Search

[EN] The processing and characterization of laminates based on TiAlC MAX phase, as matrix, and triaxial alumina braids, as reinforcing phase, are presented. TiAlC powders with a mean particle size below 1 µm are synthesized, while commercial 3M Nextel 610 alumina fibers are braided in a three-stage process consisting of spooling, braiding with an angle of 0° and ±60° and the separation to single-layer fabric. The laminates are processed by layer-by-layer stacking, where 3 two-dimensional alumina braids are interleaved between TiAlC layers, followed by full densification using a Field-Assisted Sintering Technology/Spark Plasma Sintering. The multifunctional response of the laminates, as well as for the monolithic TiAlC, is evaluated, in particular, the thermal and electrical conductivity, the oxidation resistance, and the mechanical response. The laminates exhibit an anisotropic thermal and electrical behavior, and an excellent oxidation resistance at 1200℃ in air for a week. A relatively lower characteristic biaxial strength and Weibull modulus (i.e., σ = 590 MPa and m = 9) for the laminate compared to the high values measured in the monolithic TiAlC (i.e., σ = 790 MPa and m = 29) indicates the need but also the potential of optimizing MAX-phase layered structures for multifunctional performance., Germany’s Federal Ministry of Education and Research (“Bundesministerium für Bildung und Forschung”), Grant/Award Number: 03SF0534; Spanish Ministry of Science and Innovation (MICINN/AEI) and FEDER (UE), Grant/Award Number: RTI2018- 095052- BI00; European Research Council (ERC), Grant/Award Number: 817615

In this work we demonstrate the feasibility of fabricating textured alumina employing a lithography-based ceramic manufacturing process. The combination of vat rotation and platform immersion contributes to the alignment of alumina templates during printing. Templated Grain Growth during sintering provides a high degree of texture (Lotgering Factor ​~ ​0.80) with relatively low porosity (approx. 7%). A comparable characteristic biaxial strength of 640 ​MPa and 570 ​MPa was measured for textured and equiaxed alumina samples, opening the path for 3D printing textured ceramics of complex architectures for structural and functional applications.

Free-standing Li1.5Al0.5Ti1.5P3O12 electrolyte sheets with a thickness of 50–150 μm were prepared by tape casting followed by sintering at 850–1000 °C in air. While a sintering temperature of 850 °C was too low to achieve appreciable densification and grain growth, a peak relative density of 95% was obtained at 920 °C. At higher sintering temperatures, the microstructure changed from a bimodal grain size distribution towards exclusively large grains (> 10 μm), accompanied by a decrease in relative density (down to 86% at 1000 °C). In contrast, ionic conductivity increased with increasing sintering temperature, from 0.1 mS/cm at 920 °C to 0.3 mS/cm at 1000 °C. Sintering behavior was improved by adding 1.5% of amorphous silica to the slurry. In this way, almost full densification (99.8%) and an ionic conductivity of 0.2 mS/cm was achieved at 920 °C. Mechanical characterization was carried out on the almost fully densified material, yielding elastic modulus and hardness values of 109 and 8.7 GPa, respectively. The fracture strength and Weibull modulus were also characterized. The results confirm that densification and reduction of grain size improve the mechanical properties.

In this work the influence of different colloidal processing routes on the mechanical behavior of several Ti(C,N)-based cermets has been studied. The materials were designed with a Ti(C,N) content ranging between 80 and 85 vol %, in a Fe-Ni alloy matrix (with and without carbon addition). Three processing techniques were investigated: (i) Slip Casting (SC), (ii) Slip Casting + Cold Isostatic Pressing (SC+CIP), and (iii) Spray-Dry + Uniaxial Pressing (SDP). Biaxial strength distributions were determined in all samples using the ball-on-three-balls (B3B) method on disc-shaped specimens. Results were interpreted in the framework of Weibull theory. The characteristic strength ranged between 1090 MPa and 1870 MPa. A fractographic analysis performed on selected specimens showed different critical flaws, depending on the processing route, related to the composition and porosity level in each case. Single Edge V-Notched Beam (SEVNB) specimens fabricated with SDP were tested under 4-point-bending, in order to identify the effect of Fe-Ni content and carbon addition on their fracture resistance. Detailed fractographic analyses revealed slightly different mechanisms of fracture associated with the Fe-Ni and carbon content. Fracture toughness values ranging between ∼12 and ∼14 MPa m were measured. Based upon these findings the SDP route is proposed to improve both the strength and toughness of Ti(C,N) cermets, which can be enhanced by the addition of carbon during the colloidal processing., The authors acknowledge thefinancial support from the Span-ish Government through the projects MAT2015-70780-C4-1-P and MAT2015-70780-C4-2-P, and the Regional Government of Madrid through the program MULTIMAT-CHALLENGE, ref. S2013/MIT-2862. M.Dios acknowledges MINECO through the grant BES-2013-065760

For the fabrication of complex, micro-electromechanical systems (MEMS) devices based on low-temperature co-fired ceramic (LTCC), higher firing temperatures and longer times than those proposed by the LTCC producer are needed. These changes to the thermal budget may influence the material properties and consequently its functional properties. The effect of the firing conditions on the LTCC DuPont 951 and thus on the phase composition, that is, the alumina/anorthite ratio and porosity, on the mechanical properties is presented. The samples fired at low temperatures (800°C) had a high porosity (7%), which significantly contributed to the low elastic modulus (100 GPa) and the low mechanical strength of the LTCC (140 MPa). The samples fired at 850°C, which had only 1% of porosity, resulted in an elastic modulus of 122 GPa and a flexural strength of 224 MPa. A further increase in the temperature contributed to a slight decrease in the elastic modulus, while no significant difference in the flexural strength could be observed. The enhancement of the flexural strength with an increasing firing temperature was mainly related to a decrease in the porosity and to a lesser extent to the different ratio of the alumina/anorthite phases. The effect of firing time on the phase composition at selected temperatures (i.e., 100 h at 700 and 800°C) is also discussed.