Search

Objective: Bioactive glass (BAG) is known to possess antimicrobial and remineralizing properties; however, the use of BAG as a filler for resin based composite restorations to slow recurrent caries has not been studied. Accordingly, the objective of this study was to investigate the effect of adding 15wt% BAG to a resin composite on bacterial biofilms penetrating into marginal gaps of simulated tooth fillings in vitro during cyclic mechanical loading., Methods: Human molars were machined into approximately 3mm thick disks of dentin and 1.5-2mm deep composite restorations were placed. A narrow 15-20 micrometer wide dentin-composite gap was allowed to form along half of the margin by not applying dental adhesive to that region. Two different 72wt% filled composites were used, one with 15wt% BAG filler (15BAG) and the balance silanated strontium glass and one filled with aerosol silica and silanated strontium glass without BAG (0BAG-control). Samples of both groups had Streptococcus mutans biofilms grown on the surface and were tested inside a bioreactor for two weeks while subjected to periods of cyclic mechanical loading. After post-test biofilm viability was confirmed, each specimen was fixed in glutaraldehyde, gram positive stained, mounted in resin and cross-sectioned to reveal the gap profile. Depth of biofilm penetration for 0BAG and 15BAG was quantified as the fraction of gap depth. The data were compared using a Student's t-test., Results: The average depth of bacterial penetration into the marginal gap for the 15BAG samples was significantly smaller (∼61%) in comparison to 0BAG, where 100% penetration was observed for all samples with the biofilm penetrating underneath of the restoration in some cases., Significance: BAG containing resin dental composites reduce biofilm penetration into marginal gaps of simulated tooth restorations. This suggests BAG containing composites may have the potential to slow the development and propagation of secondary tooth decay at restoration margins., (Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.)

The fracture properties and micromechanisms of fracture for two commercial dental composites, one microhybrid (FiltekZ250) and one nanofill (FiltekSupreme Plus), were studied by measuring fracture resistance curves (R-curves) using pre-cracked compact-tension specimens and by conducting both unnotched and double notched four point beam bending experiments. Four point bending experiments showed about 20% higher mean flexural strength of the microhybrid composite compared to the nanofill. Rising fracture resistance was observed over approximately 1 mm of crack extension for both composites, and higher overall fracture resistance was observed for the microhybrid composite. Such fracture behavior was attributed to crack deflection and crack bridging toughening mechanisms that developed with crack extension, causing the toughness to increase. Despite the lower strength and toughness of the present nanofill composite, based on micromechanics observations, large nanoparticle clusters appear to be as effective at deflecting cracks and imparting toughening as solid particles. Thus, with further microstructural refinement, it should be possible to achieve a superior combination of aesthetic and mechanical performance using the nanocluster approach for dental composites.