Search

The aim of this study is to reduce the manufacturing cost of a hydrophobic and heat-insulating silica aerogel and promote its industrial application in the field of thermal insulation. Silica aerogels with hydrophobicity and thermal-insulation capabilities were synthesized by using water-glass as the silicon source and supercritical drying. The effectiveness of acid and alkali catalysis is compared in the formation of the sol. The introduction of sodium methyl silicate for the copolymerization enhances the hydrophobicity of the aerogel. The resultant silica aerogel has high hydrophobicity and a mesoporous structure with a pore volume exceeding 4.0 cm3·g−1 and a specific surface area exceeding 950 m2·g−1. The obtained silica aerogel/fiber-glass-mat composite has high thermal insulation, with a thermal conductivity of less than 0.020 W·m−1·K−1. The cost-effective process is promising for applications in the industrial preparation of silica aerogel thermal-insulating material. [ABSTRACT FROM AUTHOR]

Poor cycling performance caused by massive volume expansion of silicon (Si) has always hindered the widespread application of silicon-based anode materials. Herein, bi-continuous silicon/carbon (Si/C) anode materials are prepared via magnesiothermic reduction of silica aerogels followed by pitch impregnation and carbonization. To fabricate the expected bi-continuous structure, mesoporous silica aerogel is selected as the raw material for magnesiothermic reduction. It is successfully reduced to mesoporous Si under the protection of NaCl. The as-obtained mesoporous Si is then injected with molten pitch via vacuuming, and the pitch is subsequently converted into carbon at a high temperature. The innovative point of this strategy is the construction of a bi-continuous structure, which features both Si and carbon with a cross-linked structure, which provides an area to accommodate the colossal volume change of Si. The pitch-derived carbon facilitates fast lithium ion transfer, thereby increasing the conductivity of the Si/C anode. It can also diminish direct contact between Si and the electrolyte, minimizing side reactions between them. The obtained bi-continuous Si/C anodes exhibit excellent electrochemical performance with a high initial discharge capacity of 1481.7 mAh g−1 at a current density of 300 mA g−1 and retaining as 813.5 mAh g−1 after 200 cycles and an improved initial Coulombic efficiency of 82%. The as-prepared bi-continuous Si/C anode may have great potential applications in high-performance lithium-ion batteries. [ABSTRACT FROM AUTHOR]

Cellulose aerogels are the latest generation of aerogels and have also received extensive attention due to their renewable and biocompatible properties. Herein, cellulose aerogel was facilely prepared by using NaOH/urea solution as solvent, raising the temperature to control gelation and drying wet gel sequentially. With NaOH/urea solution as solvent, the cellulose concentration has an important impact on the micromorphology of cellulose aerogels, while the aging time rarely affects the micromorphology. The appropriate solvent and drying method allow the formation of different cellulose crystalline structures. Different from the Cellulose Ⅰ crystalline structure of raw cellulose powder, the cellulose phase of as-prepared cellulose aerogels belongs to the Cellulose Ⅱ crystalline structure, and to some extent the pyrolysis temperature is also lower than that of raw cellulose powder. The resultant cellulose aerogel prepared by using NaOH/urea solution as solvent and freeze-drying has a uniform macroporous structure with a macropore size of 1~3 µm. [ABSTRACT FROM AUTHOR]

Microwave heating technology is known as an alternative to traditional gas and electric heating sources. In this work, mesoporous methylsilsesquioxane (MSQ) aerogels were prepared via a sol–gel process accompanied by microwave heating technology, and microwave heating was used in the gelation of sol and the drying of wet gels, respectively. The effects of hexadecyltrimethylammonium chloride (CTAC) as a surfactant and template, hydrochloric acid (HCl) as a catalyst, ethanol as a solvent, sodium hydroxide (NaOH) as a gelation agent, and microwave power on the pore structure of as-prepared MSQ aerogels were investigated in detail. Microwave heating at low power results in the acceleration of sol–gel transition and achieves the gelation within a few minutes. Appropriate amounts of chemical reagents and microwave heating at high power allow the preparation of mesoporous MSQ aerogels with a BET-specific surface area of 681.6 m2·g−1 and a mesopore size of 19 nm, and the resultant MSQ aerogel still has a BET specific surface area as high as 134 m2·g−1 after heat treatment at 600 °C for 2 h, showing high thermal stability. The MSQ aerogels/fibre composite possesses a low thermal conductivity of 0.039 W/(m·k)−1, displaying good thermal insulation. Microwave heating technology is a promising heating method for the preparation of other aerogels. [ABSTRACT FROM AUTHOR]

Hierarchically porous carbon aerogels (CAs) were prepared by organic condensation gelation method combined with atmospheric drying and pore-formation technology, followed by a carbonization process. With as-prepared CAs as substrate, the transition metal oxide nanoparticles loaded CAs composites (MnO2/Mn2O3@CA and Ni/NiO@CA) were achieved by means of liquid etching method combined with heat treatment, respectively. The catalyst, pore-forming agent and etching have important roles on the apparent density and pore structure of CAs. The hydrochloric acid (catalyst) significantly accelerates the gelation process and influences the size and distribution of macropores, whereas the addition of PEG2000 (pore-forming agent) and the etching of liquid solution leads to the formation of mesopore structure in CAs. Appropriate amounts of hydrochloric acid and PEG2000 allow the formation of hierarchically porous CAs with a BET surface area of 482.9 m2·g−1 and a macropore size of 11.3 μm. After etching and loading, the framework of CAs is etched to become a mesoporous structure, and the transition metal oxide nanoparticles can be uniformly loaded in CAs. These resultant composites have promising application in super capacitor, electrocatalysis, batteries and other fields. [ABSTRACT FROM AUTHOR]

Methylsilsesquioxane (MSQ) aerogels with uniform mesopores were facilely prepared via a sol–gel process followed by microwave drying with methyltrimethoxysilane (MTMS) as a precursor, hydrochloric acid (HCl) as a catalyst, water and methanol as solvents, hexadecyltrimethylammonium chloride (CTAC) as a surfactant and template, and propylene oxide (PO) as a gelation agent. The microstructure, chemical composition, and pore structures of the resultant MSQ aerogels were investigated in detail to achieve controllable preparation of MSQ aerogels, and the thermal stability of MSQ aerogels was also analyzed. The gelation agent, catalyst, solvent, and microwave power have important roles related to the pore structures of MSQ aerogels. Meanwhile, the microwave drying method was found to not only have a remarkable effect on improving production efficiency, but also to be conducive to avoiding the collapse of pore structure (especially micropores) during drying. The resulting MSQ aerogel microwave-dried at 500 W possessed a specific surface area up to 821 m2/g and a mesopore size of 20 nm, and displayed good thermal stability. [ABSTRACT FROM AUTHOR]

New flexible methylsilsesquioxane (MSQ) aerogels have been facilely prepared by a sol–gel process with methyltrimethoxysilane (MTMS) and dimethyldimethoxysilane (DMDMS) as co-precursors, followed by surface modification and ambient pressure drying. The microstructure, mechanical properties and hydrophobicity of these MSQ aerogels after surface modifications of hexamethyldisiloxane (HMDSO) and/or hexamethyldisilazane (HMDS) were investigated in detail, and the applications of surface-modified MSQ aerogels in sound-absorbance, fast dye adsorption and oil/water separation were evaluated, respectively. The MSQ aerogels surface-modified by HMDS possess flexibility, elasticity and superhydrophobicity, and demonstrate good performance in the mentioned applications. The resultant MSQ aerogel used in sound-absorbance has high frequency (about 6 kHz) acoustic absorptivity of up to 80%, benefiting from its macroporous structure and porosity of 94%, and it also possesses intermediate frequency acoustic absorptivity (about 1 kHz) up to 80% owing to its elasticity. This MSQ aerogel can selectively separate oil from oil/water mixtures with high efficiency due to its superhydrophobicity and superlipophilicity, resulting from a lot of methyl groups, density as low as 0.12 cm3·g−1 and a water contact angle as high as 157°. This MSQ aerogel can be assembled to be a monolithic column applied for fast dye adsorption, and shows selective adsorption for anionic dyes and removal efficiency of methyl orange of up to 95%. [ABSTRACT FROM AUTHOR]