Search

Extended π-conjugation with backbone-planarity-driven π-π stacking dominates charge transport in semiconducting polymers (SCPs). The roles of SCP film morphology and macromolecular conformation concerning the substrate in influencing charge transport and its impact on device performance have been a subject of extensive debate. Face-on SCPs promote out-of-plane charge transport primarily through π-π stacking, with conjugated polymeric chains assisting transport in connecting crystalline domains, whereas edge-on SCPs promote in-plane charge transport primarily through conjugation and π-π stacking. In this work, we fabricated three different types of devices, namely, organic field effect transistors, organic Schottky diodes, and organic bistable memristors, as representatives of planar and vertical devices. We demonstrate that a planar device, i.e., an organic field effect transistor, performs well in an edge-on conformation exhibiting a field-effect mobility of 0.12 cm2V−1s−1 and on/off ratio >104, whereas vertical devices, i.e., organic Schottky diodes and organic memristors, perform well in a face-on conformation, exhibiting exceptionally high on/off ratios of ~107 and 106, respectively.

A thin film of unsubstituted polythiophene (PT), an insoluble conjugated polymer, with molecular chains uniaxially oriented in plane was prepared by the friction transfer method. The structure of highly oriented thin films of PT was investigated using grazing-incidence X-ray diffraction (GIXD), ultraviolet–visible (UV–vis) spectroscopy, and infrared (IR) spectroscopy. The polarized UV–vis and IR spectra and GIXD measurements showed the PT molecular chains were well aligned in parallel to the friction direction. The GIXD studies clarified that the polymer backbones were aligned with very narrow distribution, such that the half-width was about 4 degrees. The degree of orientation of the PT friction-transferred film was higher compared with those of regioregular poly(3-alkylthiophene)s. Moreover, the GIXD results show a preferred orientation where the a-axis is perpendicular to the substrate plane.

A novel film preparation method utilizing polymer suspension, entitled adsorbing deposition in suspensions (ADS), has been proposed. The poly(3-hexylthiophene) (P3HT) toluene solution forms P3HT nanofibrils dispersed suspension by aging. P3HT nanofibrils are highly crystallized with sharp vibronic absorption spectra. By the ADS method, only P3HT nanofibrils in suspension can be deposited on the substrate surface without any disordered fraction from the dissolved P3HT in suspension. Formed ADS film contains only the nanostructured conjugated polymer. Fabricated polymer thin-film transistor (TFT) utilizing ADS P3HT film shows good TFT performances with low off current, narrow subthreshold swing and large on/off current ratio.

Multilayered oriented polyfluorene (PF) films were obtained by applying thermal treatment procedure to a multilayered PF film constructed with fluorene derivatives layer formed on top of a highly oriented friction-transferred crystalline poly(9,9-dioctylfluorene) (PF8) film. The orientations in the multilayered PF films were investigated by polarized photoluminescence (PL) spectroscopy and grazing incident X-ray diffraction (GIXD) analysis. The results of the multilayered PF film constructed with spin-coated PF8 on friction-transferred PF8 indicate that the rearrangement of the upper PF8 layer is induced from the orientation of lower PF8 layer by thermal treatment at the nematic phase temperature. Polarized green emission from the multilayered oriented PF film was demonstrated using the blend of PF8 and poly(9,9-dioctylfluorene-co-benzothiadiazol) (F8BT) as green light emitter for upper layer. By this method, the polarized emission color can be tuned using polymer blends for upper layer similar to the liquid-crystalline polymer arrangement without using different materials as an underlying layer such as the rubbed polyimide. [ABSTRACT FROM AUTHOR]

Poly(2,5-dioctyloxy-1,4-phenylenevinylene) (DOPPV) was found to form a highly oriented film by a friction-transfer technique. Structural investigation of friction-transferred DOPPV was studied by means of polarized ultraviolet−visible (UV−vis) absorption spectroscopy, polarized photoluminescence (PL) spectroscopy, and synchrotron-sourced grazing incident X-ray diffraction (GIXD) analysis. The polarized UV−vis absorption and PL spectra indicate clear axial alignment. DOPPV backbones in friction-transferred film are highly aligned along the drawing direction of the friction-transfer. Further information of the molecular arrangement in friction-transferred DOPPV film was investigated by both the out-of-plane and the in-plane GIXD analyses with synchrotron source. The DOPPV molecules in friction-transferred films were perfectly arranged three-dimensionally:  the backbones aligned along the drawing direction of friction-transfer, the alkyl side chains lay in the film plane, and the planar backbones were arranged parallel to the film surface. Additionally, two neighboring DOPPV molecules along the direction of inter-backbones separation by alkyl side chains were found to be shifted with respect to one another by the mean distance of half of a monomeric repeat. [ABSTRACT FROM AUTHOR]

Fabrication of large-area thin films and their swift characterization is highly desired for the commercial aspects of the organic electronic devices. Although a number of techniques have been proposed for the large-area thin film fabrication, the microstructural variation is still an issue. In this work, the facile characterization of distribution in thickness and macromolecular ordering in the drop-casted and spin-coated poly(3-hexylthiophene) thin films have been performed through newly developed 2D positional mapping technique. Through this technique, a comparative analysis of the absorption spectra in terms of peak absorbance and excitonic bandwidth (W) was performed for the whole sample, the lower value of W observed for the drop-casted thin film depicts its molecular ordering. Moreover, the difference in W (≈ 10 meV) was noticed between two points (≈1 mm apart) on the drop-casted film, which corresponds to the difference in microstructural ordering and it is complicated to characterize through the conventional spectroscopic techniques. [ABSTRACT FROM AUTHOR]

We demonstrated the polymer field-effect transistors (FETs) utilizing regioregular poly(3-alkylthiophene)s (P3AT) films prepared by a drawing method. The P3AT film exhibited large optical dichroic ratio, which originated in the polymer backbones aligned to the drawing direction. In-plane anisotropy and enhancement of FET characteristics have been observed that are caused by molecular alignment. In the case of poly(3-dodecylthiophene), the hole mobility along the drawing direction was enhanced by a factor of 25 compared with that of spin-coated film. © 2004 American Institute of Physics. [ABSTRACT FROM AUTHOR]