Search

Abstract The aim of this study was to assess roughness profile and surface roughness after simulated toothbrushing cycles, as well as the degree of conversion (DC) of bulk-fill resin composites at different depths. Forty nine composite discs were made from three low-viscosity bulk-fill resins (Filtek Bulk-Fill Flowable/3M Oral Care - FBF, Beautifil-Bulk Flowable/Shofu Inc. - BBF and Surefill SDR Flow/Dentsply Caulk - SDR), three high-viscosity bulk-fill resin composites (Filtek Bulk-Fill Restorative/3M Oral Care - FBR, Beautifil-Bulk Restorative/Shofu Inc. - BBR and Tetric EvoCeram Bulk Fill/Ivoclar Vivadent - TEB) and one conventional composite (Filtek Supreme Ultra/3M Oral Care - FSU) (n=7), using addition silicon molds (2 mm thick x 10 mm diameter). The roughness profile (Rv) and surface roughness (Sa) were analyzed after 30,000 brushing cycles using confocal laser scanning microscopy. Five samples (4 mm thick x 2 mm diameter) were produced per resin composite and light-cured for 20 seconds using a LED-curing unit. After 24 hours at 37oC, DC of samples was evaluated at four depths, using a confocal Raman microscope. The data were analyzed by ANOVA and Tukey post hoc multiple-comparison tests (α = 0.05). The Rv values of FSU were lower than those obtained for BBR and BBF. The toothbrushing significantly decreased the Sa for all composites. The DC was significantly reduced at 4 mm depth. Toothbrushing changed composite surface of all materials, especially for BBR and BBF. Composites were not able to maintain the DC values shown at the top compared with those at the bottom (4 mm depth).

Abstract This study aimed to evaluate the influence of the Er,Cr:YSGG irradiation and 980-nm diode lasers on the surface roughness (SR) and volume loss (VL) of dentin subjected to cariogenic challenge. Subsequently, 130 specimens of bovine dentin were divided into the following 13 groups: NT: no treatment; FG: fluoride gel; FV: fluoride varnish; Di: 980-nm diode; Di + FG; Di + FV; FG + D; FV + Di; Er: Er,Cr:YSGG; Er + FG; Er + FV; FG + Er and FV + Er. Er,Cr:YSGG laser parameters were as follows: 0.25 W; 5.0 Hz; 4.46 J/cm2 without water and 55% air. Furthermore, the 980-nm diode laser parameters were 2.0 W; 2.0 Hz; 21.41 J/cm2. The samples from each group were subjected to pH cycling. A confocal laser scanning microscope was used to evaluate SR and VL. Difference between the volume of the reference and treated areas + DES/RE was used to determine SR and VL. The mean values of the different groups were subjected to analysis of variance and Tukey’s post-hoc test. The VL values were analyzed using the Kruskal–Wallis and Dunn post-hoc test (p < 0.05). The SR of the reference area did not show a statistically significant 1807-3107-bor-38-e025treatment and cariogenic challenge (p > 0.05). Moreover, VL in the FV + Di and FV + Er groups showed a statistically significant difference compared with areas submitted to different types of treatment and cariogenic challenge (p > 0.05). Er,Cr:YSGG and 980-nm diode lasers associated with fluoride varnishes decreased dentin VL in bovine teeth submitted to cariogenic challenge.

Introduction: The purpose of this study was to evaluate the effects of different concentrations of chitosan solution used as a final rinse after root canal treatment on the shear bond strength of composite resin to enamel and coronary dentin. Materials and Methods: Sixty-four enamel/dentin fragments were taken from the cervical-third of bovine teeth. The specimens were randomly divided into four groups according to the irrigation protocol (0.2% chitosan, 0.5% chitosan, 1% chitosan, and 17% ethylenediaminetetraacetic acid [EDTA]-control) and in two subgroups according to the substrate (enamel or dentin). Each specimen was fixed in a metallic clamping device and composite resin (Single Bond/z350) was inserted in two increments and polymerized for 20s. The microshear bond strength was performed, and the adhesive interface was analyzed by three-dimensional laser confocal scanning microscopy. The data were analyzed using a two-way ANOVA and Tukey's test (α = 5%). Results: For the irrigation protocol, bond strength was significantly higher for all chitosan solutions compared to the 17% EDTA-control solution. All chitosan solutions, 0.2%, 0.5% and 1.0%, were statistically similar to each other (P > 0.05). For the substrate, enamel showed greater bond strength and was significantly different from dentin (P < 0.05). For interaction factor, 1% chitosan solution presented bond strength values statistically superior to the 17% EDTA control solution (P < 0.05) in dentin. The adhesive fracture was the most prevalent for all groups. Conclusion: The irrigation protocol on the root canal treatment does not affect the enamel bond strength and 1% chitosan solution improved dentin bond strength. Bond strength was higher for enamel than for coronary dentin.

ABSTRACT An ideal aesthetic standard consists of facial and smile harmony. Discolored teeth generally cause an imbalance in facial aesthetics, leading to low self-esteem and disturbance in social relationships. Causes of teeth discoloration are classified as intrinsic or extrinsic. Bleaching is considered a safe and effective treatment for discolored nonvital teeth and can be associated with restorative treatment to properly correct the dental color and maximize the aesthetic results. This paper aims to present two case reports of single discolored nonvital anterior teeth and the protocol used to reestablish the dental harmony of these patients by bleaching and direct composite resin restoration. To exert minimally invasive dentistry is very important to preserve tooth structure and reduce the risk of fracture. Internal bleaching, although may not be sufficient to reestablish the aesthetic in some cases, it is important to minimize dental preparation to perform an indirect or direct restoration. Dentists must take into account the patients expectations, dominate the restorative technique and know the dental materials to properly be able to restore function and aesthetics and consequently improve life quality and social relationships.

Abstract This study evaluated how Er,Cr:YSGG laser, associated or not with 5% fluoride varnish, influences the surface roughness and volume loss of bovine root dentin submitted to erosive and/or abrasive wear. One hundred and twenty dentin specimens were divided into the groups: without preventive treatment (WPT), 5% fluoride varnish (FV); Er,Cr:YSGG laser irradiation (L), and varnish combined with laser (FV + L). The specimens (n = 10) were subdivided into: 1 = erosion (E); 2 = abrasion (A); and 3 = erosion followed by abrasion (E + A). The erosive solution used was a soft-drink (pH = 2.42 at 4ºC) applied in 5-min cycles twice a day for 10d. Abrasive wear involved brushing for 60s with an electric brush (1,600-oscillations/s) at a load of 2.0N. Surface roughness and volume loss were evaluated using a laser scanning confocal microscope. Roughness data were submitted to one-way ANOVA and Tukey post-hoc test. For volume loss, the Kruskal-Wallis and Dunn’s post-hoc tests were used (α = 5%). The lowest values of roughness were found in the control areas of all subgroups (p > 0.05). In the experimental area, the [(WPT) + (E+A)] subgroup had a significantly higher roughness (5.712 ± 0.163 μm 2 ) than the other subgroups (p < 0.05). The L and (FV + L) groups had statistically similar roughness, regardless of the type of wear. The (FV + L) group had the lowest volume loss, regardless of the type of wear performed: [(FV + L) + (E)] = 7.5%, [(FV + L) + (A) = 7.3%, and [(FV + L) + (E + A)] = 8.1%. The subgroup [(WPT) + (E + A)] had the highest volume loss (52.3%). The proposed treatments were effective in controlling dentin roughness. Laser irradiation can be an effective method to increase root dentin resistance after challenges and limit problems related to non-carious lesions.

Aim: The objective of this study was to evaluate the effects of solutions on the color stability of nanohybrid composite resins. Methods: The experimental sample consisted of 90 composite specimens (Beautifil II; Z350XT; Premisa), divided into three subgroups (n=10) according to the solutions (matte tea; lemon flavor isotonic drink; artificial saliva). The specimens were immersed in the solutions (5 mL/specimen) while stirring for 5 minutes, four times a day, with 1-hour intervals, repeated for 15 days. The color of the specimens was analyzed before (baseline) and after the 15th day of cycling using the CIELAB system. Data were analyzed using the two-way analysis of variance (ANOVA) and Tukey’s test (α=5%). Results: Different behaviors were observed among resins. Beautifil II presented the highest color change (∆E=4.18) and less color stability, statistically different from the others (p

Abstract: The effects of tooth brushing could affect the long-term esthetic outcome of composite restorations. This study evaluated the effect of two different emission spectrum light-curing units on the surface roughness, roughness profile, topography and microhardness of bulk-fill composites after in vitro toothbrushing. Valo (multiple-peak) and Demi Ultra (single-peak) curing lights were each used for 10s to polymerize three bulk-fill resin composites: Filtek Bulk Fill Posterior Restorative (FBF), Tetric EvoCeram Bulk Fill (TET) and Surefil SDR Flow (SDR). After 30,000 reciprocal strokes in a toothbrushing machine, the roughness profile, surface roughness, surface morphology, and microhardness were examined. Representative SEM images were also obtained. When light-cured with the Demi Ultra, SDR showed the most loss in volume compared to the other composites and higher volume loss compared to when was light-cured with Valo. The highest surface roughness and roughness profile values were found in SDR after toothbrushing, for both light-curing units tested. FBF always had the greatest microhardness values. Light-curing TET with Valo resulted in higher microhardness compared to when using the Demi Ultra. Confocal and SEM images show that toothbrushing resulted in smoother surfaces for FBF and TET. All composites exhibited surface volume loss after toothbrushing. The loss in volume of SDR depended on the light-curing unit used. Toothbrushing can alter the surface roughness and superficial aspect of some bulk-fill composites. The choice of light-curing unit did not affect the roughness profile, but, depending on the composite, it affected the microhardness.

The use of erbium lasers to prevent caries in enamel has shown positive results. However, it is not known if Er,Cr:YSGG laser can also be used to increase acid resistance of root dentine, which is another dental tissue susceptible to the action of cariogenic bacteria. Objective: To analyze the effects of the Er,Cr:YSGG laser (λ=2.78 μm, 20 Hz) irradiation associated with 2% neutral sodium fluoride (NaF) to prevent root dentin demineralization. Material and Methods: One hundred human root dentin samples were divided into 10 groups (G) and treated as follows: G1: no treatment; G2: NaF; G3: laser (4.64 J/cm2) with water cooling (WC=5.4 mL/min); G4: laser (4.64 J/cm2) without WC; G5: laser (8.92 J/cm2) with WC; G6: laser (8.92 J/cm2) without WC; G7: laser (4.64 J/cm2) with WC and NaF; G8: laser (4.64 J/cm2) without WC and NaF; G9: laser (8.92 J/cm2) with WC and NaF; G10: laser (8.92 J/cm2) without WC and NaF. The NaF gel was applied alone or after 4 min of irradiation. After 14 days of acid challenge, the samples were sectioned and the Knoop microhardness (KHN) test was done at different depths (30, 60, 90 and 120 μm) from the outer dentin surface. Data were analyzed by one-way ANOVA and Fisher’s test (α=5%). Results: The results showed that G8 and G10 presented higher KHN than the G1 for the depths of 30 and 60 μm, indicating an increase of the acid resistance of the dentin in up to 35% (p