Search

Ecofriendly wood-based materials are required by consumers at present. Decorative panels are part of a large group of wood-composite materials, and their environmental properties must not be neglected. More environmentally friendly decorative panels can be achieved by various methods. This paper describes a method of production from larch bark. Tree bark, as a byproduct of the wood industry, is one of the research topics that have gained interest in the last decade, especially for its applications in biobased lignocomposites, with regard to the shrinkage of wood resources. In the present work, the formaldehyde content of decorative boards based on larch bark (0.6 g/cm³) was analyzed when bonded with five different types of adhesive systems: urea-formaldehyde, polyvinyl acetate, the mixture of 70% urea-formaldehyde + 30% polyvinyl acetate, polyurethane, and tannin-based adhesive. A self-agglomerated board was also analyzed. The formaldehyde content of the larch-bark samples was determined with the perforator method (EN 120:2011), and findings showed that all tested samples reached the E1 classification (≤8 mg/100 oven dry). Moreover, 75% of the values of the corrected formaldehyde content were included in the super-E0 class (≤1.5 mg/100 oven dry). In the case of boards bonded with tannin-based adhesive, this natural polymer acted as a formaldehyde scavenger., Competing Interests: The authors declare no conflict of interest.

With increasing concerns about the production of sustainable materials, the field of wood-based materials still offers a critical challenge. Indeed, a close dependence on petroleum derivatives is still required, involving high consumption of non-renewable and toxic chemicals in the assembly of wooden parts. Herein, the aim of this research was to evaluate the potentiality of an entirely renewable tannin-based adhesive for particleboard production. Industrial quebracho (Schinopsis balansae) tannin powder was selected as a raw material and analyzed in terms of polyphenols, polysaccharides, and the total condensed amount. Furfural was proposed as a bio-sourced hardener to establish crosslinking between the flavonoid units and hence produce a resin. This formulation was analyzed in terms of viscosity and curing time and then applied to laboratory-scale single-layer particleboard production. The density, mechanical properties, and thickness swelling of the panels were investigated at different glue ratios and pressing conditions. It was observed that time has a higher impact than temperature on the internal bond, and panels pressed at 160 °C for a longer pressing time (>7 min) performed better than the boards obtained at a higher temperature. The registered values at 160 °C for 11 min of pressing of internal bond (0.37 MPa) and modulus of elasticity (1417 MPa) met the required standards for P1 panels according to European norms EN 312 (2010). Conversely, the modulus of rupture (4.9 MPa) did not satisfy the requirements suggesting the need for the use of additive or post-treatments. Considering the results achieved, quebracho–furfural adhesives are an interesting base for bio-based adhesive formulations. [ABSTRACT FROM AUTHOR]

In order to improve the acceptance of broader industrial application of flax fiber reinforced beech (Fagus sylvatica L.) plywood, five different industrial applicated adhesive systems were tested. Epoxy resin, urea-formaldehyde, melamine-urea formaldehyde, isocyanate MDI prepolymer, and polyurethane displayed a divergent picture in improving the mechanical properties—modulus of elasticity, modulus of rupture, tensile strength, shear strength and screw withdrawal resistance—of flax fiber-reinforced plywood. Epoxy resin is well suited for flax fiber reinforcement, whereas urea-formaldehyde, melamine urea-formaldehyde, and isocyanate prepolymer improved modulus of elasticity, modulus of rupture, shear strength, and screw withdrawal resistance, but lowered tensile strength. Polyurethane lowered the mechanical properties of flax fiber reinforced plywood. Flax fiber reinforced epoxy resin bonded plywood exceeded glass fiber reinforced plywood in terms of shear strength, modulus of elasticity, and modulus of rupture. [ABSTRACT FROM AUTHOR]

The aim of this study is to investigate the performance of casein-based adhesives for the bonding of ash (Fraxinus spp.) veneers for the manufacture of biodegradable skis. Different formulations containing casein powder, water, lime, sodium silicate, and various glue amounts were tested for shear strength after water storage, modulus of rupture and modulus of elasticity, water absorption, and thickness swelling. Two other classic wood adhesives, namely epoxy and polyvinyl acetate (PVAc) type D4 were used as control. The highest efficiency of both mechanical and physical properties was recorded for the samples glued with caseins and an increased amount of lime. There was also an affinity between casein adhesive distribution and physical and mechanical plywood performance. Moreover, the developed casein-based glues were also used to bond the plywood for ski cores and tested in real-life winter conditions. [ABSTRACT FROM AUTHOR]