Multiferroic 2-2 type layered NFO/ (Pb0.50Sr0.50) TiO3 composite thin film on Pt/TiO2/Si substrate was prepared by novel metallo-Organic process using spin coating technique. The structural and surface morphology were confirmed by X-Ray diffraction (XRD) atomic force microscope (AFM). Significantly improved ferroelectric properties (Ps ∼ 8.69, Pr ∼ 3.19 μC/cm2 and Ec ∼ 419kV/cm) and magnetic properties (Ms), (Mr) and (Hc) is (104emu/cc, 0.8emu/cc and 25Oe.) were observed at room temperature. Our observation provides an effective way to manipulate the conduction behavior to understand the leakage current density of multiferroic composites film at the interface. Poole-Frankel tunneling conduction mechanism dominates the leakage current of films in the relatively high electric filed. [ABSTRACT FROM AUTHOR]

Multiferroic 2-2 type bi-layered NFO/ (Pb0.80Sr0.20) TiO3 composite thin film on Pt/TiO2/Si substrate was prepared by novel metallo-Organic process using spin coating technique. The structural and surface morphology were confirmed by X-Ray diffraction (XRD) atomic force microscope (AFM). Significantly improved ferroelectric properties (Ps ~ 17.25, Pr ~8.02 µC/cm² and Ec ~ 404kV/cm) and magnetic properties (Ms ~ 117emu/cc, Mr ~ 0.83emu/cc and Hc ~ 20Oe) were observed at room temperature. The leakage current densities in NFO/PST composites film have been studied. Poole-Frankel bulk limited conduction mechanism dominates of film at relatively high electric filed. [ABSTRACT FROM AUTHOR]

(Pb0.60Sr0.40) TiO3-CFO composite thin films were grown on Pt/TiO2/Si substrate by novel metallo-Organic process using spin coating technique. The structural, surface morphology and micro structural properties were confirmed by X-Ray diffraction (XRD), Raman spectroscopy, atomic force microscope (AFM) and TEM respectively. The lattice constant of the composite thin film crystallized in the pervoskite and spinel phase was 3.9531 and 8.571 Å. Excellent ferroelectric behavior at 10V was observed, a room temperature magnetic hysteresis shows good results. The saturation magnetization value of the bilayer thin film is lower than that of the pure CFO film which is may be attributed to presence of non ferromagnetic PST layer A high initial behavior of dynamic ME response coefficient for the film was observed. The ME effect of the film strongly depends on the magnetic bias. [ABSTRACT FROM AUTHOR]