The tribological behavior of traditional oil-in-water (O/W) lubricants (1.0 wt.%) and nano-TiO2 additive lubricants (1.0–9.0 wt.%) during micro rolling of titanium foils were analyzed. In this study, the surface morphologies of titanium foils under various lubrication conditions were assessed, and the corresponding lubrication mechanisms were revealed. The tribological behavior of nano-TiO2 additive lubricants during micro rolling of titanium foils was also explored through a series of characterization methods. The utilization of nano-TiO2 additive lubricants in micro rolling reduces the surface roughness of titanium foils. Moreover, it effectively inhibits the generation of indentations and cracks during rolling processes, enhancing the surface quality of rolled specimens. Additionally, owing to the synergism of rolling, tribo-film, mending and polishing effects of the nanoparticles, both the rolling force and surface roughness were minimized by using lubricants containing 3.0 wt.% TiO2 nanoparticles. Overall, an optimal concentration (3.0 wt.%) of TiO2 nanoparticles in water-based nanolubricants was obtained with enhanced tribological properties and lubrication performance during micro rolling of titanium foils. [ABSTRACT FROM AUTHOR]

A ball-on-disk tribometer was employed to evaluate the lubrication performance and mechanisms of innovative TiO 2 nano-additive water-based lubricants. Two experimental methods were applied to determine the optimal mass fraction of TiO 2 . In the method I, lubricants were added onto the worn disk tracks at a predetermined time interval. In the method II, the disks were immersed in the lubricants continuously during the whole process of tribological tests. The results both indicate that the water-based lubricants can significantly reduce the coefficient of friction (COF). The 0.8 wt% TiO 2 lubricant demonstrates excellent tribological properties including the lowest COF and the strongest wear resistance under all lubrication conditions. The lubrication mechanisms are attributed to the rolling and mending effects of the TiO 2 nanoparticles. [ABSTRACT FROM AUTHOR]