Search

The precipitation behavior of α phase in a β-quenched Ti-55511 alloy during high-temperature compression is investigated. The influences of deformation parameters on the flow characteristics, microstructural evolution, as well as the precipitation behavior of α phase, are discussed. Results show that the flow stress features and the dominant softening mechanism are sensitive to the deformation parameters. At low strain rates or high deformation temperatures, the main softening mechanism is dynamic recovery. But, the dynamic recrystallization becomes the dominant softening mechanism at high strain rates or low temperatures. At low strain rates, the continuous strengthening, induced by the pinning effect of α precipitates, happens at the late period of deformation. Distribution of α precipitates is not greatly affected by deformation parameters. In the region near β grain boundary, α precipitates are densely distributed with few orientations. While in the central region of β grain, the α precipitates are distributed a bit more sparsely with several scattering orientations. In addition, with increasing deformation temperature, the content, aspect ratio and size of α phases decrease. However, with increasing strain rate, the content, aspect ratio and size first increase and then decrease. Furthermore, the peak value of aspect ratio appears at 0.01 s−1. • Precipitation behavior of α phase in a β-quenched Ti-55511 alloy during hot compression is studied. • At low strain rates or high deformation temperatures, the main softening mechanism is dynamic recovery. • Dynamic recrystallization is the dominant softening mechanism at high strain rates or low temperatures. • α precipitates are distributed a bit more sparsely with several scattering orientations within β grains. • With increasing deformation temperature, the content, aspect ratio and size of α phases decrease. [ABSTRACT FROM AUTHOR]

Abstract The effects of solution temperature and cooling rate on microstructure and micro-hardness of a hot compressed Ti-6Al-4V alloy are investigated. The microstructure observations reveal the occurrence of static recrystallization during solution treatment. The lamellar α phases firstly decompose into the short-rod phases, and then gradually spheroidize. The increased solution temperature can accelerate the transformation of α grain boundary from the low-angle grain boundaries (LAGB) to the high-angle grain boundaries (HAGB). So, the growth and spheroidization of α grains become more and more obvious. Meanwhile, the precipitation of secondary α phases is promoted. The micro-hardness is significantly improved after the solution treatment, i.e., the micro-hardness undergoes the rapid decrease and slow increase with raising the solution temperature. In addition, the cooling rate has great impact on the microstructures and micro-hardness. With reducing the cooling rate, the mean size of equiaxed α grains and the thickness of lamellar α phases obviously increase. Highlights • Effects of post-deformation heat treatment on microstructures and micro-hardness of Ti-6Al-4V alloy are studied. • Lamellar α phases firstly decompose into the short-rod phases, and then gradually spheroidize. • The increased solution temperature accelerates the transformation of α grain boundary from LAGB to HAGB. • Micro-hardness undergoes the rapid decreases and slow increase with the increase of solution temperature. • The mean size of equiaxed α grains and the thickness of lamellar α phases increase with reducing cooling rate. [ABSTRACT FROM AUTHOR]

The hot deformation behavior and microstructural evolution of a Ti-55511 alloy in α+β region are investigated by uniaxial compressive tests at elevated temperatures. Transmission Electron Microscope (TEM) and Electron Backscattered Diffraction (EBSD) are employed to observe the microstructures. The spheroidization of lamellate α phases and the dynamic recrystallization (DRX) of β grains are analyzed. It is observed that the flow characteristics are prominently affected by deformation parameters, i.e., the flow stress, peak stress and flow softening stress decrease with the reduced strain rate or the increased deformation temperature. When the deformation temperature is slightly raised or the strain rate is properly reduced, the fraction of spheroidized α phase greatly increases. The substructures are formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. Then, the lamellate α phase is fragmentized and spheroidized. The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. Additionally, the higher dislocation density and obvious dislocation pile-ups can be noticed at the α/β interface, which induces the DRX nucleation of β grains at the α/β interface. • Hot deformation behavior and microstructure evolution of a Ti-55511 alloy in α+β region are investigated. • The fraction of spheroidized α phase increases with increasing deformation temperature or reducing strain rate. • The substructures are easily formed in the lamellate α phase, and the β phase wedges into the lamellate α phase. • The DRX of β grains is promoted with the raised strain rate or the reduced deformation temperature. • The obvious DRX of β grains easily nucleate at the α/β interface. [ABSTRACT FROM AUTHOR]