Search

Background. This study aimed to compare the cyclic fatigue resistance of ProTaper Next, Hyflex CM, 2Shape, and TF-Adaptive nickel-titanium endodontic file systems with various alloy properties and production methods and investigate the fractured cross-sectional surface of files due to cyclic fatigue by scanning electron microscopy (SEM). Methods. A total of 120 instruments were used (n=30). For standardization, #25/.06 apical diameter and taper angle were selected for each file system. The experiment of files was subjected to a static cyclic fatigue model. The time for files’ failure was recorded with a digital chronometer and multiplied by the rotation speed to calculate the number of cycles. Kolmogorov-Smirnov, one-way ANOVA, and post hoc Bonferroni analysis were used for statistical analysis. Statistical significance was set at P

Background. This study aimed to evaluate the effects of repeated sterilization cycles on the surface alterations of various nickel-titanium instruments, including ProTaper Next (PTN), TF Adaptive (TFA), HyFlex CM (HCM), and 2Shape (2S). Methods. Twenty-four new NiTi files of four different alloys were selected. The instruments in each group were divided into two equal groups, as follows: control and sterilization. The first group was chosen as the control without applying any sterilization procedure, while in group 2, five cycles of sterilization procedures were applied. The surface topographies were evaluated using scanning electron microscope (SEM) and atomic force microscope (AFM). The root mean square (RMS) and maximum height (MH) values and three-dimensional images were recorded. The data were analyzed with the Shapiro-Wilk test, one-way ANOVA, and post hoc Tukey tests. The statistical significance level was set at P≤0.05. Results. Before the experiment, HCM demonstrated the highest RMS value, and 2S showed the lowest. After the procedures, the RMS and MH values deteriorated on the surface of PTX, TFA, and 2S (P0.05). Conclusion. The initial irregularity on the surface did not affect the rate of alteration. The HCM files demonstrated superior surface properties after several cycles of sterilization. The PTN, TFA, and 2S presented similar surface responses after five cycles of autoclave sterilization.

Background. This study aimed to compare the cyclic fatigue resistance of ProTaper Next, Hyflex CM, 2Shape, and TF-Adaptive nickel-titanium endodontic file systems with various alloy properties and production methods and investigate the fractured cross-sectional surface of files due to cyclic fatigue by scanning electron microscopy (SEM). Methods. A total of 120 instruments were used (n=30). For standardization, #25/.06 apical diameter and taper angle were selected for each file system. The experiment of files was subjected to a static cyclic fatigue model. The time for files' failure was recorded with a digital chronometer and multiplied by the rotation speed to calculate the number of cycles. Kolmogorov-Smirnov, one-way ANOVA, and post hoc Bonferroni analysis were used for statistical analysis. Statistical significance was set at P<0.05. Results. The number of cycles for the failure of files was compared between the groups, and significant differences were found (P<0.05). The number of cycles for instrument failure was recorded from the highest to the lowest as follows: Hyflex CM, TF-Adaptive, ProTaper Next, and 2Shape. Conclusion. The files were fractured at different average numbers of cycles in an artificial canal in all the groups. The Hyflex CM demonstrated better cyclic fatigue resistance than TF Adaptive, ProTaper Next, and 2Shape file systems. Factors such as production patterns, alloy properties, and the phase in which the files were produced might affect the lifespan of file systems. [ABSTRACT FROM AUTHOR]

Background. This study aimed to evaluate the effects of repeated sterilization cycles on the surface alterations of various nickel-titanium instruments, including ProTaper Next (PTN), TF Adaptive (TFA), HyFlex CM (HCM), and 2Shape (2S). Methods. Twenty-four new NiTi files of four different alloys were selected. The instruments in each group were divided into two equal groups, as follows: control and sterilization. The first group was chosen as the control without applying any sterilization procedure, while in group 2, five cycles of sterilization procedures were applied. The surface topographies were evaluated using scanning electron microscope (SEM) and atomic force microscope (AFM). The root mean square (RMS) and maximum height (MH) values and three-dimensional images were recorded. The data were analyzed with the Shapiro-Wilk test, one-way ANOVA, and post hoc Tukey tests. The statistical significance level was set at P = 0.05. Results. Before the experiment, HCM demonstrated the highest RMS value, and 2S showed the lowest. After the procedures, the RMS and MH values deteriorated on the surface of PTX, TFA, and 2S (P < 0.001). The HCM was not affected by sterilization processes (P > 0.05). Conclusion. The initial irregularity on the surface did not affect the rate of alteration. The HCM files demonstrated superior surface properties after several cycles of sterilization. The PTN, TFA, and 2S presented similar surface responses after five cycles of autoclave sterilization. [ABSTRACT FROM AUTHOR]