Search

Even though transition metals can activate Oxone to degrade toxic contaminants, bimetallic materials possess higher catalytic activities because of synergistic effects, making them more attractive for Oxone activation. Herein, nanoscale CuCo-bearing N-doped carbon (CuCoNC) can be designed to afford a hollow structure as well as CuCo species by adopting cobaltic metal organic frameworks as a template. In contrast to Co-bearing N-doped carbon (CoNC), which lacks the Cu dopant, CuCo alloy nanoparticles (NPs) are contained by the Cu dopant within the carbonaceous matrix, giving CuCoNC more prominent electrochemical properties and larger porous structures and highly nitrogen moieties. CuCoNC, as a result, has a significantly higher capability compared to CoNC and Co3O4 NPs, for Oxone activation to degrade a toxic contaminant, Rhodamine B (RDMB). Furthermore, CuCoNC+Oxone has a smaller activation energy for RDMB elimination and maintains its superior effectiveness for removing RDMB in various water conditions. The computational chemistry insights have revealed the RDMB degradation mechanism. This study reveals that CuCoNC is a useful activator for Oxone to eliminate RDMB.

As cobalt (Co) has been the most useful element for activating Oxone to generate SO4•−, this study aims to develop a hierarchical catalyst with nanoscale functionality and macroscale convenience by decorating nanoscale Co-based oxides on macroscale supports. Specifically, a facile protocol is proposed by utilizing Cu mesh itself as a Cu source for fabricating CuCo2O4 on Cu mesh. By changing the dosages of the Co precursor and carbamide, various nanostructures of CuCo2O4 grown on a Cu mesh can be afforded, including nanoscale needles, flowers, and sheets. Even though the Cu mesh itself can be also transformed to a Cu-Oxide mesh, the growth of CuCo2O4 on the Cu mesh significantly improves its physical, chemical, and electrochemical properties, making these CuCo2O4@Cu meshes much more superior catalysts for activating Oxone to degrade the Azo toxicant, Acid Red 27. More interestingly, the flower-like CuCo2O4@Cu mesh exhibits a higher specific surface area and more superior electrochemical performance, enabling the flower-like CuCo2O4@Cu mesh to show the highest catalytic activity for Oxone activation to degrade Acid Red 27. The flower-like CuCo2O4@Cu mesh also exhibits a much lower Ea of Acid Red 27 degradation than the reported catalysts. These results demonstrate that CuCo2O4@Cu meshes are advantageous heterogeneous catalysts for Oxone activation, and especially, the flower-like CuCo2O4@Cu mesh appears as the most effective CuCo2O4@Cu mesh to eliminate the toxic Acid Red 27.

Development of visible light response semiconductor photocatalysts in degradation of organic compounds (pollutants) is one of the current research focuses due to the severe environmental pollution from various industrial and agricultural pollutants in water bodies. In this work, β-MnO2particles were successfully prepared by sol-gel method with potassium permanganate and manganese (II) sulphate as precursors. The transmission electron microscope/selected area electron diffraction analysis indicates that the particles were polycrystals with tubular structure. The photodegradation of Rhodamine B (RhB) solution using β-MnO2nanotubes under visible irradiation followed 1storder kinetic with rate constant of 0.022 ± 0.003 min−1and photodegradation efficiency of 90.3% after 120 min under visible light irradiation. The N-deethylation was the dominant process in photodegradation of RhB dye by β-MnO2nanotubes as compared to cycloreversion process. By applying similar synthesis condition, the β-MnO2nanotubes were successfully synthesised on PET fibre. The photodegradation efficiency of RhB dye under circulation condition by β-MnO2nanotubes grown on PET fibre under visible light irradiation was 1.23 h−1. The result suggests that β-MnO2nanotubes grown on PET fibre could be used as visible light-driven photocatalysts for wastewater purifier application. [ABSTRACT FROM PUBLISHER]