Different weight ratios of cerium (0.5, 1 and 2 wt.%) were produced in a controlled atmosphere by High Pressure Die Cast method to Mg-6Al-0.3Mn-1Sn alloy. The influence of cerium on microstructure and high-temperature mechanical properties was investigated. The microstructure study revealed that the main alloy contains intermetallic phases such as alpha-Mg, beta- Mg17Al12, Mg2Sn and Al11Ce3. The hardness values of the alloys were increased with the addition of 0.5%, 1 and 2 cerium. With the addition of 0.5 wt.% Ce, the yield strength increased to 145 MPa. With the addition of 2 wt.% of Ce, it was found to be 160 MPa with an increase of 14%. Tensile strength was obtained as 190 MPa. Elevated temperature tensile test was carried out at 120 degrees C, 180 degrees C and 240 degrees C, to all the alloys. It was found that increased Ce ratio increased the high-temperature mechanical strength. At 120 degrees C, the highest tensile and yield strength values were obtained with 159 MPa and 147 MPa, respectively, in the alloy with 2% wt. cerium added. In the tensile test performed at 180 degrees C, the highest tensile and yield strength were measured as 91 MPa and 77 MPa, respectively. The operating temperature of Mg alloys produced industrially by HPDC has a significant effect on mechanical properties. High operating temperatures reduce mechanical properties. However, the mechanical properties at high test temperatures were increased by the addition of Ce metal to the AM60-1Sn-XCe alloy produced with HPDC.

In the present study, the effect of an La alloying element with different quantities (1, 3 and 5 wt.-%) on the microstructure, mechanical and dry sliding wear properties of Mg- 3Al-3Sn-3Sb alloy was investigated. The wear tests were done on the alloys using pin on-disk equipment against a 4140 steel disc as counterpart under three different sliding velocities of 0.3, 0.6 and 1.2 ms-1 and four different loads of 5, 10, 20 and 40 N. The microstructural results showed that the new intermetallic phases (La5Sn3 and LaSnSb2) were formed with addition of La to the main alloy. Also, it was observed that the hardness of the Mg-3Al-3Sn-3Sb alloy was raised with increasing La addition. Furthermore, the tensile properties of the Mg-3Al-3Sn-3Sb alloy improved with rising La content at room and elevated temperature. The wear rates of the alloys increase with increasing of the sliding speed and load. In addition to this, the wear rate of the Mg-3Al-3Sn-3Sb alloy was found to be higher than that of the La content alloys for all test conditions.