Search

Introduction: Reticular hybrid meshes represent an alternative material for intraperitoneal repair of abdominal hernias. These consist of a reticular mesh coated or interwoven/knitted with inert materials. This study assesses the performance of two reticular polypropylene-containing hybrid meshes, TiMESH (coated with titanium) and DynaMesh (interwoven with polyvinylidene fluoride), in vitro, as well as their efficiency in adhesion prevention and tissue incorporation in an intraperitoneal model. Methods: The mesothelialization capacity of TiMESH and DynaMesh was evaluated in vitro and compared to that of Surgipro (reticular bare polypropylene) and Preclude (laminar expanded polytetrafluoroethylene). Mesh fragments were placed on the intact parietal peritoneum of New Zealand white rabbits (n = 24), and laparoscopy performed 7 days post-surgery. Fourteen days post-implantation, adhesions were evaluated and host tissue incorporation, macrophage response, collagen expression (immunohistochemistry/RT-PCR) and neoperitoneum formation assessed. Adhesions and omental tissue were also examined. Results: Mesh pores in reticular meshes were devoid of cells in the in vitro study. TiMESH, DynaMesh and Surgipro showed similar adhesion rates at 7/14 days and optimal tissue integration, with significant differences in comparison to Preclude. The greatest presence of macrophages was observed for TiMESH and was significant versus that for Preclude. Hybrid meshes revealed significantly higher collagen 1 mRNA expression in implants, with no differences in the levels of collagen 3. Omental samples from animals with a reticular mesh showed significantly greater collagen 1 mRNA levels. Conclusions: The reticular structure of a mesh limits the formation of a continuous mesothelial monolayer in vitro, regardless of its composition. The presence of titanium as a coating or polyvinylidene fluoride interwoven with polypropylene in a reticular structure did not prevent adhesions. The hybrid meshes showed proper integration and an increase in the mRNA Col 1 levels in the implant area compared to Surgipro or Preclude. [ABSTRACT FROM AUTHOR]

Biomaterials and their applications are perhaps among the most dynamic areas of research within the field of biomedicine. Any advance in this topic translates to an improved quality of life for recipient patients. One application of a biomaterial is the repair of an abdominal wall defect whether congenital or acquired. In the great majority of cases requiring surgery, the defect takes the form of a hernia. Over the past few years, biomaterials designed with this purpose in mind have been gradually evolving in parallel with new developments in the different surgical techniques. In consequence, the classic polymer prosthetic materials have been the starting point for structural modifications or new prototypes that have always strived to accommodate patients' needs. This evolving process has pursued both improvements in the wound repair process depending on the implant interface in the host and in the material's mechanical properties at the repair site. This last factor is important considering that this site—the abdominal wall—is a dynamic structure subjected to considerable mechanical demands. This review aims to provide a narrative overview of the different biomaterials that have been gradually introduced over the years, along with their modifications as new surgical techniques have unfolded. [ABSTRACT FROM AUTHOR]

Background: When repairing an abdominal wall defect, sometimes a prosthetic mesh needs to be placed directly on the parietal peritoneum. Although the standard mesh for this purpose is the laminar implant expanded polytetrafluoroethylene (PTFE), it is gradually being replaced by the laminar collagen-based meshes. This study was designed to assess the intraperitoneal behavior of three of these biomeshes, mainly in terms of their susceptibility to adhesion formation. Methods: Two 3-cm × 3-cm fragments of prosthetic material were placed on the parietal peritoneum in male New Zealand White rabbits in the following combinations: PTFE and CollaMend, PTFE and Permacol, or PTFE and Surgisis. The meshes were fixed at the four corners with individual 4/0 polypropylene sutures. Adhesion formation was quantified by sequential laparoscopy and image analysis performed at 3, 7, 14, and 90 days postimplant. All animals were killed at 90 days and the mesh specimens were subjected to microscopy and immunohistochemistry. Results: Intensely vascularized adhesions to all the implants were observed, although Surgisis showed the lowest percentage of adhesions at each follow-up time. Adhesions had stabilized by 7-14 days. The PTFE meshes were enveloped by a layer of macrophages and connective tissue, bounded by a monolayer of mesothelial cells. Permacol and CollaMend showed similar histological behavior, including cell ingrowth through their fenestrations with no signs of degradation detected at 90 days. In contrast, the Surgisis mesh at 90 days was practically replaced with neoformed tissue. Conclusions: No difference in susceptibility to adhesion formation was noted in the crosslinked collagen meshes compared to PTFE meshes. The noncrosslinked collagen mesh Surgisis showed the best behavior in that it induced fewer adhesions. Ninety days after implant, a more intense macrophage response was observed in CollaMend and Permacol than in PTFE or Surgisis. [ABSTRACT FROM AUTHOR]

Background Prior studies suggest impaired collagen metabolism involving the whole abdominal wall including the skin in patients with abdominal hernia. We compared expression patterns of matrix metalloproteinase-2 (MMP-2) and its modulators membrane type-1-matrix metalloproteinase (MT-1 MMP) and tissue inhibitor of metalloproteinase-2 (TIMP-2) in the skin of patients with and without primary inguinal hernia. Materials and methods Skin biopsy specimens from abdominal wall incisions were obtained during surgery from patients with direct inguinal hernia, indirect inguinal hernia or without hernia (controls). MMP-2, MT-1 MMP and TIMP-2 expression were determined using immunocytochemistry and immunoblotting in intact tissue and in cultured fibroblasts isolated from the biopsies. The degradation activity of MMP-2 was semiquantitatively determined using zymography. Results Significantly greater active MMP-2 expression was observed in skin fibroblasts obtained from patients with direct hernia compared with controls. MT1-MMP expression was directly correlated with MMP-2 expression with most intense staining produced in patients with direct or indirect inguinal hernia. TIMP-2, was maximally expressed in the control group, with significantly diminished expression levels recorded in the hernia groups. Conclusions Our findings indicate active MMP-2 upregulation in the abdominal skin of patients with direct inguinal hernia. This metalloproteinase plays a role in matrix degradation, weakening the abdominal wall. Skin disorders and previously described transversalis fascia defects in these patients could point to a systemic collagen metabolism abnormality as a risk factor for direct hernia. [ABSTRACT FROM AUTHOR]

Background. Over the years, reticular prostheses have undergone changes in their structure and composition to give rise to today's partially absorbable lightweight meshes. This study was designed to assess the biological and biomechanical behavior of these prostheses to establish whether they offer any advantages over nonabsorbable lightweight polypropylene prostheses. Materials and Methods. 7 × 5 cm defects were created in the anterior abdominal wall of New Zealand White rabbits and repaired by securing different prostheses to the edges of the defect with a running 4/0 polypropylene suture. The lightweight biomaterials compared were two nonabsorbable meshes: Parietene® and Optilene elastic® , and two partially absorbable prostheses: Vypro II® and Ultrapro®. At 14 and 90 days postimplant, tissue/prosthesis specimens were subjected to histological, immunohistochemical, shrinkage, and biomechanical analyses. Results. Adhesion formation on the peritoneum-facing surface of the meshes was significantly less extensive in the meshes with absorbable components at 90 days postimplant. The newly formed tissue around the prosthetic filaments was comprised of collagen fibers, fibroblasts, blood vessels, and macrophages. The partially absorbable meshes showed higher macrophage proportions (due to remnants of absorbable material and their structure) than the nonabsorbable meshes at 90 days, although differences were not significant. At 90 days postimplant, similar tensile strengths were recorded for all the implants. Conclusions. All the prosthetic materials induced good host tissue ingrowth, with no significant differences in tensile strength observed. Our findings suggest that partially absorbable lightweight prostheses could offer advantages over nonabsorbable lightweight meshes since less foreign material persists in the recipient, improving abdominal wall compliance. [ABSTRACT FROM AUTHOR]

Background: The prosthetic materials currently used to repair abdominal wall defects sometimes have to be placed in contact with the visceral peritoneum. This interface is often a site of complications such as intestinal obstruction or fistulas due to adhesions. The aim of this study was to follow the process of adhesion formation in several prosthetic materials by sequential laparoscopy. Material and Methods: Defects (7 × 5 cm) were created in the abdominal wall of 30 New Zealand White rabbits and repaired using Surgipro polypropylene mesh (PP), Ultrapro monocryl-prolene mesh (UP), Dual Mesh expanded polytetrafluoroethylene (ePTFE), Composix (PP-ePTFE), Parietex Composite (polyester with collagen-polyethylene glycol-glycerol coating [PO-gl]), or PL-PU99 (PP-polyurethane) patches fixed to the edges of the defect by running polypropylene suture. Adhesions to the implants were laparoscopically determined at 3, 7, and 14 days after surgery. Results: Percentage adhesion scores were significantly lower for ePTFE, PP-ePTFE, PO-gl, and PP-PU, compared to PP or UP. No differences were observed in adhesion scores recorded at 3, 7, and 14 days postimplant. Reticular prostheses were infiltrated by disorganized scar tissue with fibers concentric to the mesh filaments. In contrast, ePTFE implants were encapsulated by organized tissue, with fibers running parallel to the surface of biomaterial. All three composites achieved good recipient tissue integration and a homogeneous, organized, and well-vascularized neoperitoneum. Conclusion: At 14 days postimplant, laminar prostheses and composites showed similar results in terms of adhesion formation and integration within host tissue. Our findings suggest that both the composite prostheses and the laminar ePTFE performed very well in terms of reduced adhesion formation at the peritoneal interface. [ABSTRACT FROM AUTHOR]

Prosthetic mesh infection is a devastating complication of abdominal hernia repair which impairs natural healing in the implant area, leading to increased rates of patient morbidity, mortality, and prolonged hospitalization. This preclinical study was designed to assess the effects on abdominal wall tissue repair of coating meshes with a chlorhexidine or rifampicin-carboxymethylcellulose biopolymer gel in a Staphylococcus aureus (S. aureus) infection model. Partial abdominal wall defects were created in New Zealand white rabbits (n = 20). Four study groups were established according to whether the meshes were coated or not with each of the antibacterial gels. Three groups were inoculated with S. aureus and finally repaired with lightweight polypropylene mesh. Fourteen days after surgery, implanted meshes were recovered for analysis of the gene and protein expression of collagens, macrophage phenotypes, and mRNA expression of vascular endothelial growth factor (VEGF) and matrix metalloproteinases (MMPs). Compared to uncoated meshes, those coated with either biopolymer gel showed higher collagen 1/3 messenger RNA and collagen I protein expression, relatively increased VEGF mRNA expression, a significantly reduced macrophage response, and lower relative amounts of MMPs mRNAs. Our findings suggest that following mesh implant these coatings may help improving abdominal wall tissue repair in the presence of infection. [ABSTRACT FROM AUTHOR]