Search

In this paper, a simple thermal decomposition synthesis route for a carbon–nitrogen–sulfur (C–N–S) co-doped titanium dioxide (TiO2) mischcrystal with an isobandgap property for visible light applications using urea as the C, and N source and titanium(IV) sulfate [Ti(SO4)2] as S source is reported. The C–N–S co-doped TiO2 mischcrystal exhibited a unique isobandgap characteristic and prominent red-shift in the ultraviolet-visible absorption spectrum and a much narrower band gap (2.42 eV and 1.39 eV) because of defects and impurity levels which were confirmed using powder X-ray diffraction, diffuse reflectance spectroscopy (DRS), photoluminescence, Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The excellent photocatalytic performance of the C–N–S co-doped TiO2 mischcrystal samples was demonstrated using degradation of methylene blue and phenol under visible light. The apparent degradation rate of black TiO2 is 4–7 times higher than that of C–N–S co-doped TiO2 (anatase or rutile) under visible light irradiation. The valence band XPS and DRS results were carefully examined to understand the band gap reduction of C–N–S co-doped TiO2. This study confirms that the band gap structure of C–N–S co-doped TiO2 is determined by the mixed crystalline structure and the formation of impurity levels and defective levels. A new idea is presented that will be useful for the design of band gap structure for photocatalysts with higher photocatalytic activities under visible light irradiation.

A phosphate based composite ceramics system, (1 − x)SrZn2(PO4)2–xTiO2 (0 ≤ x ≤ 0.5), was prepared by the solid-state reaction method, and the relations between the phase composition, crystal structure and microwave dielectric properties were investigated. The results show that only two phases of SrZn2(PO4)2 and TiO2 can be obtained in the whole range of x value, and high relative density can be archived for all compositions as suitable sintering temperatures were applied. In the variation process of phase composition ratio, lower increase of dielectric constant value (

Li-doped TiO2/SO42− nanoparticles was successfully synthesized via a simple calcinination process in a vacuum environment using Ti(SO4)2 and LiBr as precursors, and were characterized by TEM, XRD, IR, DLS, XPS and UV-vis (DRS). Li doping can reduce the diameters of TiO2 nanoparticles and affect the surface chemical forms and structures. The as-prepared photocatalysts with different LiBr contents exhibited a notably enhanced degradation efficiency for methylene blue, and exhibited the highest photocatalytic activity under UV light when the molar doping ratio of Li was 0.0125. Moreover, the most photocatalytically efficient sample also showed much higher activity for eliminating methylene blue under visible light (380 < λ < 700 nm) by applying a negative bias than P25 and the control samples without applying a negative bias. The introduced negative bias electrostatic fields could not only render TiO2 responsive to visible light, but was also able to increase the lifetime of the photo-excited charges in the doped semiconductor. This provides a facile, fast and universal method to rapidly degrade organic materials based on the Franz–Keldysh effect and the synergetic effects of the electrostatic force.