Highlights: [•] Synthesis of ceria by homogeneous precipitation at room temperature and in supercritical water. [•] Deposition of ceria on SBA-15. [•] Characterized by XRD, SEM, TEM, XPS, nitrogen physisorption and CO2 TPD. [•] Physico-chemical and catalytic properties dependence on preparation. [•] Activity tests in synthesis of diethyl carbonate from carbon dioxide and ethanol with butylene oxide as the dehydrating agent. [Copyright &y& Elsevier]

Abstract: Synthesis of solid base Ce–H-MCM-41, Ce–Si-MCM-41, Cs-MCM-41, K-MCM-41 mesoporous materials and Na-ZSM-12, Cs-ZSM-12 microporous zeolites were carried out by means of evaporation impregnation and ion-exchange methods. The solid base catalysts were characterized using X-ray powder diffraction, scanning electron microscope, nitrogen adsorption, FTIR of pyridine and temperature programmed desorption of CO2. The H-ZSM-12, Cs-ZSM-12 zeolite, H-MCM-41, Ce–H-MCM-41 and Ce–Si-MCM-41 mesoporous catalysts were studied for the synthesis of diethyl carbonate starting from ethanol and carbon dioxide, using butylene oxide as the dehydrating agent. Catalyst testing for the synthesis of diethyl carbonate was carried out at 170°C and 4.5MPa of initial CO2 pressure. 16wt.% Ce–H-MCM-41 mesoporous material exhibited higher amount of weak, medium and strong basic sites than that of 32wt.% Ce–Si-MCM-41. The presence of weak and strong basic sites was observed in the microporous 2wt.% Cs-ZSM-12 catalyst. Diethyl carbonate formation was observed over Ce–H-MCM-41 and Ce–Si-MCM-41 mesoporous materials. Amount of basic sites and its strength influenced the synthesis of diethyl carbonate over the mesoporous materials. [Copyright &y& Elsevier]