In this study, Tl:CsI/CsCl/KCl ternary eutectic scintillators were grown using the vertical Bridgman–Stockbarger method by unidirectional solidification. The CsI and KCl phases were elongated along the growth direction, based on backscattered electron imaging (BEI) observations. The Tl:CsI scintillator phase grew as a matrix, which can be used to create optical waveguides for scintillation light. The expected Tl+ emission peak was observed at 550 nm under X-ray excitation. This emission was attributed to the self-trapped excitons perturbed by TI+ in Tl:CsI. The decay time of the Tl:CsI/CsCl/KCl eutectic was 285 ns, and its light output was estimated to be 10,800 photons/MeV.

In recent years, thermal neutron detection using scintillators has been used in a wide range of fields. Thus, the development of scintillators with a higher light yield, faster decay, and higher sensitivity for thermal neutrons is required. In this study, K2CeCl5/6LiCl and CeCl3/SrCl2/6LiCl were developed as novel eutectic scintillators for thermal neutron detection. LiCl was selected as the neutron capture phase and K2CeCl5 and CeCl3 were used as the scintillator phases. The eutectics of K2CeCl5/6LiCl and CeCl3/SrCl2/6LiCl were prepared using the Vertical Bridgman method and the phases were identified by scanning electron microscopy and powder X-ray diffraction measurements. The results of radioluminescence measurements under Ag source X-ray tube irradiation confirmed that the 5d-4f emission derived from Ce3+. The cathodoluminescence spectra and thermal neutron responses of the prepared eutectics were measured to evaluate their optical properties.

To date, 3He gas has been commonly used to detect thermal neutrons because of their high chemical stability and low sensitivity to γ-rays, owing to their low density and large neutron capture cross-section. However, the depletion of 3He gas prompts the development of a new solid scintillator for thermal neutron detection to replace 3He gas detectors. Solid scintillators containing 6Li are commonly used to detect thermal neutrons. However, they are currently used in single crystals only, and their 6Li concentration is defined by their chemical composition. In this study, 6Li-containing eutectic scintillators were developed. CeCl3 was selected as the scintillator phase because of its low density (3.9 g/cm3); high light yield (30,000 photons/MeV); and fast decay time with four components of 4.4 ns (6.6%), 23.2 ns (69.6%), 70 ns (7.5%) and >10 μs (16.3%), owing to the Ce3+ 5d-4f emission peak at approximately 360 nm. Crystals of the CeCl3, LiCl and CaCl2 ternary eutectic were fabricated by the vertical Bridgman technique. The grown eutectic crystals exhibited Ce3+ 5d-4f emission with a peak at 360 nm. The light yield was 18,000 photons/neutron, and the decay time was 10.5 ns (27.7%) and 40.1 ns (72.3%). Therefore, this work demonstrates optimization by combining a scintillator phase and Li-rich matrix phase for high Li content, fast timing, high light yield and low density.