Neutron and x‐ray diffraction measurements have been performed on CaO–MgO–Al2O3–SiO2 (CMAS) glasses doped with NiO–FeXO at room temperature, along with x‐ray measurements on aerodynamically levitated liquids at ≥2000 K. The disordered structures have been modeled using empirical potential structure refinement to investigate the relation between the aluminosilicate network and the modifying cations. The SiO4 and AlO4 tetrahedra are found to have wider Si–O and Al–O bond distance distributions in the glass, and the first Ca–On coordination shell is highly distorted, redistributing different populations of long and short bonds between the liquid and the glass. The addition of Fe and Ni at low aluminosilicate content increases the number of free oxygens not bonded to AlO4 or SiO4. Mg–O and Fe–O are both found to be predominantly fourfold and fivefold in the liquid and glassy states. Despite these low coordination numbers, their bond angle distributions indicate that they are predominantly in nontetrahedral‐type geometries, with ferrous and ferric iron possessing similar coordination environments. The Ca–O and Mg–O average coordination numbers and enthalpies of solution are consistent with their higher reactivity within relatively acidic aluminosilicate melts. [ABSTRACT FROM AUTHOR]

Understanding and controlling liquid–liquid phase separation in aluminosilicates is crucial for optimizing glass properties. However, the metastable nature of aluminosilicates' phase separation has made it difficult to study experimentally, and uncertainty persists regarding the compositional and temperature extents of the miscibility gap. Here, we present new experimental evidence that suggests a consolute temperature between 1440 and 1590°C and endmember compositions of 7 and 62 mol.% Al2O3 for the phase‐separated glasses. Using containerless melt processing, deeply supercooled liquids over the 0–60 mol.% Al2O3 range are probed with in situ small‐ and wide‐angle X‐ray scattering, which simultaneously reveals changes in nanoscale density heterogeneity and atomic structure. Correlations between phase separation and atomic coordination environments are compared for liquids and glasses. Pair distribution function analysis shows mean O–(Si + Al) coordination increases with Al2O3 content and decreases with temperature. [ABSTRACT FROM AUTHOR]