Search

In Korea, the issue of particulate matter pollution is growing, and many solutions are being developed to deal with it. Photocatalytic technology has been found to be helpful in removing precursors such as nitrogen oxides that cause particulate matter. In a microcosm setup, ISO 22197-1 has been successfully used to quantify the removal of nitrogen oxides from the specimen to which the photocatalyst is applied. However, owing to a lack of suitable tools, on-site measurement of real-scale efficacy is difficult. Depending on the substrate and surrounding circumstances at the application location, the photocatalyst may function at varying levels. Additionally, the expected photocatalytic effect may differ depending on the ambient air quality and sunlight irradiation intensity. This article describes two approaches for studying outdoor concrete photocatalysis. Standard gas measurement and dual-reactor measurement are the recommended evaluation approaches. The standard gas measurement method was found useful for assessing the applied photocatalyst itself as an outcome of field assessment. The performance of photocatalysts at different sites was found to be mutually exclusive and comparable. Over 180 min, on a building roof deck, the NO removal by the standard gas method was 0.68 ppm, whereas, at two shaded locations, the removal amount was 0.51 ppm (side wall) and 0.24 ppm (underpass) for 300 min. The dual reactor measurement approach, on the other hand, was discovered to be one of the most suitable methods for assessing how much of an improvement there has been in the air quality in areas where photocatalysts have been placed.

In this study, anatase titania was utilized to prepare a durable photocatalytic paint with substantially enhanced photoactivity towards NO oxidation. Consequently, to alleviate the choking effect of photocatalytic paint and incorporate self‐cleaning properties, the parent anatase titania was modified with Al(OH)3 and a number of organosilane (tetraethyl orthosilicate, propyltrimethoxysilane, triethoxy(octadecyl)silane, and trimethylchlorosilane) coatings. A facile hydrolysis approach in ethanol was employed to coat the parent titania. To facilitate uniform dispersion in photocatalytic paint and strong bonding with the prevailing organic matrix, it is necessary to avail both hydrophobic and hydrophilic regions on the titania surface. Therefore, during the preparation of modified titania, the weight proportion of the total weight of alkyl silane and trimethylchlorosilane was adjusted to a ratio of 1:1. As the parent titania has few hydrophilic portions on the surface, tetraethyl orthosilicate was coated with an organic silane having an extended alkyl group as a hydrophobic group and tetraethyl orthosilicate as a hydrophilic group. When these two silane mixtures are hydrolyzed simultaneously and coated on the surface of parent titania, a portion containing a large amount of tetraethyl orthosilicate becomes hydrophilic, and a part containing an alkyl silane becomes hydrophobic. The surface morphology and the modified titania’s optical attributes were assessed using X‐ray powder diffraction (XRD), scanning electron microscopy (SEM), energy‐dispersive X‐ray spectroscopy (EDS), UV‐Vis diffuse reflectance spectroscopy (DRS), and electrochemical impedance spectroscopy (EIS) analysis. Based on the advanced characterizations, the NO removal mechanism of the modified titania is reported. The modified titania coated at 20 wt.% on the ceramic substrate was found to remove ~18% of NO under one h of UV irradiation. An extensive UV durability test was also carried out, whereby the coated surface with modified titania was exposed to 350 W/m2 of UV irradiance for 2 weeks. The results indicated that the coated surface appeared to preserve the self‐cleaning property even after oil spraying. Hence, facile hydrolysis of multiple organosilane in ethanol could be a viable approach to design the coating on anatase titania for the fabrication of durable photoactive paint.

Titanium oxide (TiO2) is a potential photocatalyst for removing toxic NOx from the atmosphere. Its practical application is, however, significantly limited by its low absorption into visible light and a high degree of charge recombination. The overall photocatalytic activity of TiO2 remains too low since it can utilize only about 4–5% of solar energy. Nitrogen doping into the TiO2 lattice takes advantage of utilizing a wide range of solar radiation by increasing the absorption capability towards the visible light region. In this work, N-doped TiO2, referred to as TC, was synthesized by a simple co-precipitation of tri-thiocyanuric acid (TCA) with P25 followed by heat treatment at 550 degrees C. The resulting nitrogen doping increased the visible-light absorption and enhanced the separation/transfer of photo-excited charge carriers by capturing holes by reduced titanium ions. As a result, TC samples exhibited excellent photocatalytic activities of 59% and 51% in NO oxidation under UV and visible light irradiation, in which the optimum mass ratio of TCA to P25 was found to be 10.

© 2020 by the authors. Licensee MDPI, Basel, Switzerland. The purpose of the study was to effectively treat algae bloomed water while using a Ti-based coagulant (TiCl4) and recover photoactive novel anatase TiO2 from the flocculated sludge. Conventional jar tests were conducted in order to evaluate the coagulation efficiency, and TiCl4 was found superior compared to commercially available poly aluminum chloride (PAC). At a dose of 0.3 g Ti/L, the removal rate of turbidity, chemical oxygen demand (COD), and total phosphorus (TP) were measured as 99.8%, 66.7%, and 96.9%, respectively. Besides, TiO2 nanoparticles (NPs) were recovered from the flocculated sludge and scanning electron microscope (SEM), energy dispersive X-ray spectroscope (EDX), and X-ray diffraction (XRD) analysis confirmed the presence of only anatase phase. The recovered TiO2 was found to be effective in removing gaseous CH3CHO and NOx under UV-A lamp at a light intensity of 10 W/m2. Additionally, the TiO2 mixed mortar blocks that were prepared in this study successfully removed atmospheric nitrogen oxide (NOx) under UV irradiance. This study is one of the first to prepare anatase TiO2 from flocculated algal sludge and it showed promising results. Further research on this novel TiO2 concerning internal chemical bonds and shift in the absorbance spectrum could explore several practical implications.