The objective of this study was to evaluate the ability of one versatile peroxidase and the biocatalytically generated complex Mn(III)-malonate to polymerize coniferyl alcohol (CA) to obtain dehydrogenation polymers (DHPs) and to characterize how closely the structures of the formed DHPs resemble native lignin. Hydrogen peroxide was used as oxidant and Mn2+ as mediator. Based on the yields of the polymerized product, it was concluded that the enzymatic reaction should be performed in aqueous solution without organic solvents at 4.5 ≤ pH ≤ 6.0 and with 0.75 ≤ H2 O2 :CA ratio ≤ 1. The results obtained from the Mn3+ -malonate-mediated polymerization showed that the yield was almost 100%. Reaction conditions had, however, effect on the structures of the formed DHPs, as detected by size exclusion chromatography and pyrolysis-GC/MS. It can be concluded that from the structural point of view, the optimal pH for DHP formation using the presently studied system was 3 or 4.5. Low H2 O2 /CA ratio was beneficial to avoid oxidative side reactions. However, the high frequency of β-β linkages in all cases points to dimer formation between monomeric CA rather than endwise polymerization. © 2017 American Institute of Chemical Engineers Biotechnol. Prog., 34:81-90, 2018.

A concept for direct surface modification on self-standing films of cellulose nanofibrils (CNF) is demonstrated using an aminosilane group in cellulose compatible solvent (dimethyl acetamide, DMA). The chemically modified structure efficiently prevents the oxygen molecules from interacting with the nanocellulose film in the presence of water molecules. Oxygen permeability values lower than 1 mL mm m-2 day-1 atm-1 were achieved at extremely high levels of relative humidity (RH95%). The aminosilane reaction is compared to conventional hydrophobization reaction using hexamethyldisilazane. The differences with respect to interactions between cellulosic nanofibrils, water and oxygen molecules taking place with aminated and silylated CNF films correlated with the degree of surface substitution, surface hydrophilicity and permeability of the formed layer. The self-condensation reactions taking place on the film surface during aminosilane-mediated bonding were decisive for low oxygen permeability. Experimental evidence on the importance of interfacial processes that hinder the water-cellulose interactions while keeping film's low affinity towards oxygen is demonstrated.