Tritium was extracted from tritium-contaminated aluminum samples by heating it in a high-temperature furnace at 200, 300, or 400 °C for 15 h. The extracted tritium was analyzed by using a liquid scintillation counter (LSC); the sample thicknesses were 0.4 and 2 mm. The differences in tritium extraction over time were also investigated by cutting aluminum stick samples into several pieces (1, 5, 10, and 15) with the same thickness, and subsequently heating them. The results revealed that there are most of the hydrated material based on tritium on the surface of aluminum. When the temperature was increased from 200 or 300 °C–400 °C, there are no large differences in the heating duration required for the radioactivity concentration to be lower than the MDA value. Additionally, at the same thickness, because the surface of aluminum is only contaminated to tritiated water, cutting the aluminum samples into several pieces (5, 10, and 15) did not have a substantial effect on the tritium extraction fraction at any of the applied heating temperatures (200, 300, or 400 °C). The proportion of each tritium-release materials (aluminum hydrate based on tritium) were investigated via diverse analyses (LSC, XRD, and SEM-EDS).

Tritium extraction from radioactively contaminated cement mortar samples was performed using heating and liquid scintillation counting methods. Tritiated water molecules (HTO) can be present in contaminated water along with water molecules (H2O). Water is one of the primary constituents of cement mortar dough. Therefore, if tritium is present in cement mortar, the buildings and structures using this cement mortar would be contaminated by tritium. The radioactivity level of the materials in the environment exposed to tritium contamination should be determined for their disposal in accordance with the criteria of low-level radioactive waste disposal facility. For our experiments, the cement mortar samples were heated at different temperature conditions using a high-temperature combustion furnace, and the extracted tritium was collected into a 0.1 M nitric acid solution, which was then mixed with a liquid scintillator to be analyzed in a liquid scintillation counter (LSC). The tritium extraction rate from the cement mortar sample was calculated to be 90.91% and 98.54% corresponding to 9 h of heating at temperatures of 200 °C and 400 °C, respectively. The tritium extraction rate was close to 100% at 400 °C, although the bulk of cement mortar sample was contaminated by tritium.