Duplex stainless-steel grade 2205 (2205 DSS) is the most widely used of the current duplex materials. The duplex steel alloy is characterized by high strength and high corrosion resistance through enhancing nitrogen and molybdenum contents. The activated tungsten inert gas (ATIG) welding technique uses the same equipment as tungsten inert gas (TIG), but prior to the welding operation, a thin layer of flux is deposited. Activation fluxes are known to influence the shape and energy characteristics of the arc. They promote the change in shapes and dimensions of the welds, namely, increasing the depth and narrowing the weld width. This work is dedicated to investigate the influence of the thermophysical properties of individual metal oxide fluxes on 2205 DSS welding morphology. It helps also to identify the recommended flux properties in order to perform full penetrated ATIG welds. Thirteen kinds of oxides (SiO2, TiO2, Fe2O3, Cr2O3, ZnO, Mn2O3, V2O5, MoO3, Co3O4, SrO, ZrO2, CaO, and MgO) have been tested and three current intensity levels (120, 150 and 180 A) have been considered. The results showed that the main input factors affecting the weld depth (D) were the welding current intensity with a contribution of up to 53.36%, followed by the oxides enthalpy energy with 15.05% and then by the difference between the oxides and the base metal of 2205 DSS (BM 2205 DSS) melting points with a contribution of 9.71% of the data variance. The conditions on individual oxides' thermophysical properties to achieve full penetrated weld beads have been also revealed. [ABSTRACT FROM AUTHOR]

Activating metal inert gas (AMIG) welding was designed to address difficulties with MIG welding, such as the limitation on workpiece thickness that may be welded in a single pass. This investigation was carried out on 304L stainless steel using ER 308L as a filler metal. Five oxides (SiO2, TiO2, Fe2O3, Mn2O3, and Cr2O3) have been investigated without edge preparation. The welded joints were evaluated for weld morphology, microstructure, mechanical properties, and corrosion, and the findings were compared. The depth of the AMIG weld was determined to be greater than that of the MIG weld. The microstructure is composed of austenitic and retained delta ferrite with 3.3% for MIG and up to 8% for AMIG weld carried out with Cr2O3 oxide flux, the tensile strength is up to 604 MPa when using Cr2O3 oxide against MIG weld (532 MPa), and the resistance to sudden load in AMIG welds (189 J/cm2) is higher than that of MIG weld (149 J/cm2). The corrosion resistance of the weld made with Fe2O3 oxide flux is greater than that of the other AMIG and MIG welds, as well as the parent metal. The AMIG welding technique variant enhances productivity and decreases the cost and energy consumption of the welding material compared to the traditional MIG process. This allows for joining the same thickness without affecting mechanical properties and corrosion resistance, meeting the industry's requirements. [ABSTRACT FROM AUTHOR]