Thermally assisted hydrolysis and methylation-gas chromatography (THM-GC) in the presence of an organic alkali was applied to the direct analysis of copolymer composition for poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] accumulated in whole bacterial cells. Cupriavidus necator was grown on a liquid medium with different molar ratios of valeric acid (V) to glucose (G) in order to control the compositions of P(3HB-co-3HV) produced in the cells. Trace amounts (0.03 mg) of dried Cupriavidus necator cells were directly subjected to THM-GC in the presence of tetramethylammonium hydroxide (TMAH) at 400°C. The obtained chromatograms clearly showed nine characteristic peaks, attributed to the THM products from 3HB and 3HV units in the polymer chains, without any appreciable interference by the bacterial matrix components. Based on these peak intensities, the copolymer compositions were determined rapidly without using any cumbersome sample pretreatment. Moreover, the compositions thus obtained were in good agreement with those obtained by the conventional technique.

A simple, efficient and economical method for the recovery of P(3HB-co-3HHx) was developed using various chemicals and parameters. The initial content of P(3HB-co-3HHx) in bacterial cells was 50-60 wt%, whereas the monomer composition of 3HHx used in this experiments was 3-5 mol%. It was found that sodium hydroxide (NaOH) was the most effective chemical for the recovery of biodegradable polymer. High polyhydroxyalkanoate purity and recovery yield both in the range of 80-90 wt% were obtained when 10-30 mg/ml of cells were incubated in NaOH at the concentration of 0.1 M for 60-180 min at 30 °C and polished using 20 % (v/v) of ethanol.