MoS 2 nanosheets with size of several-hundred nanometers were prepared by a hydrothermal intercalation/exfoliation method, then MoS 2 /Bi 2 Te 3 composite nanopowders were prepared by a microwave-assisted wet chemical method using the MoS 2 nanosheets, TeO 2 , Bi(NO 3 ) 3 ·5H 2 O, KOH and ethylene glycol as raw materials. Bulk MoS 2 /Bi 2 Te 3 nanocomposites were prepared by hot pressing the MoS 2 /Bi 2 Te 3 composite nanopowders with MoS 2 nanosheet content ranging from 0 to 17 wt% at 80 MPa and 648 K in vacuum. X-ray photoelectron spectroscopy and X-ray diffraction analyses indicate that MoS 2 and Bi 2 Te 3 did not react each other during the hot pressing. FESEM observation reveals that the MoS 2 /Bi 2 Te 3 composite samples had a more compact microstructure than the pristine Bi 2 Te 3 bulk sample. The MoS 2 phase was relatively randomly dispersed in the composite. At a given temperature, the electrical conductivity of the composites increases first then decreases as the MoS 2 content increases, whereas the Seebeck coefficient of the bulk nanocomposites does not change much. A highest power factor, ~18.3 μW cm −1 K −2 which is about 30% higher than that of pristine Bi 2 Te 3 sample, at 319 K has been achieved from a nanocomposite sample containing 6 wt% MoS 2 . [ABSTRACT FROM AUTHOR]

AgInTe2 compound has not received enough recognition in thermoelectrics, possibly due to the fact that the presence of Te vacancy (VTe) and antisite defect of In at Ag site (InAg) degrades its electrical conductivity. In this work, we prepared the Ag1-xInTe2 compounds with substoichiometric amounts of Ag and observed an ultralow lattice thermal conductivity (κL = 0.1 Wm−1K−1) for the sample at x = 0.15 and 814 K. This leads to more than 2-fold enhancement in the ZT value (ZT = 0.62) compared to the pristine AgInTe2. In addition, we have traced the origin of the untralow κL using the Callaway model. The results attained in this work suggest that the engineering of the silver vacancy (VAg) concentration is still an effective way to manipulate the thermoelectric performance of AgInTe2, realized by the increased point defects and modified crystal structure distortion as the VAg concentration increases. [ABSTRACT FROM AUTHOR]