Search

Copyright of Atomic Energy Science & Technology is the property of Editorial Board of Atomic Energy Science & Technology and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

LT21 a type of aluminum alloy used for the irradiation channel of the first heavy water research reactor (HWRR) in China. Studying the mechanical property of irradiated LT21 aluminum under actual service conditions is essential for evaluating its application property. In this paper, tensile specimens of irradiated LT21 were manufactured from the decommissioned irradiation channel of an HWRR; then, tensile tests were carried out, and then the fracture surfaces were observed. The effect of neutron irradiation on tensile behavior and the failure mechanism was analyzed by comparing the result of irradiated and unirradiated LT21 specimens. The results show that, with the thermal neutron flux increasing to 2.38 × 1022 n/cm2, the YS gradually increased from the initial 158 MPa to 251 MPa, the UTS increased from 262 MPa to 321 MPa, and the elongation decreased from 28.8% to about 14.3%; the brittle fracture of the LT21 specimen appeared after irradiation, and the proportion of brittle fracture increased as the neutron fluence increased; the nanophase structures, with a size of less than 50 nm, were precipitated in the LT21 aluminum alloy after neutron irradiation. Transmutation Si is presumed to be the main cause of the radiation effect mechanism of LT21. [ABSTRACT FROM AUTHOR]

The fitness for service code of the Japan Society of Mechanical Engineers (JSME) provides a fracture evaluation methodology based on linear elastic fracture mechanics (LEFM) for boiling water reactor (BWR) internal components irradiated to a neutron fluence of 3.0 × 1024 n/m2 or more. On the other hand, it is known that austenitic stainless steel maintains its ductility and toughness even after neutron irradiation up to the fluence expected for BWR internal components. Accordingly, it is preferable to apply the ductile fracture evaluation methodology for BWR internal components. The present study examined the applicability of damage mechanics analysis based on the Gurson‒Tvergaard‒Needleman (GTN) model for irradiated stainless steel. The changes of mechanical properties of the material due to neutron irradiation were simulated by cold working. As a result, in terms of material strength properties the applicability of the GTN model was confirmed for irradiated stainless steel using the simulated material for neutron fluence up to about 1.5 × 1025 n/m2. • Damage mechanics analysis based on the Gurson‒Tvergaard‒Needleman (GTN) model for irradiated stainless steel was investigated. • Changes of mechanical properties of the material due to neutron irradiation were simulated by cold working. • Fracture tests and analyses were performed with plate specimens. • Applicability of GTN model was examined by comparing the maximum loads and fracture behaviors between the tests and analyses. • Applicability of the GTN model was confirmed for irradiated stainless steel using the simulated material for neutron fluence up to about 1.5 × 1025 n/m2. [ABSTRACT FROM AUTHOR]

LT21 a type of aluminum alloy used for the irradiation channel of the first heavy water research reactor (HWRR) in China. Studying the mechanical property of irradiated LT21 aluminum under actual service conditions is essential for evaluating its application property. In this paper, tensile specimens of irradiated LT21 were manufactured from the decommissioned irradiation channel of an HWRR; then, tensile tests were carried out, and then the fracture surfaces were observed. The effect of neutron irradiation on tensile behavior and the failure mechanism was analyzed by comparing the result of irradiated and unirradiated LT21 specimens. The results show that, with the thermal neutron flux increasing to 2.38 × 1022 n/cm2, the YS gradually increased from the initial 158 MPa to 251 MPa, the UTS increased from 262 MPa to 321 MPa, and the elongation decreased from 28.8% to about 14.3%; the brittle fracture of the LT21 specimen appeared after irradiation, and the proportion of brittle fracture increased as the neutron fluence increased; the nanophase structures, with a size of less than 50 nm, were precipitated in the LT21 aluminum alloy after neutron irradiation. Transmutation Si is presumed to be the main cause of the radiation effect mechanism of LT21.

• The changes in fracture behavior of stainless steel with in neutron dose can be predicted from the presented method. • The multiaxial fracture strain model is determined by simulating tensile and fracture toughness test. • The neutron irradiation embrittlement constant is determined by simulating tensile test. • The neutron irradiation embrittlement constant is multiplied with the multiaxial fracture strain model to simulate fracture toughness tests, enabling the prediction of degradation in fracture toughness due to neutron irradiation. This paper proposes a numerical method for predicting the reduction in the fracture toughness with neutron dose using the concept of an embrittlement constant. Tensile and fracture toughness test data for type 304 stainless steel in the literature [ 41 , 42 ] are used to validate the proposed method. Fracture toughness tests are simulated using a stress-modified fracture strain damage model implemented in an ABAQUS user-subroutine. The true stress-strain curve and one point of the fracture strain locus are obtained from the tensile test simulation. The remaining parameters of the fracture strain locus are determined by simulating a fracture toughness test. The fracture strain locus is modified to reflect the irradiation effect on the fracture toughness using the proposed irradiation embrittlement constant C I. The function of the constant with the neutron dose is calculated from the tensile tests and simulations. Subsequently, the modified damage model is used to predict the reduction in the fracture toughness. The predicted simulation results are compared with experimental data, showing good agreement. [Display omitted] [ABSTRACT FROM AUTHOR]

The microstructure and nanomechanical properties of three samples of the modified stainless steel (referred as the alloy D9) were systematically characterized after neutron irradiation in the Advanced Test Reactor. The samples were irradiated to 5.0, 8.2, and 9.2 displacements per atom at 448, 430, and 683°C, respectively. The evolutions of dislocation loops, cavities, and radiation-induced precipitates were quantitatively studied to reveal their dose and temperature dependencies. Nanohardness and nanoindentation creep tests were conducted at room temperature on the irradiated samples. Unexpected radiation hardening was observed in the highest-temperature-irradiated sample due to the formation of an unknown type of Ni- and Si-rich precipitates whose contributions to the radiation and mechanical performances of the alloy were discussed. We provide the radiation-microstructure-property correlations of alloy D9 with new insights, which can benefit the development and optimization of advanced austenitic alloys for future nuclear applications. Image, graphical abstract [ABSTRACT FROM AUTHOR]

Reactor pressure vessel (RPV) is the critical un-changeable component of the reactor during its service lifetime, which prevents the radioactive leak of the nuclear power plant core. The irradiation test (about 10 × 10 19 cm − 2 , E > 1 MeV) in research reactor of the pressure vessel material was carried out, and the charpy impact test has been carried out before and after the neutron irradiation. Analysis of the impact energy and the fracture morphology has been done to estimate the embrittlement due to neutron irradiation. It shows that the main effects of neutron irradiation to fracture are the crack initiation and stable expansion process. And there also are a small amount of intergranular fracture in the unstable crack expansion after neutron irradiated which aware us pay more attention to the increasing intergranular fracture behavior of higher neutron fluence level after 60a nuclear power plant operation. [ABSTRACT FROM AUTHOR]