Biocomposites based on polylactic acid (PLA), tall wheatgrass (TWG), and hemp (H) were made by injection molding. The article discusses the impact of the agrofiller content on the composite properties, including thermal (DSC, DMA, and TG) and mechanical characteristics (tensile modulus, tensile strength, and impact strength). Generally, the introduction of a plant filler into the polylactide matrix reduced the thermal resistance of the resulting composites. Plant fillers influenced primarily the cold crystallization process, probably due to their nucleating properties. The addition of fillers to the PLA matrix resulted in an increased storage modulus across all tested temperatures compared to pure PLA. In the case of a composite with 50% of plant fillers, it was almost 118%. The mechanical properties of the tested composites depended significantly on the amount of plant filler used. It was observed that adding 50% of plant filler to PLA led to a twofold increase in tensile modulus and a decrease in tensile strength and impact strength by an average of 23 and 70%, respectively. It was determined that composites incorporating tall wheatgrass (TWG) particles exhibited a slightly elevated tensile modulus while showcasing a marginally reduced strength and impact resistance in comparison to composites containing hemp (H) components. [ABSTRACT FROM AUTHOR]

The fractionation of diatomaceous earth (DE) using sedimentation made it possible to obtain separate unbroken diatom fractions from broken or agglomerated bodies with a range of particle sizes. The produced filler was used to prepare polylactide (PLA)/diatomaceous earth biocomposite samples containing different particle sizes, which were subjected to mechanical testing (tensile strength, flexural strength, impact strength), colloidal testing (contact angle, color change test, SEM/EDS), and thermal testing (TGA, DSC, DMA). Modification of the PLA containing the smallest particle size with diatomaceous earth (Fraction 5) resulted in a higher impact strength compared to both the pure PLA and the PLA/DE composite that contained base diatomaceous earth. Furthermore, the melt flow rate was improved by more than 80 and 60% for the composite modified with fractionated diatomaceous earth (Fraction 4) compared to pure PLA and base diatomaceous earth, respectively. The elasticity of the composite was also improved from 3.3 GPa for pure polylactide to 4.4 GPa for the system containing the smallest diatomaceous earth particles (Fraction 5). [ABSTRACT FROM AUTHOR]