Single crystals of Ca1– хBaхF2 (x = 0.001–0.05 and 0.85–0.99) solid solutions have been grown by the Bridgman method, and their thermal conductivity has been measured in the range 50–300 K by an absolute steady-state axial heat flow technique. The thermal conductivity of all samples has been shown to decrease with increasing temperature. At 300 K, the lowest thermal conductivity of the samples with x ≤ 0.05 exceeds 6 W/(m K), and that of the samples with x ≥ 0.85 is a factor of 2 lower. [ABSTRACT FROM AUTHOR]

Featured Application: laser surface-processing. Monocrystalline barium fluoride (BaF2) slab targets were irradiated by focused 46.9-nm laser radiation at various fluence levels above the ablation threshold. Well-developed ablation patterns with sharp edges were studied by AFM (atomic force microscopy). Their inner surfaces were uniformly covered by periodic structures. The spatial period of the ripples depends on the laser fluence. When the sample is rotated by 45°, the orientation of the grating-like structure changes accordingly. Thus, the grating vector of the periodic structure seems to be coupled to the crystallographic planes of the single crystal. This means that the XUV-laser induced ripples reported here differ from LIPSS (laser-induced periodic surface structures) associated with interference phenomena occurring on illuminated surfaces. Therefore, other mechanisms are discussed to explain the formation of the periodic nanostructures reported in this article. [ABSTRACT FROM AUTHOR]

Barium fluoride (BaF2) crystals are attracting much attention as efficient inorganic scintillator promising for high‐energy physics, industrial inspection, and other fields because of the fast component of the decay time (0.6 ns) and high radiation resistance. However, two major drawbacks limit its practical application: (i) a slow decay time of ~600 ns is derived from self‐trapping excitons; (ii) the absolute light yield from the fast luminescence component is not competitive. The introducing of rare earth ions and preparation of BaF2 polycrystalline ceramics is considered to be effective measures to solve these bottlenecks. Pr3+ is extremely suitable as the activated ion of scintillation materials, which possess emission peaks located in visible band and the faster 5d–4f transition. In this work, highly sinterable Pr3+:BaF2 precursor powder was synthesized via the coprecipitation method by adjusting the reactant concentration and temperature. The morphology and microstructure of as‐synthesized powders were characterized using scanning electron microscopy (SEM) and transmittance electron microscopy analysis. The 5 at.% Pr3+:BaF2 transparent ceramic with a transmittance of 50.7% at the wavelength of 500 nm was fabricated by hot pressing the as‐prepared powders at 900°C for 4 h under the axial pressure of 50 MPa. The SEM images of ceramic cross‐section show that the residual pore is the main light scattering source. The absorption and emission spectrum of ceramic samples were discussed. [ABSTRACT FROM AUTHOR]