Abstract Hexagonal boron nitride (h-BN) nanoparticles could induce interesting properties to silicone rubber (SR) but, the weak filler-matrix interfacial interaction causes agglomeration of the nanoparticles and declines the performance of the nanocomposite. In this work, h-BN nanoparticles were surface modified using vinyltrimethoxysilane (VTMS) at different concentrations. Before silane modification, h-BN nanoparticles were hydroxylated using 5 molar sodium hydroxide. The nanoparticles were characterized to assess success of silane grafting. The pure and modified h-BN nanoparticles were applied at 1, 3 and 5 wt% to HTV silicon rubber (SR). The curing, thermal, mechanical and morphological properties and hydrophobicity of the nanocomposites were evaluated. The morphology of the SR nanocomposites was characterized using AFM and FE-SEM analysis. It was found that silane grafting on the h-BN nanoparticles improves crosslink density but declines curing rate index (CRI) of the SR nanocomposite (at 5 wt% loading content) by 0.7 (dN m) and 3.5%, respectively. It also increased water contact angle of the nanocomposites from 97.5° to 107°. The improved nanoparticle-rubber interfacial interactions caused better dispersion of h-BN nanoparticles in SR matrix (at 5 wt%) that enhanced the elongation at break, modulus at 300% and Tg of the SR nanocomposites.

In this work, boron nitride nano sheets (BNNSs) were prepared by exfoliation of h-BNs using mono ethylene glycol (MEG) as a novel exfoliating agent. For comparison, isopropyl alcohol (IPA)/water mixture was also used for exfoliation of h-BNs. It was found that using MEG caused preparing nano layers with higher yield and lower thickness compared to the IPA/water mixture. Thereafter, silicon rubber nanocomposites contained 3 and 5 wt% of pure and exfoliated BNNSs were prepared and evaluated for thermal and electrical performances. It was found that h-BNs and exfoliated-BNs drastically enhanced thermal conduction of SR. The silicon rubber contained 5 wt% of the h-BN and exfoliated-BNs illustrated around 20 times higher thermal conductivities compared to pure SR. Exfoliation of h-BNs had negligible effect on improvement of thermal properties, however, it caused 5.7 and 2.3 times enhancement in the electrical volume resistivity compared to the pristine SR and pure h-BN containing nanocomposite, respectively. Both of the BNNSs caused improvement in the heat dissipation performances of SR matrix, however, the exfoliated one with MEG showed better performances. Based on the results, it was claimed that mono ethylene glycol could improve exfoliation of h-BNs and enhance the performances of silicon rubber.