Search

When magnetic nanoparticles (MNPs) are single-domain and magnetically independent, their magnetic properties and the conditions to optimize their efficiency in magnetic hyperthermia applications are now well-understood. However, the influence of magnetic interactions on magnetic hyperthermia properties is still unclear. Here, we report hyperthermia and high-frequency hysteresis loop measurements on a model system consisting of MNPs with the same size but a varying anisotropy, which is an interesting way to tune the relative strength of magnetic interactions. A clear correlation between the MNP anisotropy and the squareness of their hysteresis loop in colloidal solution is observed : the larger the anisotropy, the smaller the squareness. Since low anisotropy MNPs display a squareness higher than the one of magnetically independent nanoparticles, magnetic interactions enhance their heating power in this case. Hysteresis loop calculations of independent and coupled MNPs are compared to experimental results. It is shown that the observed features are a natural consequence of the formation of chains and columns of MNPs during hyperthermia experiments: in these structures, when the MNP magnetocristalline anisotropy is small enough to be dominated by magnetic interactions, the hysteresis loop shape tends to be rectangular, which enhance their efficiency. On the contrary, when MNPs do not form chains and columns, magnetic interactions reduces the hysteresis loop squareness and the efficiency of MNPs compared to independent ones. The present work should improve the understanding and interpretation of magnetic hyperthermia experiments., Comment: 21 pages, 9 figures

The influence of a transverse static magnetic field on the magnetic hyperthermia properties is studied on a system of large-losses ferromagnetic FeCo nanoparticles. The simultaneous measurement of the high-frequency hysteresis loops and of the temperature rise provides an interesting insight into the losses and heating mechanisms. A static magnetic field of only 40 mT is enough to cancel the heating properties of the nanoparticles, a result reproduced using numerical simulations of hysteresis loops. These results cast doubt on the possibility to perform someday magnetic hyperthermia inside a magnetic resonance imaging setup., Comment: 6 pages, 3 figures

We report on the magnetic and hyperthermia properties of iron nanoparticles synthesized by organometallic chemistry. They are 5.5 nm in diameter and display a saturation magnetization close to the bulk one. Magnetic properties are dominated by the contribution of aggregates of nanoparticles with respect to individual isolated nanoparticles. Alternative susceptibility measurements are been performed on a low interacting system obtained after eliminating the aggregates by centrifugation. A quantitative analysis using the Gittleman s model allow a determination of the effective anisotropy Keff = 1.3 * 10^5 J.m^{-3}, more than two times the magnetocristalline value of bulk iron. Hyperthermia measurements are performed on agglomerates of nanoparticles at a magnetic field up to 66 mT and at frequencies in the range 5-300 kHz. Maximum measured SAR is 280 W/g at 300 kHz and 66 mT. Specific absorption rate (SAR) displays a square dependence with the magnetic field below 30 mT but deviates from this power law at higher value. SAR is linear with the applied frequency for mu_0H=19 mT. The deviations from the linear response theory are discussed. A refined estimation of the optimal size of iron nanoparticles for hyperthermia applications is provided using the determined effective anisotropy value.

We report on the magnetic hyperthermia properties of chemically synthesized ferromagnetic 11 and 16 nm Fe(0) nanoparticles of cubic shape displaying the saturation magnetization of bulk iron. The specific absorption rate measured on 16 nm nanocubes is 1690+-160 W/g at 300 kHz and 66 mT. This corresponds to specific losses-per-cycle of 5.6 mJ/g, largely exceeding the ones reported in other systems. A way to quantify the degree of optimization of any system with respect to hyperthermia applications is proposed. Applied here, this method shows that our nanoparticles are not fully optimized, probably due to the strong influence of magnetic interactions on their magnetic response. Once protected from oxidation and further optimized, such nano-objects could constitute efficient magnetic cores for biomedical applications requiring very large heating power.

We report on hyperthermia measurements on a colloidal solution of 15 nm monodisperse FeCo nanoparticles (NPs). Losses as a function of the magnetic field display a sharp increase followed by a plateau, which is what is expected for losses of ferromagnetic single-domain NPs. The frequency dependence of the coercive field is deduced from hyperthermia measurement and is in quantitative agreement with a simple model of non-interacting NPs. The measured losses (1.5 mJ/g) compare to the highest of the literature, though the saturation magnetization of the NPs is well below the bulk one., Comment: 14 pages, 3 figures

We report on transport properties of millimetric super-lattices of CoFe nanoparticles surrounded by organic ligands. R(T)s follow R(T) = R_0.exp(T/T_0)^0.5 with T_0 ranging from 13 to 256 K. At low temperature I(V)s follow I=K[(V-V_T)/V_T]^ksi with ksi ranging 3.5 to 5.2. I(V) superpose on a universal curve when shifted by a voltage proportional to the temperature. Between 1.8 and 10 K a high-field magnetoresistance with large amplitude and a strong voltage-dependence is observed. Its amplitude only depends on the magnetic field/temperature ratio. Its origin is attributed to the presence of paramagnetic states present at the surface or between the nanoparticles. Below 1.8 K, this high-field magnetoresistance abruptly disappears and inverse tunnelling magnetoresistance is observed, the amplitude of which does not exceed 1%. At this low temperature, some samples display in their I(V) characteristics abrupt and hysteretic transitions between the Coulomb blockade regime and the conductive regime. The increase of the current during these transitions can be as high as a factor 30. The electrical noise increases when the sample is near the transition. The application of a magnetic field decreases the voltage at which these transitions occur so magnetic-field induced transitions are also observed. Depending on the applied voltage, the temperature and the amplitude of the magnetic field, the magnetic-field induced transitions are either reversible or irreversible. These abrupt and hysteretic transitions are also observed in resistance-temperature measurements. They could be the soliton avalanches predicted by Sverdlov et al. [Phys. Rev. B 64, 041302 (R), 2001] or could also be interpreted as a true phase transition between a Coulomb glass phase to a liquid phase of electrons.