In the present study, Mg-6Zn-1Zr (ZK60) alloy with a homogeneous fine-grained structure (~5 µm) was produced by hot extrusion. The influence of temperature on tensile properties anisotropy and the associated change in deformation mechanisms in the range of 25–275 °C of the fine-grained ZK60 alloy were investigated. Under room temperature, the fine-grained ZK60 alloy exhibited a high tensile strength of ~269–327 MPa and high ductility of ~15–39% when tested at three different directions, indicating a high anisotropy. With increasing testing temperature to 150 °C and further to 275 °C, the alloy showed a gradual decrease in anisotropy. Especially, the fine-grained ZK60 alloy exhibited superplasticity of ~376–434% when tested at 275 °C, which should be due to the increasing role of grain boundary sliding (GBS), as the strong basal texture associated with room temperature deformation became almost random at elevated temperatures. Moreover, the abrupt decrease in tensile anisotropy and associated change in texture with increasing temperature correlates closely to the transformation of deformation mode from a dislocation-dominated behavior to a GBS-mediated one. [ABSTRACT FROM AUTHOR]

Inspired by nacre, we designed biomimetic metal–ceramic composites in which hard and ductile phases were alternately arranged. We first prepared lamellar-structured TiC scaffolds with 25, 30 and 35 vol% solid loadings using a unidirectional freeze casting technique and then measured wetting and infiltration dynamics for a commercial Al cast alloy, ZL107, with the main composition of Al–7Si–5Cu on the porous TiC scaffold using a modified sessile drop method at 850 °C. The wetting was affected by liquid spreading at horizontal surface and infiltration in depth, while the latter played a dominant role in the decrease in contact angle. On the basis of the wetting results, the lamellar ZL107/TiC composites were successfully fabricated by pressure infiltration of the molten ZL107 alloy into porous TiC scaffolds and their mechanical properties were evaluated. The compressive strength and elastic modulus increased while bending strength decreased with increasing TiC content, giving maximum values of 1166 ± 20 MPa, 205 ± 2 GPa and 363 ± 5 MPa, respectively. Formation of (Al m ,Si 1 − m ) 3 Ti, Al 3 Ti and Al 4 C 3 phases in the composites was presumed to deteriorate the toughness of the composites, leading to brittle fracture under loading. [ABSTRACT FROM AUTHOR]