Iron-based superconductors have great potential for high-power applications due to their prominent high-field properties. One of the central issues in enhancing the critical current density of iron-based superconducting wires is to reveal the roles and limitations of grain boundaries in supercurrent transport. Here, we finely tuned the electronic properties of grain boundaries by doping Ba1-xKxFe2As2 superconductors in a wide range (0.25

Superconducting joints are one of the key technologies to make Ba1-xKxFe2As2 (Ba-122) superconducting wires or tapes for high-field applications. Herein, superconducting joints were fabricated by a simple cold-pressing method, and the joint resistance of the iron-based superconducting joint was estimated for the first time. The superconducting properties, microstructures, and elements distribution in the joint regions were investigated. At 4.2 K and 10 T, a transport critical current Ic of 105 A for the joint was obtained, and the critical current ratio (CCR= Ic-joint/Ic-tape) of the joint was 94.6%. On the other hand, the joint show very low joint resistance of 2.7x10^-13 ohm in self-field at 4.2 K. Among iron-based superconductors (IBS), this work is the first to successfully realize a superconducting joint with such high CCR and low joint resistance. This work shows great potential to apply Ba-122 in a range of practical applications, where superconducting joints are essential., Comment: 20 pages, 8 figures

Superconducting materials hold great potential to bring radical changes for electric power and high-field magnet technology , enabling high-efficiency electric power generation, high-capacity lossless electric power transmission, small light-weighted electrical equipment, high-speed maglev transportation, ultra-strong magnetic field generation for high-resolution magnetic resonance imaging (MRI) systems, nuclear magnetic resonance (NMR) systems, the future advanced high energy particle accelerators, nuclear fusion reactors and so on. The performance, economy and operating parameters (temperatures and magnetic fields) of these applications strongly depend on the electromagnetic and mechanical properties, as well as manufacturing and material cost of superconductors. This perspective examines the basic properties relevant to practical applications and key issues of wire fabrication for practical superconducting materials, and describes their challenges and current state in practical applications. Finally, future perspectives for their opportunities and development in the applications of superconducting power and magnetic technologies are given., Comment: 40 pages, 8 figures

Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work., Comment: 30 pages, 7 figures, accepted to SCIENCE CHINA Materials

We report the temperature, magnetic field and time dependences of magnetization in advanced Ba122 superconducting tapes. The sample exhibits a peculiar vortex creep behavior. Below 10 K, the normalized magnetization relaxation rate S=dln(-M)/dln(t) shows a temperature insensitive plateau with a value comparable to that of the low temperature superconductors, which can be explained within the framework of the collective creep theory. It then enters into a second collective creep regime when the temperature increases. Interestingly, the relaxation rate below 20 K tends to saturate with the increasing field. However, it changes to a power law dependence on field at a higher temperature. A vortex phase diagram composed of the collective and the plastic creep regions is concluded. Benefit from the strong grain boundary pinning, the advanced Ba122 superconducting tape has promising potential to be applied not only in liquid helium but also in liquid hydrogen or at the temperature accessible with cryocoolers., Comment: 5 pages, 4 figures

The iron-based superconductor (IBS) single pancake coil (SPC) with 30 mm inner diameter was firstly fabricated and tested under 24 T background field. This SPC was successfully made using the 7-filamentary Ba1-xKxFe2As2 (Ba122) tape by wind-and-react method. This IBS coil show the highest Ic value at magnetic field reported so far. For example, the transport critical current of this Ba122 SPC achieved 35 A at 4.2 K and 10 T, which is about half of that of short sample. This indicates that the non-insulation winding process together with the stainless-steel tape is suitable to the iron-based superconductor. Even more encouraging is the fact that the Ic of this SPC is still as high as 26 A under 24 T background field, which is still about 40% of that at zero external magnetic field. These results clearly demonstrate that the iron-based superconductors are very promising for high-field magnet applications., Comment: 16 pages, 3 figures

Ag-sheathed CaKFe4As4 superconducting tapes have been fabricated via the ex-situ powder-in-tube method. Thermal and X-ray diffraction analyses suggest that the CaKFe4As4 phase is unstable at high temperatures. It decomposes into the CaAgAs phase which reacts strongly with the silver sheath. We therefore sintered the tape at 500C and obtain a transport critical current density Jc(4.2 K, 0 T)~ 2.7x10^4 A/cm2. The pinning potential derived from magnetoresistance measurements is one order of magnitude lower than that of the (Ba/Sr)1-xKxFe2As2 tapes. Combining with the scanning electron microscopy and magneto-optical imaging results, we suggest that bad connectivity between superconducting grains caused by the low sintering temperature is the main factor responsible for the low Jc. However, this system is still a promising candidate for superconducting wires and tapes if we further optimize the post-annealing process to achieve better grain connectivity., Comment: 17 pages, 6 figures

Superconducting joints are essential for iron-based superconductor's applications in future. In this study, a process for fabricating superconducting joints between Sr1-xKxFe2As2 (Sr-122) tapes is developed for the first time. The Ag sheath was peeled off from one side of each sample. The exposed superconducting parts of the two tapes were joined and wrapped again with Ag foil. The diffusion bonding of the iron-based superconducting joint was achieved by hot-pressing process in Argon atmosphere. The superconducting properties, microstructures and the elements distribution of the joint regions had been investigated. The pressure and pressing times were optimized in order to enhance the transport current of the joints. At 4.2 K and 10 T, a transport critical current Ic of 57 A for the joint was obtained, which is approximately 63.3% of the current capacity of the tapes themselves. Furthermore, the joint resistances dV/dI were estimated from the V-I curve of the joints and the calculated joint resistances values are below 10^-9 Ohm. These results demonstrate that the hot pressing was useful for fabricating the superconducting joint samples., Comment: 26 pages, 9 figures, main results were published in SuST

Superconducting nanowire single-photon detectors (SNSPDs) have an absolute advantage over other types of single photon detectors except the low operating temperature. Therefore, many efforts have been devoted to find high-temperature superconducting materials that are suitable for preparing SNSPDs. Copper-based and MgB2 ultra-thin superconducting nanowires have been already reported. However, the transport properties of iron-based ultra-thin superconducting nanowires have not been studied. In this work, a 10 nm thick 200 nm wide 30 {\mu}m long high quality superconducting nanowire was fabricated from ultrathin BaFe1.84Co0.16As2 films by a lift-off process. The precursor BaFe1.84Co0.16As2 film with a thickness of 10 nm and root-mean-square roughness of 1 nm was grown on CaF2 substrates by pulsed laser deposition. The nanowire shows a high superconducting critical temperature Tzero c=20 K with a narrow transition width of Delta T=2.5 K and exhibits a high critical current density Jc of 1.8E7 A/cm2 at 10 K. These results of ultrathin BaFe1.84Co0.16As2 nanowire will attract interest in electronic applications, including SNSPDs, Comment: 18 pages, 6figures

Iron with a large magnetic moment was widely believed to be harmful to the emergence of superconductivity because of the competition between the static ordering of electron spins and the dynamic formation of electron pairs (Cooper pairs). Thus, the discovery of a high critical temperature (Tc) iron-based superconductor (IBSC) in 2008 was accepted with surprise in the condensed matter community and rekindled extensive study globally. IBSCs have since grown to become a new class of high-Tc superconductors next to the high-Tc cuprates discovered in 1986. The rapid research progress in the science and technology of IBSCs over the past decade has resulted in the accumulation of a vast amount of knowledge on IBSC materials, mechanisms, properties, and applications with the publication of more than several tens of thousands of papers. This article reviews recent progress in the technical applications (bulk magnets, thin films, and wires) of IBSCs in addition to their fundamental material characteristics. Highlights of their applications include high-field bulk magnets workable at 15-25 K, thin films with high critical current density (Jc) > 1 MA/cm2 at ~10 T and 4 K, and an average Jc of 1.3*104 A/cm2 at 10 T and 4 K achieved for a 100-m-class-length wire. These achievements are based on the intrinsically advantageous properties of IBSCs such as the higher crystallographic symmetry of the superconducting phase, higher critical magnetic field, and larger critical grain boundary angle to maintain high Jc. These properties also make IBSCs promising for applications using high magnetic fields., Comment: Published online in Materials Today. Open Access

We comparatively studied the critical current density, magnetization and specific heat of the rolled and the hot-pressed Sr1-xKxFe2As2 tapes. The Schottky anomaly that is obvious in the specific heat of the rolled tape disappears in the hot-pressed tape. Moreover, the hot-pressed tape has a higher fraction of superconductivity and a narrower distribution of superconducting transition temperature than the rolled tape. Combined with the magnetization data, we conclude that sintering under high pressure provides a better environment for complete chemical reaction and more homogenous dopant distribution, which is beneficial to the global current of a superconductor., Comment: 13 pages, 4 figures

The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link effect between misaligned grains inside wire and tape conductors. Here we demonstrate a high transport critical current density (Jc) reaching 1.5x10^5 A/cm^2 (Ic = 437 A) at 4.2 K and 10 T in Ba0.6K0.4Fe2As2 (Ba-122) tapes prepared by a combination of conventional powder-in-tube method and optimized hot-press technique. The transport Jc measured at 4.2 K under high magnetic fields of 27 T is still on the level of 5.5x10^4 A/cm^2, which is much higher than those of low-temperature superconductors. This is the first report of hot-pressed Ba-122 superconducting tapes and these Jc values are by far the highest ever reported for iron-based superconducting wires and tapes. These high-performance tapes exhibit high degree of c-axis texture of Ba-122 grains and low anisotropy of transport Jc, showing great potential for construction of high-field superconducting magnets., Comment: 23 pages, 6 figures

Iron-pnictides are hotly studied since 2008 in the superconducting materials research area, due to their special properties and unclear mechanism. Big achievement has been made in the pnictide research during the past years. For practical uses, pnictide superconductor should be fabricated in a long wire form which can be used for different devices. In this work, 100 m class 7-core Sr0.6K0.4Fe2As2 (Sr122) tapes have been made using the powder-in-tube technique, which is reported for the first time. Clearly, an average Jc of 1.3x10^4 A/cm^2 at 10 T was reached over the 115 meter length, showing a high property and good uniformity of 100 meter level Sr122 tapes. Using the 10 m long Sr122 tapes, two double-pancake coils were fabricated by a wind and reaction technique. No transport current could be measured for the coil made from the mono-filamentary tape. However, transport Ic was obtained in the coil made from the 7-filamentary tape. The factors which affect the superconducting property of the coil were discussed in this work., Comment: 5 pages, 8 figures

We have studied vortex pinning and dynamics in a Sr0.6K0.4Fe2As2 superconducting tape with critical current density Jc~0.1 MA/cm2 at 4.2 K and 10 T. It is found that grain boundary pinning is dominant in the vortex pinning mechanism. Furthermore, we observe large density of dislocations which can also serve as effective pinning centers. We find that the temperature dependence of critical current density is in agreement with the model of vortices pinned via spatial fluctuation of charge carrier mean free path. Magnetic relaxation measurement indicates that the magnetization depends on time in a logarithmic way. The relaxation rate in the low and intermediate temperature region is small, and it exhibits a weak temperature and field dependence. A crossover from elastic creep to plastic creep regime is observed. Finally, we conclude a vortex phase diagram for the high performance Sr0.6K0.4Fe2As2 superconducting tape., Comment: 19 pages, 4 figures

Strong pinning depends on the pinning force strength and number density of effective defects. Using hydrostatic pressure method, we demonstrate that hydrostatic pressure up to 1.2 GPa can significantly enhance flux pinning or Jc by a factor of up to 5 especially in both low and high fields in optimally doped Ba0.6K0.4Fe2As2 crystals. Our analysis on the flux pining mechanism indicate that both pinning centre number density (Np) and pinning force (Fp) are greatly increased by the pressure and contribute to strong pinning., Comment: Nil

Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires and tapes with silver as matrix and iron as outer reinforcing sheath were produced by the ex situ powder-in-tube method. The mass densities of Sr-122 phase in 7- and 19-filament conductors were investigated by microhardness characterization, which revealed a positive correlation between hardness and transport critical current density (Jc) in round wires and flat tapes with various thicknesses. For Sr-122/Ag/Fe 114-filament conductors, in which an average cross-sectional filament size smaller than 50 microns was achieved by drawing into round wires of 2.0 mm in diameter, the transport Jc can be significantly enhanced by flat rolling, as for the 7- and 19-filament conductors. The highest transport Jc of the 7-,19- and 114-filament Sr-122/Ag/Fe tapes reached 1.4x10^4, 8.4x10^3 and 6.3x10^3 A cm-2 (4.2 K, 10 T), respectively, showing a Jc degradation with the increase of filament number. This Jc degradation can be ascribed to the sausage effect for filaments in longitudinal direction and the grain refinement in these very fine filaments., Comment: 27 pages, 8 figures

Conventional powder-in-tube (PIT) method has been the most effective technique for fabricating iron-based superconducting wires and tapes. Tremendous advances have been made during the last few years, especially for 122 family pnictide tapes. Here we review some of the most recent and significant developments in making high-performance iron-based tapes by the ex-situ PIT process, paying particular attention to several fabrication techniques to realize high-field Jc performance in terms of increase of core density and improvement of texture. At 4.2 K, the practical level transport Jc up to 0.12 MA/cm2 in 10 T and 0.1 MA/cm2 in 14 T have been achieved in the K-doped 122/Ag tapes. As for multifilamentary 122 iron-based wires and tapes, the highest Jc values reached so far are 61 kA/cm2 and 35 kA /cm2 at 4.2 K and 10 T, respectively for 7- and 19-core Sr-122 tapes. Recently, high Jc Cu-cladded and stainless steel/Ag double-sheathed 122 tapes have also been produced in order to improve either mechanical properties or thermal stability. More importantly, the scalable rolling process has been used for the first time to demonstrate high Jc values in 122 conductor tapes of 11 m in length., Comment: 32 pages, 18 figures. Review Article

Copper sheath is the first choice for manufacturing high-Tc superconducting wires and tapes because of its high electrical and thermal conductivities, low cost and good mechanical properties. However, Cu can easily react with superconducting cores, such as BSCCO, MgB2 and pnictides, during high-temperature sintering process and therefore drastically decrease the transport Jc. Here, we report the fabrication of Cu-sheathed Sr1-xKxFe2As2 tapes with superior Jc performance using a simple hot pressing method that is capable of eliminating the lengthy high-temperature sintering required by conventional process. We obtained high-quality Sr1-xKxFe2As2 tapes with processing at 800oC for 30 minutes and measured high Tc and sharp transition. This rapid fabrication method can effectively thwart the diffusion of Cu into polycrystalline Sr-122 core. As a consequence, we achieved high transport Jc of 3.1x10^4 A/cm^2 in 10 T and 2.7x10^4 A/cm^2 in 14 T at 4.2 K. The in-field Jc performance is by far the highest reported for Cu-sheathed high-Tc conductors. Our results demonstrate the potential of Cu sheath for practical application of pnictide wires and tapes., Comment: 21 pages, 7 figures

We report on fully epitaxial FeSe0.5Te0.5 (FST) thin films with high-quality grown on CaF2 (00l) substrate at a low temperature of 300{\deg}C by pulsed laser deposition. The transport Jc of thin films is up to 1.36 MA/cm2 in self-field and 0.97 MA/cm2 in 9 T at 4.2 K, indicating very weak field dependence. A nearly isotropy of Jc ({\gamma}= Jc(H//ab)/Jc(H//c) as low as 1.09 at 9 T is achieved in the FST thin films. Moreover, no clear amorphous interfacial layer presents between the film and the substrate probably ascribing to low temperature and low laser repetition rate grown, while the thickness of reaction layer is approximate 5 nm in many other works. The evidences of transmission electron microscopy show some lattices with lateral size of < 5 nm x 20 nm seem to be disturbed. Those location defects are thought to be responsible for nearly isotropic behavior of superconductivity., Comment: 13 pages, 4 figures. Supercond. Sci. Technol., in press

The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application level, their fabrication procedures are relatively complicated or required specialized instruments. Ag-sheathed Ba0.6K0.4Fe2As2 superconducting tapes were fabricated by the scalable rolling process. At 4.2 K and 10 T, the critical current density Jc has achieved 5.4x10^4 A/cm2. We ascribe the excellent performance to the high purity and homogeneity of the superconducting phase, high density and high c-axis texture of the superconducting core. Our method provides a simple way to scale up the production of the long-length iron-based superconducting tapes with high Jc., Comment: 15 pages, 5 figures, 1 table. Scripta Materialia, in press