloy prepared with four different diameters. Then, MR images were recorded under fast spin echo and gradient echo conditions, from which the artifact volume was measured. The artifact volume decreased with the magnetic susceptibility, volume, and mass of the specimens, and significant linear correlations were observed. The artifact volume can be estimated by the equations presented here; nevertheless, further studies are necessary to interpret the influence of some important factors (e.g., imaging conditions, shape, and orientation) to predict the artifact volume more precisely.

The aim of this study was to investigate the bond strength of dental porcelain and the preheated Zr-14Nb alloy, and compare this strength with that of titanium. White oxide layers, which were predominantly composed of monoclinic zirconia, were formed on the preheated sample groups, and exhibited a greater roughness than the control samples. At the metal-ceramic interface, a greater Nb diffusion range was observed than in the control samples. The bond strengths of the samples subjected to 20min preheating treatment were the lowest (33.6 ± 3.2 MPa), which may be ascribed to the formation of a brittle thick oxide layer under excessive heat treatment. The samples subjected to this heat treatment for 5 min exhibited the highest mean bond strength (43.7 ± 5.9 MPa), which was significantly higher than that of titanium (35.3 ± 3.5 MPa). Thus, the Zr-14Nb alloy is a promising candidate for fixed dental prosthesis, as long as the appropriate treatment conditions are adopted., (Copyright © 2015 Elsevier Ltd. All rights reserved.)