Search

Herein, we report a green synthetic strategy for the preparation of ZnO@rGO nanocomposites. Bioinspired synthesis of ZnO nanoarchitectures has been done using a series of biotemplates such as dextrose, sucrose, soluble starch, and carboxy methyl cellulose. The as-prepared morphologically tuned ZnO nanoarchitectures are homogeneously distributed over the surface of rGO sheets, resulting in the formation of ZnO@rGO nanocomposites. For the first time, zinc (Zn) dust, a waste byproduct from industry (Binani Zinc Limited, Kerala, India), is employed for the chemical reduction of GO. ZnO@rGO nanocomposite based nonenzymatic urea and glucose sensors have been developed over a glassy carbon electrode, and the electrochemical performance of the nanocomposite for the detection of urea and glucose are investigated. The biosensor electrode is sensitive to urea in the concentration range of 0.02 × 10−3 mM to 7.2 × 10−3 mM with a detection limit of 0.012 μM. When used for glucose detection, the linear range is 0.02 × 10−3 mM to 18 × 10−3 mM, with a detection limit of 0.008 μM. The developed sensor exhibits an ultra-high sensitivity of 682.8 μA mM−1 cm−2 towards urea and 481 μA mM−1 cm−2 towards glucose.

Metal to bulk metal oxide nanoparticles have been successfully processed via a sustainable, facile, and ecofriendly (green) approach, namely, aqueous mechanical-oxidation. Micron-sized zinc (Zn) dust (∼45 μm) was directly wet-milled using ceramic milling media for 72 h, resulting in the production of bulk monocrystalline ZnO nanorods (aspect ratio ∼5.2, hydrodynamic diameter of 315 nm) and voluminous H2 gas by catalyst-free water-splitting reaction. The mill-induced surface oxidation and the chemical purity of the synthesized nano ZnO were carefully studied using the XPS analysis. Other standard analytical tools were also employed to understand the crystallinity, phase purity, morphology, and surface area of the final artifact. The photocatalytic activities of these mechanically grown ZnO nanorods were ascertained from two cationic dye-degradation experiments, using the dyes methylene blue and rhodamine 6G. In a nutshell, the study throws a new insight into a cost-effective, zero-effluent, single-step, an...

This study investigated the role of poly-ethylene glycol (PEG) in the microwave synthesis of ZnO (ZPMx) nanorods. The molecular weight of PEG was found to strongly influence the aspect ratio of the synthesized material. The as-prepared ZPMx nanorods were post-grafted onto the surface of GO sheets using 3-amino propyl trimethoxy silane (APTMS) as a cross-linking agent to obtain ZPMx-Si@GO hybrid nanocomposites. Microscopic observations showed that ZPMx nanorods with different aspect ratios were evenly distributed on the surface of the GO sheets. It also showed enhanced thermal and chemical properties. The dependence of the antibacterial behavior on the aspect ratio of the ZPMx nanorods and GO was also investigated. An antibacterial assay was carried out using both the Gram-positive bacteria Staphylococcus aureus (S. aureus) and Gram-negative bacteria Escherichia coli (E. coli), and Klebsiella pneumonia (K. pneumonia). The results showed that the ZPMx-Si@GO hybrid nanocomposite had an excellent antibacterial property toward the test bacteria compared to pure ZPMx and GO. The synergistic effect of ZPMx and GO resulted in a superior antibacterial activity in ZPMx-Si@GO. Interestingly, the hybrid nanocomposite with a higher ZPMx aspect ratio (ZPM6000-Si@GO) showed excellent inhibition zones with diameters of ∼3.7, 3.1, and 2.4 cm corresponding to S. aureus, E. coli, and K. pneumonia, respectively. An optical density measurement, as well as the morphological changes in the bacteria, again confirmed the excellent bacterial growth inhibition of ZPM6000-Si@GO. The studies indicated that the ZPMx-Si@GO hybrid nanocomposite is a promising candidate for use in real waste-water disinfection.