Search

Two Lithium Disilicate (LD) glass ceramics based on SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting method. The glass rods were then fabricated into dental crowns via a hot pressing at 900˚C and 850˚C in order to study the effect of the pressing temperatures on the phase formation and microstructure of the glasses. Different samples of as cast glass and heat treated samples (600˚C and 700˚C) were used to press for investigating the effect of an initial microstructure on the hot pressing technique. Xray diffraction (XRD) and scanning electron microscopy (SEM) were performed to determine the phase formation and microstructure of the samples, respectively. XRD results show that the main crystalline structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3, Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with different heat treatment temperatures exhibited a difference phase formations but have less effect during pressing. SEM micrographs showed the microstructure of Li2Si2O5 as lath-like shape in all glasses. With increasing the initial heat treatment temperature, the longer the lath-like crystals of lithium disilicate were increased especially when using glass heat treatment at 700˚C followed by pressing at 900˚C. This could be suggested that LD1 heat treatment at 700˚C which pressing at 900˚C presented the best formation by the hot pressing and compiled microstructure.

Calcium phosphate cement (CPC) is one of the most attractive bioceramics due to its moldable and shape ability to fill complicated bony cavities or small dental defect positions. In this study, CPC was produced by using mixture of tetracalcium phosphate (TTCP, Ca4O(PO4)2) and dicalcium phosphate anhydrous (DCPA, CaHPO4) in equimolar ratio (1/1) with aqueous solutions of acetic acid (C2H4O2) and disodium hydrogen phosphate dehydrate (Na2HPO4.2H2O) in combination with sodium alginate in order to improve theirs moldable characteristic. The concentration of the aqueous solutions and sodium alginate were varied to investigate the effect of different aqueous solutions and alginate on properties of the cements. The cement paste was prepared by mixing cement powder (P) with aqueous solution (L) in a P/L ratio of 1.0g/0.35ml. X-ray diffraction (XRD) was used to analyses phase formation of the cements. Setting time and compressive strength of the set CPCs were measured using the Gilmore apparatus and Universal testing machine, respectively. The results showed that CPCs could be produced by using both basic (Na2HPO4.2H2O) and acidic (C2H4O2) solutions. XRD results show the precipitation of hydroxyapatite in all cement samples. No change in phase formation among cements using difference concentrations of Na2HPO4.2H2O solutions. With increasing concentration of acidic solutions, samples obtained less hydroxyapatite with a high dicalcium phosphate dehydrate leaded to a shorter setting time. Samples with sodium alginate exhibited higher crystallization of hydroxyapatite than that of without alginate as a result of shorten setting time in a basic solution but a longer setting time in an acidic solution. The stronger cement was attained from samples using the acidic solution with sodium alginate; however the strength was lower than that of using the basic solution., {"references":["C.D. Friedman, P.D. Costantino, S. Takagi, L.C. Chow, \"Bone Source\nhydroxyapatite cement: a novel biomaterial for craniofacial skeletal\ntissue engineering and reconstruction,\" J. Biomed. Mater. Res., Vol.\n43,1998, pp. 428–432.","D.B. Kamerer, B.E. Hirsch, C.H. Snyderman, P. Costantino, C.D.\nFriedman, \"Hydroxyapatite cement: a new method for achieving\nwatertight closure in transtemporal surgery,\" Am. J. Otol., vol. 15, 1994,\npp. 47–49.","B.R. Constantz, I.C. Ison, M.T. Fulmer, R.D. Poser, S.T. Smith, M.\nVanWagoner,et al., \"Skeletal repair by in situ formation of the mineral\nphase of bone,\" Science, vol 267, 1995, pp. 1796–1799.","W.G. Horstmann, C.C.P.M. Verheyen, R. Leemans, \"An injectable\ncalcium phosphate cement as a bone-graft substitute in the treatment of\ndisplaced lateral tibial plateau fractures,\" Injury, vol. 34, 2003, pp. 141–\n144.","E.J. Strauss, K.A. Egol, \"The management of ankle fractures in the\nelderly,\" Injury, vol 38 (Suppl. 3), 2007, pp. S2–S9.","P.A. Liverneaux, \"Osteoporotic distal radius curettage—filling with an\ninjectable calcium phosphate cement. A cadaveric study,\" Eur. J.\nOrthop. Surg. Traumatol., vol. 15, 2004, pp. 1–6.","R.D. Welch, H. Zhang, D.G. Bronson, \"Experimental tibial plateau\nfractures augmented with calcium phosphate cement or autologous bone\ngraft,\" J. Bone Joint Surg., vol. 85, 2003, pp. 222.","A. Aral, S. Yalçin, Z.C. Karabuda, A. Anil, J.A. Jansen, Z. Mutlu,\n\"Injectable calcium phosphate cement as a graft material for maxillary\nsinus augmentation: an experimental pilot study,\" Clin. Oral Implants\nRes., vol. 19, 2008, pp. 612–617.","M.P. Ginebra, T. Traykova, J.A. Planell, \"Calcium phosphate\ncements: competitive drug carriers for the musculoskeletal system,\"\nBiomaterials, vol. 27, 2006, pp. 2171–2177.\n[10] S. Hirayama, S. Hirayama, S. Takagi, M. Markovic, L.C. Chow,\nProperties of calcium phosphate cements with different tetracalcium\nphosphate and dicalcium phosphate anhydrous molar ratios, J. Res. Natl.\nInst. Stand. Technol., vol. 113, 2008, pp. 311–320.\n[11] S. Hirayama, S. Takagi, M. Markovic, L.C. Chow, \"Properties of\ncalcium phosphate cements with different tetracalcium phosphate and\ndicalcium phosphate anhydrous molar ratios,\" J. Res. Natl. Inst. Stand.\nTechnol., vol. 113, 2008, pp. 311–320.\n[12] H. Suzuki, H. Suzuki, M. Sakurai, M. Watanabe, \"The effect of\nstimulator on hardening of calcium phosphates,\" Phos. Res. Bull., vol.\n12, 2001, pp. 31–38.\n[13] K. Muroyama,T. Matumoto, K. Yamashita, T. Umegaki, \"Effect of\naddition of water-soluble polymers of hydraulically hardened calcium\nphosphates,\" Mukimateriaru, vol. 3, 1996, pp. 380–385.\n[14] M. Watanabe, M. Tanaka, M. Sukurai, M. Maeda, \"Development of\ncalcium phosphate cement,\" J. Eur. Ceram. Soc., vol. 26, 2006, pp. 549–\n552.\n[15] S.Takagi, L.C.ChowandK.Ishikawa, \"Formation of hydroxyapatite in\nnew calcium phosphate cements,\" Biomaterial, vol. 19, 1998, pp. 1593-\n1599.\n[16] M.P. Ginebra, C. Canal, M. Espanol, D. Pastorino, E.B. Montufar,\n\"Calcium phosphate cements as drug delivery materials,\" Adv. Drug\nDeliv. Rev., vol. 64, 2012, pp. 1090–1110.\n[17] F. C. M. Driessens, M. G. Boltong, O. Bermudez and J. A. Planell,\n\"Formulation and setting times of some calcium orthophosphate\ncements: a pilot study,\" J. Mater. Sci.: Mater. Med., vol. 4, 1993, pp.\n503-508.\n[18] F. C. M. Driessens, J.A. Planell,M.G. Boltong, I. Khairoun and M.P.\nGinebra, J. Eng. Med., \"Proceedings of the Institution of Mechanical\nEngineers, Part H,\" 1998, pp. 212-427."]}