Search

In the present study, two types of diamond films with a diameter of 123 mm were deposited by DC arc plasma jet chemical vapor deposition (CVD) operating in the gas recycling mode. These two diamond films were found to possess peculiar grain family morphologies. The fracture strengths of the samples were 182.65 and 995.58 MPa, respectively. To investigate the possible reason for the large difference in the fracture strength between the samples, the surface and fracture morphologies of the two types of diamond films as well as their grain size were characterized. The results revealed that the sample with low fracture strength suffered from a typical intergranular fracture. Weak grain boundary, impurities distributed in the boundary, and low strength of diamond grains led to a decrease in the fracture strength. However, the sample with high fracture strength mainly suffered from transgranular fracture and the columnar grain exhibited numerous voids. Owing to the impact of twinning, the voids could be occupied, thus increasing the contact area between the adjacent grains. Moreover, large grain family on the growth side contained numerous small grains and twins. These small grains, twins on growth side along with the difference of stress on surfaces inhibit fracture strength from decreasing rapidly. All these features benefitted fracture strength. Moreover, when the sample was loaded, the tips located in the voids probably resulted in increase of risk of stress concentration, which might have led to initiation of crack origin and eventual fracture. [ABSTRACT FROM AUTHOR]

Abstract: Highly c-axis oriented ZnO film is often deposited on diamond substrates by RF magnetron sputtering and widely used for high frequency surface acoustic wave (SAW) devices. Deposition temperature is a key factor affecting the quality of the ZnO film. Different quality polished free-standing diamond films prepared by DC Arc Plasma Jet were used as the substrates to deposit ZnO films at different temperatures. Effect of the deposition temperature and the quality of the diamond films on the properties of the ZnO films were investigated by means of scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show that highly c-axis oriented ZnO films can be much easier deposited on the optical-grade diamond films with <111> preferred orientation than the tool-grade diamond films with <220> preferred orientation. The optimal deposition temperature is 200°C for highly c-axis oriented and lower roughness ZnO films. Acoustic phase velocity of more than 10,000m/s for the SAW devices based on the ZnO/optical-grade free-standing diamond films was obtained. [Copyright &y& Elsevier]

Abstract: A destroyable Ti interlayer on graphite substrate was used for fabrication of crack-free free-standing diamond films by high-power DC Arc Plasma Jet. Ti interlayer was arc ion plated on the polycrystalline graphite substrate. The thickness, morphology and composite phase of the Ti interlayer were examined by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Titanium carbide (TiC) was detected in both sides of the interlayer, which played an important role with respect to reasonable adhesion and diamond nucleation. Semi-translucent and crack-free diamond films were obtained and characterized by SEM and Raman spectroscopy. It is shown that the diamond films so obtained have excellent Raman signature. The overall results suggest that plating Ti interlayer on graphite substrate is an effective way to obtain potentially crack-free free-standing diamond films. [Copyright &y& Elsevier]