Search

In the present study, two types of diamond films with a diameter of 123 mm were deposited by DC arc plasma jet chemical vapor deposition (CVD) operating in the gas recycling mode. These two diamond films were found to possess peculiar grain family morphologies. The fracture strengths of the samples were 182.65 and 995.58 MPa, respectively. To investigate the possible reason for the large difference in the fracture strength between the samples, the surface and fracture morphologies of the two types of diamond films as well as their grain size were characterized. The results revealed that the sample with low fracture strength suffered from a typical intergranular fracture. Weak grain boundary, impurities distributed in the boundary, and low strength of diamond grains led to a decrease in the fracture strength. However, the sample with high fracture strength mainly suffered from transgranular fracture and the columnar grain exhibited numerous voids. Owing to the impact of twinning, the voids could be occupied, thus increasing the contact area between the adjacent grains. Moreover, large grain family on the growth side contained numerous small grains and twins. These small grains, twins on growth side along with the difference of stress on surfaces inhibit fracture strength from decreasing rapidly. All these features benefitted fracture strength. Moreover, when the sample was loaded, the tips located in the voids probably resulted in increase of risk of stress concentration, which might have led to initiation of crack origin and eventual fracture. [ABSTRACT FROM AUTHOR]

Diamond has attracted increasing attention because it has high thermal conductive. Here, a freestanding diamond thermal conductive film with a diameter of about 7 in. and an average thickness of 1.54 mm was prepared by DC arc plasma jet CVD with multi-stage magnetic fields. Specifically, the thickness uniformity was ensured by adding the magnetic field during the deposition of the freestanding diamond film. The morphology, structure and thermal conductivity of the diamond film were studied. The results showed that the expansion area of the DC arc plasma approached the surface of the substrate increasing duo to add the bottom magnetic field. Structural characterization revealed that the grain of the diamond film in the arc main were coarse, affected by the shape of DC arc plasma, while in the arc center and edge were fine. The main orientation of polycrystalline structure of the diamond film was the crystalline plane of (220). The Raman peaks of diamond film in different areas moved to a higher wavelength, indicating the existence of compressive stress inside the diamond film. The coarse columnar grain and a few grain boundaries were in the arc main. Therefore, the average value of the thermal conductivity (k ⊥) of diamond film measured in the arc main was 1728.9 ± 4.9 W/(m·k). Meanwhile, the thermal conductivity of the arc center and edge area was lower than that of the arc main. [Display omitted] • A freestanding diamond thermal conductive film with a diameter of about 7 in. was prepared. • DC arc plasma jet CVD with multi-stage magnetic fields was adopted. • The average value of the thermal conductivity (k ⊥) of diamond film measured in the arc main was 1728.9 ± 4.9 W/(m·k). [ABSTRACT FROM AUTHOR]

Abstract: Highly c-axis oriented ZnO film is often deposited on diamond substrates by RF magnetron sputtering and widely used for high frequency surface acoustic wave (SAW) devices. Deposition temperature is a key factor affecting the quality of the ZnO film. Different quality polished free-standing diamond films prepared by DC Arc Plasma Jet were used as the substrates to deposit ZnO films at different temperatures. Effect of the deposition temperature and the quality of the diamond films on the properties of the ZnO films were investigated by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show that highly c-axis oriented ZnO films can be much easier deposited on the optical-grade diamond films with <111> preferred orientation than the tool-grade diamond films with <220> preferred orientation. The optimal deposition temperature is 200°C for highly c-axis oriented and lower roughness ZnO films. Acoustic phase velocity of more than 10,000m/s for the SAW devices based on the ZnO/optical-grade free-standing diamond films was obtained. [Copyright &y& Elsevier]

In this study, standard diamond bars were prepared using an ultra-thick diamond plate, and the bars had sizes consistent with the International Organization for Standardization (ISO) 14704:2016(E) three-point bending method for measuring the fracture strength. Ultra-thick diamond plate with dimensions of 125 mm (diameter) × 6.5 mm (thickness) were deposited using direct current arc plasma jet chemical vapour deposition. After cutting, grinding, and polishing, 12 diamond bars meeting the requirements of the ISO standard were prepared (36 mm × 4 mm × 3 mm) and tested for fracture strength using the cited ISO standard and elastic modulus using deflection measurements. The fracture strength of the ultra-thick diamond plate was found to be 580 ± 66 MPa. In addition, for comparison, the fracture strengths of standard ZnS, sapphire, and alumina were also analysed. Crucially, this is the first report of the fracture strength of standard-sized diamond plate. The effects of the defects and grain size on the crack formation and failure of the diamond film were analysed. The diamond's fracture strength was affected by the sample thickness, which caused the gradual accumulation of defects as this dimension increased, but not by its length and width. The elastic moduli of sapphire and alumina were compared. Overall, the measurement of the fracture strengths of ultra-thick diamond plate via the ISO standard is important for industrial applications. [ABSTRACT FROM AUTHOR]

Abstract: A destroyable Ti interlayer on graphite substrate was used for fabrication of crack-free free-standing diamond films by high-power DC Arc Plasma Jet. Ti interlayer was arc ion plated on the polycrystalline graphite substrate. The thickness, morphology and composite phase of the Ti interlayer were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Titanium carbide (TiC) was detected in both sides of the interlayer, which played an important role with respect to reasonable adhesion and diamond nucleation. Semi-translucent and crack-free diamond films were obtained and characterized by SEM and Raman spectroscopy. It is shown that the diamond films so obtained have excellent Raman signature. The overall results suggest that plating Ti interlayer on graphite substrate is an effective way to obtain potentially crack-free free-standing diamond films. [Copyright &y& Elsevier]

The direct-current arc plasma jet method is advantageous for the rapid deposition of large-area self-supporting diamond films. However, dark defects tend to be generated during the growth process, significantly affecting the performance of the diamond. In this study, we use the direct-current arc plasma jet method to prepare transparent and translucent samples. Subsequently, we compare their optical, thermal, and mechanical properties and analyze the differences in their performances via microstructure and defect analyses. The results indicate that the transparent diamond samples exhibit excellent optical and thermal properties, with a transmittance of 68.4 % at a wavelength of 10.6 μm and a thermal conductivity similar to that of type-IIa single crystal diamond (i.e. 2002 W/(m·K)). Meanwhile, the translucent diamond exhibits outstanding mechanical properties, with a fracture strength of 984 MPa. Characterization results based on electron backscatter diffraction and X-ray computed tomography suggest that a preferred orientation along the (220) planes is conducive to the densification growth of the samples, thereby enhancing their optical and thermal properties. However, the generation of numerous twins results in interlocking between grains, which improves sample's mechanical properties but introduces porosity and impurities, thus deteriorating its optical and thermal performance. [Display omitted] • Optical and thermal diamond films were deposited by DC-arc plasma jet CVD with growth rates >6 μm/h. • Strong (220) texture and numerous twins can improve optical transmittance and fracture strength, respectively. • X-ray CT was used to reveal defects distribution and content within diamond samples. [ABSTRACT FROM AUTHOR]

The growth process of carbon film on the surface of hydrocooling copper substrate in high-density direct current (DC) arc plasma was studied. Scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, nuclear magnetic resonance spectroscopy, and UV confocal Raman spectroscopy were used to analyze the structural constituents of the intermediate products generated at different growth periods. Results show that despite the remarkable heating effect of DC arc plasma to the copper substrate, one layer of cauliflower saturated carbon and double carbon bond as main component loose matter are first formed because of water-cooled copper substrate. With the increase in thickness of carbon film, the surface temperature gradually increases, the etching ability of the atomic hydrogen is enhanced and high concentration reactive units are maintained on the surface of carbon film. The cauliflower structure may effectively reduce the diamond nucleation barrier and promote the generation of nano-diamond. The diamond grains gradually grow up to the micron scale by the continuing influence of carbon-based active group and plasma. The growth pattern of carbon film on the hydrocooling copper substrate in high-density DC arc plasma may provide a new way to prepare large crack-free diamond films. [ABSTRACT FROM AUTHOR]