Search

Bromination of activated carbon GSGD was performed and active bromine-containing precursors were obtained, in which bromine is capable of being replaced by sulfur-containing functional groups. Bromination with liquid bromine and a solution of bromine in potassium bromide at room temperature leads to the introduction of 0.44–0.45 mmol g–1 of bromine into the surface layer of activated carbon. The treatment of brominated samples with sulfur-containing reagents with subsequent oxidation allows obtaining carbon samples that are catalytically active in the dehydration reaction of isopropyl alcohol in a gas phase. The temperature of complete conversion of isopropyl alcohol to propylene is a measure of catalytic activity. The concentration of sulfogroups in the prepared samples is up to 0.3 mol g–1. Thermogravimetry and thermoprogrammed desorption with mass spectrometric registration of products were used to study the thermal stability of modified activated carbon samples. The influence of the nature of brominating reagents, hydrolysis conditions and oxidation conditions on the structure, surface concentration of grafted S-containing groups and catalytic properties of the obtained materials was studied. Pre-bromination leads to an increase in the catalytic activity of activated carbon modified with sulfur-containing groups and the temperature of complete conversion of isopropyl alcohol to propylene decreases up to 400C depending on the concentration of sulfogroups.

The production of propylene by dehydration of 2-propanol at solid-vapor interfaces, as an example of the acidcatalyzed surface reaction, was explored by using sulfonated polyacrylonitrile-derived activated carbon fibers (PAN-ACFs). To prepare these catalysts, the PAN-ACFs obtained by onestep carbonation-activation were modified with a surface coverage of high acidity. The surface of PAN-ACFs was sulfurated with sulfur vapors at high temperatures followed by oxidation, to yield the corresponding sulfonates. The chemical analysis showed that the carbon surface layer contains from 1.28 to 6.10 mmol$\mathrm{g}^{-1}$ of sulfur, including the contribution of sulfonic $(\mathrm{S}\mathrm{O}{}_{3}\mathrm{H})$ groups. In addition to sulfonic groups, the obtained catalysts contain carboxyl, lactone, and phenolic groups, which are formed as a result of oxidation treatment. In order to understand the changes in surface chemistry and the results of sulfuration and oxidation, the sulfonated PAN-ACFs were characterized by a variety of techniques including TPD MS, TGA, SEM, and FTIR ATR. During a typical temperature mode screening at catalyst testing, it was found that the sulfonated PAN-ACFs prepared by treatment with sulfur vapor at low temperature, at $400\circ \mathrm{c}$ and $500\circ \mathrm{c}$, are very efficient at dehydrating 2-propanol. A weighed mass of 100 mg of each of these catalysts was operated at 165-175°C in 12 hours, and the catalysts were characterized by high conversion of 2-propanol and high selectivity to propylene, with a propylene yield of about 100%. Furthermore, the solid acid catalysts have high stability and strong acidity and can be reused with no significant loss in the activity after the third cycle in the subsequent 20 cycles. The preparation of solid acid catalysts from PAN-ACFs affords a novel strategy for producing propylene through alternative green and sustainable technologies.

Fluorination of nanoporous activated carbon and its subsequent modification with sodium sulfide, which leads to the introduction of sulfur-containing groups in the carbon matrix containing fluorine, was carried out. After oxidation with hydrogen peroxide, sulfo groups are formed in the surface layer of activated carbon, i.e., in this way, it is possible to obtain samples that have both fluorine-and sulfur-containing functional groups. As a result of this work, active and stable catalysts of the reactions catalyzed by acids were obtained. They have a fairly high catalytic activity and thermal stability. When testing the obtained samples in the temperature range up to 250°C under the catalytic 2-propanol dehydration, the yield of propylene remains unchanged for each cycle, the temperature of the dehydration reaction does not change, the activity remains stable for at the least three catalysis cycles, with no deactivation of catalysts.

Here we report on the phosphorylation of activated carbon (AC) at 500–800 °C. From thermal, titrimetric, and catalytic data, high surface acidity of the prepared solids is attributed to the total concentration of the protogenic groups. Transmission electron microscopy and nitrogen physisorption measurements showed a chemisorption-induced contraction of microporosity. The most active catalysts prepared at 700 °C contain 1.04 mmol g−1 of the phosphonic groups and supports dehydration of isopropanol with about 100% conversion and 100% selectivity to propylene at 170–180 °C.

Here we report on the preparation of effective aminated sorbents based on activated carbon (AC), which was produced from natural raw material (Apricot pits) for the removal of heavy metal ions from wastewaters. For effective functionalization, bromination and following amination were carried out. At the amination stage, the grafted bromine groups were substituted by amino groups. Amination by ethylenediamine and monoethanolamine alcohol solutions can replace 0.52 mmol of bromine groups by 0.51–0.57 mmol of amino groups per gram of sorbent. We showed that the aminated ACs could remove 90% of Cu(II) ions from aqueous solutions containing from 4×10−5 to 1×10−3 mol/L of Cu2+. The regeneration of used sorbents and the recovery of copper were also studied to evaluate the reusability of the sorbents.