Search

The thermal stability of Au nanoparticles on ceria support of various morphology (nanocubes, nanooctahedra, and {111}-nanofacetted nanocubes) in oxidizing and reducing atmospheres was investigated by electron microscopy. A beneficial effect of the reconstruction of edges of ceria nanocubes into zigzagged {111}-nanofacetted structures on the inhibition of sintering of Au nanoparticles was shown. The influence of different morphology of Au particles on various ceria supports on the reducibility and catalytic activity in CO oxidation, and CO PROX of Au/ceria catalysts was also investigated and discussed. It was shown, that ceria nanocubes with flat {110} terminated edges are more suitable as a support for Au nanoparticles, used to catalyze CO oxidation, than zigzagged {111}- nanofacetted structures. Graphic Abstract

Control of metal–support interactions is one of the major challenges in heterogeneous catalysis. In this study, we explored the effect of Eu doping on the metal–support interactions in Au/Ce1–xEuxO...

This works presents comprehensive studies on fundamental excitations trapping and the resulting charge destabilization in cubanite AgxS/AgInS2 quantum-confined random alloys. The observed optical activity of defect levels, related to silver alloying, is discussed basing on the femtosecond excited time-resolved photoluminescence spectrograms as well as theoretical predictions obtained via the density functional theory within the reduced cluster model. Impact of the charge trapping on the third-order optical hyper-polarizabilities has also been investigated basing on the two-photon excitation action cross sections. It has been shown that silver induced defects in the AgxS/AgInS2 random alloys are responsible for effective electron/hole trapping and strong temporal charge uncompensation. The silver on indium AgIn, silver interstitials Agi and higher-order defect clusters e.g. (AgIn2--2Agi+) formed effectively due to defect compensation mechanism have been considered in this work as providing possible pathways of defect mediated depopulation of the excited states. The electron/hole trapping mechanism is also discussed as a major mechanism responsible for fast trionic relaxations leading to strong deviation from the first-order decay law and significant temporal red-shifts of the photoluminescence band maximum. Further, it is shown that controlling the silver alloying ratio and the resulting number of defects charge states, it is possible to cause variation of the average photoluminescence decay times by an order of magnitude. The silver alloying was also found as an efficient route for significant increase of the two-photon excitation action cross section.

Thermally induced reconstruction of ceria nanocubes into {111}-nanofacetted structures was investigated by XRD, TEM and Raman spectroscopy. The beneficial role of reducing atmosphere on the surface reconstruction processes was observed and is discussed. The activity of ceria nanoparticles with various surface morphology in catalytic oxidation of CO was investigated. The order of catalytic activity of the particles: smooth ceria nanocubes > {111}-nanofacetted ceria nanocubes > smooth octahedra correlates with the concentration of Ce3+ - oxygen vacancy pairs determined by Raman spectroscopy.

Ce1-xEuxO2 nanocubes, with maximum Eu content x = 0.4, were synthesized by a simple hydrothermal method. Application of various experimental techniques (SEM-EDS, STEM-EDS, XPS, ICP-AES) revealed a uniform distribution of Eu and Ce in the nanocubes, but some oxygen depletion near the surface was detected. A model explaining the effect of the Eu doping on the growth of ceria nanocubes by the oriented attachment mechanism is proposed. The oxygen vacancy ordering in high-doped (x [greater-than-or-equal] 0.1) ceria nanoparticles was found, and its effect on the reduction of ceria nanocubes is discussed.

This work presents results of studies on the shape and structural stability of the crystalline ceria-based Ce 1−x Yb x O 2−(x/2) mixed oxides with increasing Yb content (x = 0–0.50). The cube-like, and octahedral nanocrystals of the oxides were synthesized by the hydrothermal method using two different heating methods of the stainless steel Teflon-lined autoclaves — conventional (the heating mantle) and microwave assisted one. It was observed that the predetermined shape of the investigated samples was kept up to x = ~0.2. Above this value, the co-product of synthesis as a rice-like Yb-phosphates have been observed near to octahedron-like Ce 1−x Yb x O 2−(x/2) mixed oxides. In case of cube-like samples, for concentrations of Yb-ions over 20–30%, the shape of crystals starts to be round. Moreover, weaker incorporation of the Yb 3+ -ions into the CeO 2 structure was noticed in case octahedron-like samples than cube-like ones. Additionally, it was found that the mean particle sizes of the octahedral ceria based mixed oxides prepared by the conventional hydrothermal method were larger than the same materials prepared by the microwave assisted method. Thanks to enhanced reducibility at low temperatures and good thermal stability of Ce 1−x Yb x O 2−(x/2) , the investigated oxides are good candidates for catalysts of soot oxidation. For the octahedron-like Ce 0.9 Yb 0.1 O 1.95 the temperature of half oxidation (T 50% = 423 °C) was 154 °C lower than that for non-catalysed oxidation (T 50% = 577 °C). On the other hand, the most stable catalysts were cube-like oxides, both pure and doped ceria (CeO 2 — T Icycle 50% = 438 °C; T IIcycle 50% = 454 °C and Ce 0.9 Yb 0.1 O 1.95 — T Icycle 50% = 435 °C; T IIcycle 50% = 453 °C).