This paper investigates the biaxial stretchability of polylactic acid (PLA)/poly (butylene adipate co-terephthalate) (PBAT)/thermoplastic cereal flour (TCF) ternary blends with a PLA/PBAT ratio close to 60/40 and a constant TCF content. A twin-screw extrusion process was used to gelatinize the starch and devolatilize the water in order to obtain a water-free TCF, which was then blended into a compatibilized or non-compatibilized PLA/PBAT matrix, introduced in the molten state. These blends were subsequently cast into sheets and biaxially drawn using a biaxial laboratory stretcher. The prepared ternary blends were found to present a typical ductile behavior. Scanning electron micrography highlighted dispersion and adhesion properties in the PLA/PBAT/TCF blends, where two different phases were observed. Moreover, the addition of the thermoplastic cereal flour did not significantly affect the biaxial stretchability of the PLA/PBAT blends but was found to lower the maximum stress before breaking. The modification of the interfacial tension between PLA and PBAT with the compatibilizer Joncryl before mixing with TCF had no effect on the durability of the PLA/PBAT/TCF sheet. Still, it slightly increased the maximum of nominal stress before failure. [ABSTRACT FROM AUTHOR]

This study was dedicated to the blown film extrusion of poly(lactic acid), which mainly presents poor shear and elongation viscosities, and its blends. In order to enhance its melt strength, two main routes were selected (i) a structural modification through chain extension and branching mechanisms by adding a reactive multifunctional epoxide (named Joncryl) and (ii) blending with poly(butylene adipate-co-terephtalate), named PBAT in presence (or not) of Joncryl. The effects of the reactive agent on the shear and elongation rheology, morphological, and interfacial properties of the blends were systematically investigated. A decrease of the interfacial tension has been also demonstrated according to the deformed drop retraction method (DDRM). Hence, the role of Joncryl as a compatibilizer was highlighted. Consequently, finer morphology of the dispersed phase was obtained. Furthermore, the impact of the two modification routes on the blown film extrusion ability of PLA has been studied. Based on the improved shear and elongational rheological properties, a great enlargement of the blowing processing window of PLA modified with Joncryl was demonstrated. Indeed, with the addition of Joncryl into PLA-PBAT blends, a reduction of the instability defects has been detected. Finally, the induced crystalline structure and the thermo-mechanical properties of blown films were shown to be improved. [ABSTRACT FROM AUTHOR]