Search

The phase behavior of block copolymers (BCPs) at the water-oil interface is influenced by the segmental interaction parameter ( χ${\chi }$ ) and chain architecture. We synthesized a series of star block copolymers (s-BCPs) having polystyrene (PS) as core and poly(2-vinylpyridine) (P2VP) as corona. The interaction parameters of block-block ( χ${\chi }$ PS-P2VP ) and block-solvent ( χ${\chi }$ P2VP-solvent ) were varied by adjusting the pH of the aqueous solution. Lowering pH increased the fraction of quaternized-P2VP (Q-P2VP) with enhanced hydrophilicity. By transferring the equilibrated interfacial assemblies, morphologies ranging from bicontinuous films at pH of 7 and 3.1 to nanoporous and nanotubular structure at pH of 0.65 were observed. The nanoporous films formed hexagonally packed pores in s-BCP matrix, while nanotubes comprised Q-P2VP as corona and PS as core. Control over pore size, d-spacing between pores, and nanotube diameters was achieved by varying polymer concentration, molecular weight, volume fraction and arm number of s-BCPs. Large-scale nanoporous films were obtained by freeze-drying emulsions. Remarkably, the morphologies of linear BCPs were inverted, forming hexagonal-packed rigid spherical micelles with Q-P2VP as core and PS as corona in multilayer. This work provides insights of phase behaviors of BCP at fluids interface and offer a facile approach to prepare nanoporous film with well-controlled pore structure.

Star block copolymers (s-BCPs), comprised of multiple linear diblock copolymers joined at a central point, are shown to segregate to the interface between two immiscible homopolymers that are identical to the blocks of the s-BCPs. The s-BCPs undergo a configurational transition at the interface, with different blocks of copolymers being embedded in their respective homopolymers, thereby bridging the interface and promoting adhesion. A series of 4-arm s-BCPs were synthesized with hydrogenated or deuterated polystyrene (PS/dPS) as the core block and poly(2-vinylpyridine) (P2VP) as the corona block, which was directly placed at the interface between the two homopolymers. Neutron reflectivity (NR) was used to determine the concentration profiles of the PS homopolymer, s-BCP core blocks, and P2VP total segments under equilibrium. The investigation varies the molecular weight (MW) and the total number of s-BCPs at the interface. Self-consistent-field theory (SCFT) was also employed to calculate the concentration profiles of the components at the interface, which were in excellent agreement with experimental results. The NR showed that the interfacial width between the homopolymers increased with the increasing number of s-BCPs at the interface up to a saturation limit. Beyond this limit, additional s-BCPs were released into the corona-miscible phase as unimolecular micelles. For a comparable interlayer thickness of s-BCPs at the interface, lower MW s-BCPs generated a broader interface. SCFT analysis suggested that, at the same packing density, the arms of the low MW s-BCPs align more parallel to the interface, while the arms of high MW s-BCPs adopt a more normal orientation, like their linear BCP counterparts. Furthermore, it was also observed that the core blocks, constrained by the junction points, were oriented more parallel and closer to the interface than the corona blocks. The phase behavior of the polymer blends revealed that s-BCP additives can efficiently reduce the domain size, with the low MW yielding smaller domain sizes due to the greater reduction in the interfacial energy and the high MW arresting phase separation due to their higher binding energy and a jamming of the interfacial assemblies. Asymmetric double cantilever beam (ADCB) tests demonstrated that s-BCPs promoted adhesion more efficiently than their linear BCP counterparts due to stronger binding energy per molecule, suggesting a more efficient compatibilizer for polymer upcycling. The results from these studies provide fundamental insights into the assembly of s-BCPs at homopolymer interfaces, the reduction of domain size, and promotion of adhesion, providing a strategy for the use of s-BCPs as stealth surfactants and universal compatibilizers.

Anion exchange membranes (AEMs) are a promising class of materials for applications that require selective ion transport, such as fuel cells, water purification, and electrolysis devices. Studies of structure–morphology–property relationships of ion-exchange membranes revealed that block copolymers exhibit improved ion conductivity and mechanical properties due to their microphase-separated morphologies with well-defined ionic domains. While most studies focused on symmetric diblock or triblock copolymers, here, the first example of a midblock quaternized pentablock AEM is presented. A symmetric ABCBA pentablock copolymer was functionalized to obtain a midblock brominated polymer. Solution cast films were then quaternized to obtain AEMs with resulting ion exchange capacities (IEC) ranging from 0.4 to 0.9 mmol/g. Despite the relatively low IEC, the polymers were highly conductive (up to 60 mS/cm Br− at 90 °C and 95%RH) with low water absorption (