Search

In the present study, cold-rolled low-carbon steel is annealed at three different conditions: 700 oC for 0 s, 800 oC for 0 s and 800 oC for 2 min at the heating rate of ~10 oC/s. Recrystallization behaviour on sample surface is studied using a heated stage Scanning Electron Microscopy and Electron Backscattered Diffraction. For the lower annealing temperature of 700 oC with no dwell, almost no recrystallization is observed and microstructure resembles the as-received deformed material with the exception of occasional sub-micron sized nuclei. For the annealing conditions of 800 oC 0 s and 800 oC 2 min, onset and evolution of recrystallization is observed in-situ as a function of the initial as-cold rolled texture. Slower recovery rate of alpha fibre than gamma fibre is observed and confirmed by lower drop in average geometrically necessary dislocation (GND) density for un-recrystallized alpha fibres (1.1E+14 m-2 for 700 oC 0 s , 1.4E+14 m-2 for 800 oC 0 s and 4.5E+14 m-2 for 800 oC 2 min) than for un-recrystallized gamma fibre grains (3.0E+14 m-2 for 700 oC 0 s , 6.2E+14 m-2 for 800 oC 0 s and 9.8E+14 m-2 for 800 oC 2 min) during annealing. Strong gamma texture in recrystallized matrix is found for annealing conditions of 800 oC 0 s and 800 oC 2 min. From TEM characterisation it was shown that sub-grain boundaries are decorated with fine precipitates (diameter d < 15 nm) of titanium-vanadium carbides (Ti,V)C for the annealing condition of 700 oC 0 s, which suggests that these precipitates play a major overall role in retardation of the recrystallization kinetics.

The precipitation kinetics of vanadium carbides and its interaction with the austenite-to-ferrite phase transformation is studied in two micro-alloyed steels that differ in vanadium and carbon concentrations by a factor of two, but have the same vanadium-to-carbon atomic ratio of 1:1. Dilatometry is used for heat-treating the specimens and studying the phase transformation kinetics during annealing at isothermal holding temperatures of 900, 750 and 650 °C for up to 10 h. Small-Angle Neutron Scattering (SANS) and Atom Probe Tomography (APT) measurements are performed to study the vanadium carbide precipitation kinetics. Vanadium carbide precipitation is not observed after annealing for 10 h at 900 and 750 °C, which is contrary to predictions from thermodynamic equilibrium calculations. Vanadium carbide precipitation is only observed during or after the austenite-to-ferrite phase transformation at 650 °C. The precipitate volume fraction and mean radius continuously increase as holding time increases, while the precipitate number density starts to decrease after 20 min, which corresponds to the time at which the austenite-to-ferrite phase transformation is finished. This indicates that nucleation and growth are dominant during the first 20 min, while later precipitate growth with soft impingement (overlapping diffusion fields) and coarsening take place. APT shows gradual changes in the precipitate chemical composition during annealing at 650 °C, which finally reaches a 1:1 atomic ratio of vanadium-to-carbon in the core of the precipitates after 10 h.

A new generation of low-carbon microalloyed High Strength Low Alloy (HSLA) steels has been developed to utilize a combination of single-phase ferritic microstructures and optimized interphase precipitation to provide high level strength and exceptional formability. The interphase precipitation reaction is a transient process lending itself strongly to take advantage of in-situ characterization techniques. The austenite/ferrite interface kinetics during isothermal transformation at 1003 K is measured using HT-CSLM, the pre-exponential effective mobility constant was found to be mobility 0.822 (m J)/(mole s). The V interphase precipitation is characterised using TEM at isothermal transformation temperatures of 923 and 973 K as having inter-sheet spacing of 22±7 and 32±9 nm respectively. Interphase precipitation inter-sheet-spacing is simulated using a revised Quasi-Ledge model and qualitatively predicts the observed trends observed for inter-sheet spacing. The results of in-situ characterisation and modelling suggest that it is possible to optimize the strengthening potential of the precipitation processes by controlling the thermal processing of microalloyed HSLA.

In-situ characterization techniques have been applied to elucidate the influence of γ/α transformation upon the extent of interphase precipitation in a low-carbon, vanadium-HSLA steel. Electron Back-scattered diffraction analyses of the γ/α orientation relationship with continuous cooling at 2 and 10 K/s suggest that the proportion of ferrite likely to hold interphase precipitation varies little with cooling rate. However, TEM analyses show that the interphase precipitation refines with increasing cooling rate in this cooling range. With cooling rates in excess of 20 K/s, interphase precipitation is increasingly suppressed due to the increasingly diffusional-displacive nature of the Widmanstatten γ/α transformation that is activated. The present study illustrates that the extent and dimensions of interphase precipitation can be controlled through controlled cooling.

Despite much research into steels strengthened through interphase precitation, there remains much that is not clear, such as the role of a range of elements, particularly Mo, in the interphase precipitation process. Four steels were manufactured with identical composition, but with variations in Ti, V, Mo and N content to investigate the effect of composition on interphase precipitation. Alloys were rapidly cooled from the single austenite phase field and isothermally transformed at 630 °C and 650 °C for 90min. The addition of Mo was found to significantly reduce the austenite to ferrite transformation kinetics, particularly for the V steel. Interphase precipitation was observed in all alloys at both transformation temperatures. For the Ti bearing steel, the two types of precipitate were observed throughout the sample, namely TiC (finer) and Ti2C (coarser), while for the V bearing steels, VC (finer) and V4C3 (coarser) were observed. Where Mo was present in the alloy, it was found dissolved in all carbide types. The (Ti,Mo)C and (V,Mo)C formed by classical planer interphase precipitation (PIP) while the (Ti,Mo)2C and (V,Mo)4C3, that had a much wider row spacing, formed through curved interphase precipitation (CIP). Each adopted one variant of the Baker-Nutting orientation relationship. The Ti-microalloyed steels exhibited the smallest precipitates of all the steels, which were approximately the same size irrespective of whether Mo was present in the alloy and irrespective of the transformation temperature. However, the addition of Mo to the V bearing steels resulted in a significant increase in precipitate volume fraction and a reduction in precipitate size. The mechanisms of interphase precipitation leading to the coincident production of two different precipitate types is considered and the role of Mo on the interphase precipitation process is discussed. The resultant effect on strength is considered.

Nanosteels are used in automotive applications to accomplish resource-efficiency while providing high-tech properties. Quantitative data and further understanding on the precipitation kinetics in Nanosteels can contribute to fulfil this goal. Small-Angle Neutron Scattering measurements are performed on a Fe-C-Mn-V steel, previously heat-treated in a dilatometer at 650°C for several holding times from seconds to 10 hours. The evolution of the precipitate volume fraction, size distribution and number density is calculated by fitting the experimental Small-Angle Neutron Scattering curves. The effect of phase transformation on precipitation kinetics is also discussed. Complementary Transmission Electron Microscopy, Scanning Electron Microscopy and Inductively Coupled Plasma Optical Emission Spectroscopy measurements are performed to support the Small-Angle Neutron Scattering data analysis.