Search

Nanograined nuclear materials are expected to have a better performance as spallation targets and nuclear fuels than conventional materials, but many basic properties of these materials are still unknown. The present work aims to contribute to their better understanding by studying the effect of grain size on the melting and solid-solid transitions of nanograined UC 2-y . We laser-heated 4 nm-10 nm grain size samples with UC 2-y as the main phase (but containing graphite and UO 2 as impurities) under inert gas to temperatures above 3000 K, and their behavior was studied by thermal radiance spectroscopy. The UC 2-y solidification point (2713(30) K) and α-UC 2 to β-UC 2 solid-solid transition temperature (2038(10) K) were observed to remain unchanged when compared to bulk crystalline materials with micrometer grain sizes. After melting, the composite grain size persisted at the nanoscale, from around 10 nm to 20 nm, pointing to an effective role of carbon in preventing the rapid diffusion of uranium and grain growth.

This paper presents an experimental study about the preparation, by electrospinning, of uranium carbide fibers with nanometric grain size. Viscous solutions of cellulose acetate and uranyl salts (acetate, acetylacetonate, and formate) on acetic acid and 2,4-pentanedione, adjusted to three different polymer concentrations, 10, 12.5, and 15 weight %, were used for electrospinning. Good quality precursor fibers were obtained from solutions with a 15% cellulose acetate concentration, the best ones being produced from the uranyl acetate solution. As-spun precursor fibers were then decomposed by slow heating until 823 K under argon, resulting in a mixture of nano-grained UO 2 and C fibers. A last carboreduction was then carried out under vacuum at 2073 K for 2 h. The final material displayed UC 2-y as the major phase, with grain sizes in the 4 nm-10 nm range. UO 2+x was still present in moderate concentrations (~30 vol.%). This is due to uncomplete carboreduction that can be explained by the fiber morphology, limiting the effective contact between C and UO 2 grains.

Actinide research at the nanoscale is gaining fundamental interest due to environmental and industrial issues. The knowledge of the local structure and speciation of actinide nanoparticles, which possibly exhibit specific physico-chemical properties in comparison to bulk materials, would help in a better and reliable description of their behaviour and reactivity. Herein, the synthesis and relevant characterization of PuO 2 and ThO 2 nanoparticles displayed as dispersed colloids, nanopowders, or nanostructured oxide powders allow to establish a clear relationship between the size of the nanocrystals constituting these oxides and their corresponding An(iv) local structure investigated by EXAFS spectroscopy. Particularly, the first oxygen shell of the probed An(iv) evidences an analogous behaviour for both Pu and Th oxides. This observation suggests that the often observed and controversial splitting of the Pu-O shell on the Fourier transformed EXAFS signal of the PuO 2 samples is attributed to a local structural disorder driven by a nanoparticle surface effect rather than to the presence of PuO 2+ x species., Competing Interests: There are no conflicts to declare., (This journal is © The Royal Society of Chemistry.)

Fundamental knowledge on intrinsic plutonium colloids is important for the prediction of plutonium behaviour in the geosphere and in engineered systems. The first synthetic route to obtain salt-free intrinsic plutonium colloids by ultrasonic treatment of PuO 2 suspensions in pure water is reported. Kinetics showed that both chemical and mechanical effects of ultrasound contribute to the mechanism of Pu colloid formation. In the first stage, fragmentation of initial PuO 2 particles provides larger surface contact between cavitation bubbles and solids. Furthermore, hydrogen formed during sonochemical water splitting enables reduction of Pu(IV) to more soluble Pu(III), which then re-oxidizes yielding Pu(IV) colloid. A comparative study of nanostructured PuO 2 and Pu colloids produced by sonochemical and hydrolytic methods, has been conducted using HRTEM, Pu L III -edge XAS, and O K-edge NEXAFS/STXM. Characterization of Pu colloids revealed a correlation between the number of Pu-O and Pu-Pu contacts and the atomic surface-to-volume ratio of the PuO 2 nanoparticles. NEXAFS indicated that oxygen state in hydrolytic Pu colloid is influenced by hydrolysed Pu(IV) species to a greater extent than in sonochemical PuO 2 nanoparticles. In general, hydrolytic and sonochemical Pu colloids can be described as core-shell nanoparticles composed of quasi-stoichiometric PuO 2 cores and hydrolyzed Pu(IV) moieties at the surface shell.