Search

Silicon solar cells are described which operate at energy conversion efficiencies independently measured at 18.7 percent under standard terrestrial test conditions (AM1.5, 100 mW/sq cm, 28 C). These are apparently the most efficient silicon cells fabricated to date. The high-efficiency results from a combination of high open-circuit voltage due to the careful attention paid to the passivation of the top surface of the cell, high fill factor due to the high open-circuit voltage and low parasitic resistance losses, and high short-circuit current density due to the use of shallow diffusions, a low grid coverage, and an optimized double layer antireflection coating.

A project is underway at the University of New South Wales aimed at producing a 20 percent efficient silicon solar cell. A prerequisite for obtaining such a significant increase in cell efficiency is the improvement of the open circuit voltage of these cells. Two techniques are described which have produced experimental devices with open circuit voltages of 690 mV or higher. These high voltage techniques have been combined with other high efficiency design features to produce silicon cells with independently measured energy conversion efficiencies in excess of 19 percent under standard terrestrial test conditions (direct beam AM1.5 spectrum, 100 mW/sq cm, 28 C).

Silicon solar cells are described which operate at energy conversion efficiencies in excess of 18 percent under standard terrestrial test conditions (AM1.5, 100 mW/sq cm, 28 C). These are believed to be the most efficient silicon cells reported to date. The high efficiency is a result of the combination of high open-circuit voltage due to the careful attention paid to passivation of the top surface of the cell; high fill factors due to the high open-circuit voltage and low parasitic resistance losses; and high short-circuit current due to the use of shallow diffusions, a low grid coverage, and an optimized double-layer antireflection coating.

The relationship between the response at blue wavelengths and the open-circuit voltage of high performance silicon solar cells with a virtually 'transparent' emitter is analyzed. It is shown that a one-dimensional cell model cannot simultaneously model the optical collection properties and operating characteristics of such cells. The analysis highlights the importance of surface conditions and shows that previous conclusions regarding bounds on Auger coefficients imposed by correlating these parameters must be treated with caution.

The key to improved silicon solar cell performance lies in increasing cell open circuit voltage. Not only does improved voltage direclty increase cell efficiency, but it also increases the limiting value of fill factor and decreases the temperature sensitivity of the cell. Limits on attainable open circuit voltage are not well defined. A thermodynamic limit of 850 mV exists for black body silicon cells, with 700 mV long regarded as a practical limit. This paper describes experimental work which has resulted in experimental devices with open circuit voltages approaching 700 mV. Values up to 694 (AM0, 25 C) have been demonstrated. The cells are similar in structure to conventional p-n junction cells, but particular attention is paid to passivating the entire top surface of the cell, including regions under the top contact.