Search

Abstract The effects of solution temperature and cooling rate on microstructure and micro-hardness of a hot compressed Ti-6Al-4V alloy are investigated. The microstructure observations reveal the occurrence of static recrystallization during solution treatment. The lamellar α phases firstly decompose into the short-rod phases, and then gradually spheroidize. The increased solution temperature can accelerate the transformation of α grain boundary from the low-angle grain boundaries (LAGB) to the high-angle grain boundaries (HAGB). So, the growth and spheroidization of α grains become more and more obvious. Meanwhile, the precipitation of secondary α phases is promoted. The micro-hardness is significantly improved after the solution treatment, i.e., the micro-hardness undergoes the rapid decrease and slow increase with raising the solution temperature. In addition, the cooling rate has great impact on the microstructures and micro-hardness. With reducing the cooling rate, the mean size of equiaxed α grains and the thickness of lamellar α phases obviously increase. Highlights • Effects of post-deformation heat treatment on microstructures and micro-hardness of Ti-6Al-4V alloy are studied. • Lamellar α phases firstly decompose into the short-rod phases, and then gradually spheroidize. • The increased solution temperature accelerates the transformation of α grain boundary from LAGB to HAGB. • Micro-hardness undergoes the rapid decreases and slow increase with the increase of solution temperature. • The mean size of equiaxed α grains and the thickness of lamellar α phases increase with reducing cooling rate. [ABSTRACT FROM AUTHOR]

Cu-15Ni-8Sn coatings were prepared using atmospheric plasma spraying. The influences of arc current and aging treatment on the microstructure, mechanical and tribological properties were investigated. The coating microstructure, the wear track and the wear debris were observed and analyzed. The melting state of the particles is improved by increasing of arc current. The hardness of the aged coatings is higher than the as-sprayed coatings. The wear resistance of the aged coatings is 3–4 times higher than the as-sprayed coatings. The continuous smooth tribolayer formed on the wear tracks contributes to the low wear rate of aged coatings. The dominant wear mechanism of the coatings is delamination coupled with spalling under dry sliding condition. This work provides an effective method for producing spinodal alloy coatings with enhanced mechanical and tribological properties. [ABSTRACT FROM AUTHOR]

Spheroidization and dynamic recrystallization (DRX) mechanisms of a Ti-55511 alloy during hot compression in α+β region is investigated. It is found that the spheroidization of lamellar α phases and DRX of β phases, which are obviously influenced by deformation conditions, are the main softening mechanisms. The spheroidization fraction of lamellar α phases first increases with the raised temperature or strain rate. However, the spheroidization fraction of lamellar α phases begins to drop at about 700 °C as the strain rate is higher than 0.01 s−1, and the maximum spheroidization fraction of lamellar α phase is about 2.3%. This phenomenon is attributed to the Implanting-Mechanism, which is induced by the common or close orientation relationships of the spheroidized and equiaxed α phases, as well as few dislocations between the spheroidized and equiaxed α phases. Contrarily, the lamellar α phases are obstructed from equiaxed α phases by a mass of dislocations. Additionally, the DRX degree of β phases increases with the reduced temperature or the raised strain rate. • Spheroidization and DRX mechanisms of a Ti-55511 alloy during hot compression in α+β region is investigated. • Spheroidization fraction of lamellar α phase first increases then drops with the raised strain rate. • The maximum spheroidization fraction of lamellar α phase is about 2.3% near 700 °C and 0.01 s−1. • Implanting-Mechanism, induced by the close orientation relationships of spheroidized and equiaxed α phases, is proposed. • The DRX extent of β phases increases with the reduced temperature and raised strain rate. [ABSTRACT FROM AUTHOR]

The hot deformation behavior and microstructural evolution of a Ti-55511 alloy in α+β region are investigated by uniaxial compressive tests at elevated temperatures. Transmission Electron Microscope (TEM) and Electron Backscattered Diffraction (EBSD) are employed to observe the microstructures. The spheroidization of lamellate α phases and the dynamic recrystallization (DRX) of β grains are analyzed. It is observed that the flow characteristics are prominently affected by deformation parameters, i.e., the flow stress, peak stress and flow softening stress decrease with the reduced strain rate or the increased deformation temperature. When the deformation temperature is slightly raised or the strain rate is properly reduced, the fraction of spheroidized α phase greatly increases. The substructures are formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. Then, the lamellate α phase is fragmentized and spheroidized. The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. Additionally, the higher dislocation density and obvious dislocation pile-ups can be noticed at the α/β interface, which induces the DRX nucleation of β grains at the α/β interface. • Hot deformation behavior and microstructure evolution of a Ti-55511 alloy in α+β region are investigated. • The fraction of spheroidized α phase increases with increasing deformation temperature or reducing strain rate. • The substructures are easily formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. • The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. • The obvious DRX of β grains easily nucleate at the α/β interface. [ABSTRACT FROM AUTHOR]