The effects of chromium content on microstructure, hardness and wear resistance of as-cast Fe-xCr-1.0B (x = 0, 4, 8, 12, 16, 20) alloys were investigated by means of optical microscope (OM), scanning electron microscope (SEM), x-ray diffractometer (XRD), hardness tester and ring block wear tester. The results showed that the microstructures of chromium-free alloy were mainly composed of pearlite, ferrite, and eutectic borocarbides, and the hardness was very low, only 18.8 HRC. With the increase in chromium content, the matrix of as-cast Fe-Cr-B alloy gradually began to transform from pearlite and ferrite to lath martensite, and the type of borocarbides changed from Fe2(B, C) to M2(B, C), M7(C, B)3 and M23(C, B)6 (M = Fe, Cr). When the chromium content was 12 wt.%, the hardness of alloy reached the highest value of 61.1 HRC, and the wear resistance of alloy was the best. The results of worn surface analysis showed that the wear failure of as-cast Fe-Cr-B alloy was mainly caused by multiple plastic deformation and micro-cutting. [ABSTRACT FROM AUTHOR]

Highlights: [•] The as-received microstructure of bulk Fe2B comprises iron and silicon borides. [•] The orientation of Fe2B in liquid zinc strongly affects on corrosion resistance. [•] The Fe2B/FeB phase transition process of bulk Fe2B in liquid zinc occurs. [•] Phase transition and spalling dominate corrosion of Fe2B in liquid zinc. [Copyright &y& Elsevier]

The effects of orientation and lamellar spacing on the interface microstructure and corrosion behavior of a directionally solidified (DS) Fe-B alloy in a hot-dip galvanization bath were investigated. The results indicated that the microstructure of the DS Fe-B alloy consisted of oriented α -Fe and Fe 2 B grains. The oriented Fe 2 B with [002] preferred growth orientation displayed low-angle grain boundaries on the Fe 2 B (001) basal plane. The DS Fe-B alloy with Fe 2 B vertical to the corrosion interface possessed the best corrosion resistance to liquid zinc owing to the formation of an interface-pinning multilayer induced by the Fe 2 B orientation. The epitaxially grown columnar ζ-FeZn 13 products were controlled by the geometric constraint of Fe 2 B grain orientation and size, and a mechanism model that explains the interfacial orientation-pinning behavior is discussed in detail. Transmission electron microscopy (TEM) results revealed that the possible orientation relationships of the oriented Fe 2 B and columnar ζ-FeZn 13 products are (001) Fe2B //(−402) ζ-FeZn13 and [002] Fe2B //[110] ζ-FeZn13 . The corrosion damage of the DS Fe-B alloy with Fe 2 B [002] orientation vertical to the corrosion interface in liquid zinc was governed by the competitive mechanisms of Fe 2 B/FeB transformation and microcrack-spallation resistance, which is proposed as being the result of a multiphase synergistic effect in the micro-structures. [ABSTRACT FROM AUTHOR]